Phosphorus based flame retardant composition for reaction injection molded polydicyclopentadiene

Claim 2

A composition that is polymerizable by contacting it with an olefin metathesis catalyst comprising dicyclopentadiene, red phosphorus, and a brominated aromatic compound selected from the group consisting of decabromodiphenyl oxide, N, N'-ethylene-bis-(tetrabromophthalimide), brominated polystyrene, brominated polyphenylene oxide, tetradecabromodiphenoxy benzene, tetrabromoxylene, and octabromodiphenyl oxide.

Claim 3

The composition of claim 1, further comprising another polymerizable cycloolefin.

Claim 4

The composition of claim 1, wherein the red phosphorus is microencapsulated in a phenol-formaldehyde resin.

Claim 5

The composition of claim 1, wherein the microencapsulated red phosphorus is stabilized by contact with magnesium oxide.

Claim 6

The composition of claim 1, wherein the brominated aromatic compound is decabromodiphenyl oxide.

Claim 7

The composition of claim 1, wherein the red phosphorus and brominated aromatic compound have a maximum particle size of about 44 microns.

Claim 8

The composition of claim 1, wherein the red phosphorus comprises at least about 0.9%, by weight, of the composition.

Claim 9

The composition of claim 1, wherein the bromine content comprises at least about 6%, by weight, of the composition.

Claim 10

In a process of making a thermoset polymer that comprises the steps of: (a) combining a plurality of reactant streams one of which contains the activator of a metathesis-catalyst system and a moderator, a second which contains the catalyst of the catalyst system, and at least one of which contains dicyclopentadiene and from 0% to about 10% of another polymerizable cycloolefin to form a reaction mixture; and (b) immediately injecting the reaction mixture into a mold where polymerization occurs; the improvement wherein at least one of the reactant streams contains red phosphorus and a brominated aromatic compound selected from the group consisting of decabromodiphenyl oxide, N, N'-ethylene-bis(tetrabromophthalimide), brominated polystyrene, brominated polyphenylene oxide, tetradecabromodiphenoxy benzene, tetrabromoxylene, and octabromodiphenyl oxide.

Claim 11

In a process of making a thermoset polymer that comprises the steps of: (a) combining a plurality of reactant streams one of which contains the activator of a metathesis-catalyst system and a moderator, a second which contains the catalyst of the catalyst system, and at least one of which contains dicyclopentadiene and from 0% to about 10% of another polymerizable cycloolefin to form a reaction mixture; and (b) immediately injecting the reaction mixture into a mold where polymerization occurs; the improvement wherein at least one of the reactant streams contains red phosphorus and a brominated aromatic compound selected from the group consisting of decabromodiphenyl oxide, N, N'-ethylene-bis(tetrabromophthalimide), brominated polystyrene, brominated polyphenylene oxide, tetradecabromodiphenoxy benzene, tetrabromoxylene, and octabromodiphenyl oxide.

Claim 12

The process of claim 9, wherein the red phosphorus and brominated aromatic compound comprise less than about 40% by weight of the reaction mixture.

Claim 13

The thermoset polymer made according to the process of claim 10.

Claim 14

A thermoset polymer comprising olefin metathesispolymerized dicyclopentadiene interspersed throughout with red phosphorus and a brominated aromatic compound selected from the group consisting of decabromodiphenyl oxide, N,N'-ethylene-bis(tetrabromophthalimide), brominated polystyrene, brominated polyphenylene oxide, tetradecabromodiphenoxy benzene, tetrabromoxylene, and octabromodiphenyl oxide.

Claim 15

A thermoset polymer comprising olefin metathesispolymerized dicyclopentadiene interspersed throughout with red phosphorus and a brominated aromatic compound selected from the group consisting of decabromodiphenyl oxide, N,N'-ethylene-bis(tetrabromophthalimide), brominated polystyrene, brominated polyphenylene oxide, tetradecabromodiphenoxy benzene, tetrabromoxylene, and octabromodiphenyl oxide.

Claim 16

The thermoset polymer of claim 12 wherein the red phosphorus is encapsulated in a phenol-formaldehyde resin.

Claim 17

The thermoset polymer of claim 13, wherein the microencapsulated phosphorus is stabilized by contact with magnesium oxide.

Claim 18

The thermoset polymer of claim 12, wherein the brominated aromatic compound is decabromodiphenyl oxide.

Claim 19

The thermoset polymer of claim 12, wherein the red phosphorus and brominated aromatic compound have a maximum particle size of about 44 microns.

Claim 20

The thermoset polymer of claim 12, wherein the red phosphorus comprises at least about 0.9%, by weight, of the thermoset polymer.

Claim 21

The thermoset polymer of claim 12, wherein the bromine content comprises at least about 6%, by weight, of the thermoset polymer.