Coated optical fibers
Assignee: Nippon Paint Co Ltd
•
Filing: 1986-03-12
•
Granted: 1988-04-26
•
Expires: 2006-03-12
Abstract
Abstract Coated optical fibers surrounded by a protective coating film comprising a continuous phase of film-forming matrix resin and polymer microparticles of a polymer of ethylenically unsaturated polymerizable monomers.
Inventors
- 👤 Kazunori Kanda
- 👤 Ryuzo Mizuguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:12
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/106; C03C25/1065; G; G02; G02B; G02B6/00; G02B6/02; G02B6/44; G02B6/4401; G02B6/4429; G02B6/443
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
124 words
In an optical fiber surrounded by a protective coating film comprising a plurality of layers, the improvement wherein a primary layer of said coating film which is directly on the fiber surface comprises a continuous phase of a film-forming matrix resin and 0.02 to 20% by weight of said primary layer of polymer microparticles having a particle size from 0.01 to 6 microns uniformly dispersed in said matrix resin, thereby improving its Young's modulus and elongation over a wide temperature range as well as its peelability, said polymer microparticles consisting essentially of an internally cross-linked polymer of a mixture of ethylenically unsaturated monomers containing a monomer having at least two polymerizable sites per molecule or a combination of two monomers having mutually reactive groups.
Claim 2
Dependent Claim
124 words
In an optical fiber surrounded by a protective coating film comprising a plurality of layers, the improvement wherein a primary layer of said coating film which is directly on the fiber surface comprises a continuous phase of a film-forming matrix resin and 0.02 to 20% by weight of said primary layer of polymer microparticles having a particle size from 0.01 to 6 microns uniformly dispersed in said matrix resin, thereby improving its Young's modulus and elongation over a wide temperature range as well as its peelability, said polymer microparticles consisting essentially of an internally cross-linked polymer of a mixture of ethylenically unsaturated monomers containing a monomer having at least two polymerizable sites per molecule or a combination of two monomers having mutually reactive groups.
Claim 3
Dependent Claim
64 words
The optical fiber as claimed in claim 1, wherein a secondary layer of said coating film, which covers said primary layer, also comprises a continuous phase of a second film-forming matrix resin and 0.02 to 20% by weight of said secondary layer of said polymer microparticles uniformly dispersed in said second matrix resin, thereby improving its toughness and elongation over a wide temperature range.
Claim 4
Dependent Claim
16 words
The optical fiber as claimed in claim 1, wherein said matrix resin is a thermosetting resin.
Claim 5
Dependent Claim
17 words
The optical fiber as claimed in claim 1, wherein said matrix resin is a radiation curable resin.
Claim 6
Dependent Claim
16 words
The optical fiber as claimed in claim 3, wherein said matrix resin is a silicone resin.
Claim 7
Dependent Claim
46 words
The optical fiber as claimed in claim 4, said matrix resin is selected from the group consisting of unsaturated polyester resin, urethane acrylate resin, epoxy acrylate resin, polyester acrylate resin, spirane acrylate resin, polyether acrylate resin, silicon acrylate resin, polybutadiene acrylate resin and vinyl acrylate resin.
Claim 8
Dependent Claim
34 words
The optical fiber as claimed in claim 1, wherein said polymer microparticles are prepared by a polymerization method selected from the group consisting of emulsion polymerization, non-aqueous dispersion polymerization, precipitation polymerization and suspension polymerization.
Claim 9
Dependent Claim
21 words
The optical fiber as claimed in claim 7, wherein said emulsion polymerization is carried out using an emulsifier containing ampho-ionic groups.
Claim 10
Dependent Claim
18 words
The optical fiber as claimed in claim 2, wherein said second matrix resin is a radiation curable resin.
Claim 11
Dependent Claim
22 words
The optical fiber as claimed in claim 9, wherein said radiation curable resin is a urethane acrylate resin or expoxy acrylate resin.
Claim 12
Dependent Claim
112 words
In an optical fiber surrounded by a protective coating film comprising a plurality of layers, the improvement wherein an outermost layer of said coating film comprises a continuous phase of a thermoplastic matrix resin and 0.02 to 20% by weight of said outermost layer of polymer microparticles having a particle size from 0.01 to 6 microns uniformly dispersed in said matrix resin, thereby improving the toughness and abrasion resistance of said outermost layer, said polymer microparticles consisting essentially of an internally cross-linked polymer of a mixture of ethylenically unsaturated polymerizable monomers containing a monomer having at least two polymerizable sites per molecule or a combination of two monomers having mutually reactive groups.
Claim 13
Dependent Claim
112 words
In an optical fiber surrounded by a protective coating film comprising a plurality of layers, the improvement wherein an outermost layer of said coating film comprises a continuous phase of a thermoplastic matrix resin and 0.02 to 20% by weight of said outermost layer of polymer microparticles having a particle size from 0.01 to 6 microns uniformly dispersed in said matrix resin, thereby improving the toughness and abrasion resistance of said outermost layer, said polymer microparticles consisting essentially of an internally cross-linked polymer of a mixture of ethylenically unsaturated polymerizable monomers containing a monomer having at least two polymerizable sites per molecule or a combination of two monomers having mutually reactive groups.
Claim 14
Dependent Claim
41 words
The optical fiber as claimed in claim 11, wherein said thermoplastic resin is selected from the group consisting of polyamide, polyethylene, polypropylene, polyester, polysulfone, acrylic resins, methacrylic resins, polyvinyl chloride, polyphenylene oxide, polyphenylene sulfide, fluorocarbon resins and blends of these polymers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-26 | 1991-10-26 | 1992-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-26 | 1995-10-26 | 1996-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-26 | 1999-10-26 | 2000-04-26 | $7700.00 | Window Closed / Lapsed |