Metal forming
Assignee: BTG International Ltd
•
Filing: 1986-04-18
•
Granted: 1988-04-19
•
Expires: 2006-04-18
Abstract
Abstract Metal forming process and apparatus are described. The process comprises directing a stream (4) of atomized droplets of molten metal onto a chill surface (5) such that the metal is partially solidified to form a slurry of solidified metal suspended in liquid metal. The slurry is then collected (for example, in a casting mold 7) and then cast or otherwise formed before solidification is complete. It is particularly preferred that the stream of atomized droplets is directed onto a fully solidified layer (6) of the same metal on the chill surface.
Inventors
- 👤 Alfred R. Singer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:29
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/10; B22D11/11; B22D11/112; C; C22; C22C; C22C1/00; C22C1/12
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
83 words
A metal casting process, which comprising directing a stream of atomized metal on to a chill surface so as to initially form a fully solidified metal layer and continuing directing a stream of the metal onto said formed metal layer to cause the metal of the stream to partially solidify in the form of a slurry comprising solidified metal suspended in still-molten metal; flowing the slurry under liquid flow conditions into a casting mold; and allowing the slurry to solidify in said mold.
Claim 2
Dependent Claim
83 words
A metal casting process, which comprising directing a stream of atomized metal on to a chill surface so as to initially form a fully solidified metal layer and continuing directing a stream of the metal onto said formed metal layer to cause the metal of the stream to partially solidify in the form of a slurry comprising solidified metal suspended in still-molten metal; flowing the slurry under liquid flow conditions into a casting mold; and allowing the slurry to solidify in said mold.
Claim 3
Dependent Claim
78 words
A metal casting process, which comprises splatting a stream of atomized droplets of molten metal on to a chill surface to cause partial solidification of the metal, and fracture and fragmentation of dendrites in the partially solidified metal by subsequently impacting atomized metal thereon, such that the latter has the consistency of a slurry comprising fractured dendrites in still-molten metal; flowing said partially solidified metal into a casting mold; and allowing the material in said mold to solidify.
Claim 4
Dependent Claim
78 words
A metal casting process, which comprises splatting a stream of atomized droplets of molten metal on to a chill surface to cause partial solidification of the metal, and fracture and fragmentation of dendrites in the partially solidified metal by subsequently impacting atomized metal thereon, such that the latter has the consistency of a slurry comprising fractured dendrites in still-molten metal; flowing said partially solidified metal into a casting mold; and allowing the material in said mold to solidify.
Claim 5
Dependent Claim
52 words
A process according to claim 1 or 2, in which a substantially fully solidified layer of said metal is initially formed on said chill surface such that a steady state is reached in which the atomised molten metal impacts a surface consisting of partially solidified metal overlying said substantially fully solidified layer.
Claim 6
Dependent Claim
32 words
A process according to caim 1, in which the molten metal is atomised by means of jets of an inert or reducing gas directed at a falling stream of said molten metal.
Claim 7
Dependent Claim
32 words
A process according to caim 1, in which the molten metal is atomised by means of jets of an inert or reducing gas directed at a falling stream of said molten metal.
Claim 8
Dependent Claim
14 words
A process according to claim 2, in which the molten metal is atomised centrifugally.
Claim 9
Dependent Claim
20 words
A process according to claim 2, in which said slurry flows off said chill surface directly into said receiving vessel.
Claim 10
Dependent Claim
56 words
A process according to claim 1, in which said chill surface is in the form of an inverted truncated cone and said stream is caused to rotate about the axis of said truncated cone such that the area of impact between said stream and the chill plate is itself in the form of a truncated cone.
References Cited (Backward Citations)
GB809412A
Cited
GB1262471A
Cited
US3826301A
Cited
US3909921A
Cited
US4114251A
Cited
GB1601181A
Cited
US4579168A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-19 | 1991-10-19 | 1992-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-19 | 1995-10-19 | 1996-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-19 | 1999-10-19 | 2000-04-19 | $7700.00 | Window Closed / Lapsed |