Self-adhering polyorganosiloxane elastomer compositions and method for preparing same
Assignee: Dow Silicones Corp
•
Filing: 1986-10-15
•
Granted: 1988-04-12
•
Expires: 2006-10-15
Abstract
Abstract Polyorganosiloxane compositions yielding cured elastomers exhibiting cohesive bonding to inorganic substrates contain as the adhesion promoter the combination of (1) a 1,2- bis(trialkoxysilyl)ethane of the general formula (RO) 3 SiCH 2 CH 2 Si(OR) 3 where R represents an alkyl or haloalkyl radical containing from 1 to 8 carbon atoms, (2) an organosilicon compound containing at least one hydroxyl group or a hydrolyzable precursor thereof and at least one group that reacts at ambient temperature with the alkoxy groups of the silylethane or with the curable polyorganosiloxane composition, and (3) a catalyst for the reaction of the adhesion promoter ingredients. Preferred compositions are cured at room temperature by a platinum catalyzed hydrosilation reaction and are applied to metallic substrates that have not been cleaned or otherwise treated prior to application of the composition.
Inventors
- 👤 Manoj K. Chaudhury
- 👤 John H. Gaul
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:39
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/54; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/14; C08G77/16; C08G77/18; C08G77/20; C08G77/22; C08G77/24
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
212 words
A composition which reacts to form a cured silicone elastomer capable of cohesively bonding to inorganic substrates, said composition comprising the product obtained by blending to homogeniety A. a curable polyorganosiloxane, B. a crosslinking agent for curing said polyorganosiloxane, and C. a liquid adhesion promoter that is miscible with (A) and (B) and consists essentially of (1) a first organosilicon compound of the general formula (RO) 3 SiCH 2 CH 2 Si(OR) 3 , where R represents an alkyl or haloalkyl radical containing from 1 to 8 carbon atoms, inclusive; (2) an second organosilicon compound containing in each molecule at least one silicon-bonded group represented by X and at least one silicon-bonded group represented by Y, where X represents hydroxyl or a group that is hydrolyzable to a hydroxyl group, Y is selected from the group consisting of X, hydrogen and organofunctional radicals and reacts with said curable polyorganosiloxane and/or said crosslinking agent; and (3) a catalyst for the reaction of said X group with said substrate or the alkoxy groups of said first organosilicon compound and the reaction of said Y group, with the proviso that said second organosilicon compound is not represented by said general formula, and said organofunctional radicals are bonded to silicon by means of a silicon-carbon bond.
Claim 2
Dependent Claim
212 words
A composition which reacts to form a cured silicone elastomer capable of cohesively bonding to inorganic substrates, said composition comprising the product obtained by blending to homogeniety A. a curable polyorganosiloxane, B. a crosslinking agent for curing said polyorganosiloxane, and C. a liquid adhesion promoter that is miscible with (A) and (B) and consists essentially of (1) a first organosilicon compound of the general formula (RO) 3 SiCH 2 CH 2 Si(OR) 3 , where R represents an alkyl or haloalkyl radical containing from 1 to 8 carbon atoms, inclusive; (2) an second organosilicon compound containing in each molecule at least one silicon-bonded group represented by X and at least one silicon-bonded group represented by Y, where X represents hydroxyl or a group that is hydrolyzable to a hydroxyl group, Y is selected from the group consisting of X, hydrogen and organofunctional radicals and reacts with said curable polyorganosiloxane and/or said crosslinking agent; and (3) a catalyst for the reaction of said X group with said substrate or the alkoxy groups of said first organosilicon compound and the reaction of said Y group, with the proviso that said second organosilicon compound is not represented by said general formula, and said organofunctional radicals are bonded to silicon by means of a silicon-carbon bond.
Claim 3
Dependent Claim
83 words
A composition according to claim 1 where said curable polyorganosiloxane and crosslinking agent react at room temperature, R is methyl or ethyl, the substrate is metallic, X is hydroxyl or alkoxy containing from 1 to 10 carbon atoms, and Y is alkoxy, hydrogen, or an organofunctional radical selected from the group consisting of terminally unsaturated alkenyl radicals and radicals of the general formula Z'"--where R'" represents alkylene containing at least 3 carbon atoms and Z represents acryloxy, methacryloxy, glycidoxy, mercaptos, amino and N-aminoalkylamino.
Claim 4
Dependent Claim
133 words
A composition according to claim 2 where said second organosilicon compound is selected from the group consisting of (a) silanes of the general formula Y a SiX.sub.(4--a) or Y a R"SiX.sub.(3-a) and partial hydrolysis products of said silanes, where a represents an integer from 1 to 3, inclusive, and R" represents a monovalent hydrocarbon radical containing from 1 to about 8 carbon atoms, (b) reaction products of said silanes with at least one polyorganosiloxane containing an average of two or more silicon atoms per molecule that are linked by oxygen atoms, the remaining valences of the silicon atoms being satisfied by Y groups and monovalent hydrocarbon radicals, and (c) reaction products of said polyorganosiloxanes with organic compounds containing at least one Y group and at least one group that reacts with said polyorganosiloxane.
Claim 5
Dependent Claim
51 words
A composition according to claim 2 where said composition is curable by a platinum catalyzed hydrosilation reaction, said catalyst is a titanium compound, X is alkoxy, Y is vinyl, allyl or hydrogen and the molar ratio of said first organosilicon compound to said second organosilicon compound is from 0.1 to 7.
Claim 6
Dependent Claim
75 words
A composition according to claim 4 where said second organosilicon compound is selected form the group consisting of vinyltrialkoxysilanes, allyltrialkoxysilanes, and reaction products of (1) silanes of the formula (R") n Si(OR*) 4 -- n , where n is 0 or 1. R* is methyl or ethyl and R" is methyl, ethyl or (R*O) 3 SiCH 2 CH 2 --, with (2) an organohydrogensiloxane or an alcohol containing at least one terminally unsaturated alkenyl radical.
Claim 7
Dependent Claim
79 words
A composition according to claim 5 where said first organosilicon compound is 1,2-bis(trimethoxysilyl)ethane, said second organosilicon compound is selected from the group consisting of vinyltrimethoxysilane, allyltrimethoxysilane, reaction products of the mono- or diallyl ether of trimethylolpropane with an organosilicon compound selected from the group consisting of methyltrimethoxysilane, methyl orthosilicate and 1,2-bis(trimethoxysilyl)ethane, the curable polyorganosiloxane is a vinyl terminated polydiorganosiloxane and the crosslinking agent is an organohydrogensiloxane containing an average of at least three silicon bonded hydrogen atoms per molecule.
Claim 8
Independent Claim
187 words
A method for promoting adhesion of a cured silicone elastomer to an inorganic substrate, said method comprising incorporating into a curable precursor of said elastomer a miscible liquid adhesion promoter consisting essentially of the product obtained by blending to homogeniety A. a first organosilicon compound of the general formula (RO) 3 SiCH 2 CH 2 Si(OR) 3 , where R represents an alkyl or haloalkyl radical containing from 1 to 8 carbon atoms, inclusive; B. a second organosilicon compound containing at least one silicon-bonded group per molecule represented by X and at least one silicon-bonded group per molecule represented by Y, where X represents hydroxyl or a group that is hydrolyzable to a hydroxyl group, Y is selected from the group consisting of X, hydrogen and organofunctional radicals, and reacts with the ingredients of said curable precursor; and C. a catalyst in an amount sufficient to promote the reaction of said X groups with said substrate or the alkoxy groups of said first organosilicon compound and the reaction of said Y group, with the proviso that said second organosilicon compound does not correspond to said general formula.
Claim 9
Independent Claim
187 words
A method for promoting adhesion of a cured silicone elastomer to an inorganic substrate, said method comprising incorporating into a curable precursor of said elastomer a miscible liquid adhesion promoter consisting essentially of the product obtained by blending to homogeniety A. a first organosilicon compound of the general formula (RO) 3 SiCH 2 CH 2 Si(OR) 3 , where R represents an alkyl or haloalkyl radical containing from 1 to 8 carbon atoms, inclusive; B. a second organosilicon compound containing at least one silicon-bonded group per molecule represented by X and at least one silicon-bonded group per molecule represented by Y, where X represents hydroxyl or a group that is hydrolyzable to a hydroxyl group, Y is selected from the group consisting of X, hydrogen and organofunctional radicals, and reacts with the ingredients of said curable precursor; and C. a catalyst in an amount sufficient to promote the reaction of said X groups with said substrate or the alkoxy groups of said first organosilicon compound and the reaction of said Y group, with the proviso that said second organosilicon compound does not correspond to said general formula.
Claim 10
Dependent Claim
84 words
A method according to claim 7 where said curable polyorganosiloxane and crosslinking agent react at room temperature, R is methyl or ethyl, the substrate is metallic, X is hydroxyl or alkoxy containing from 1 to 10 carbon atoms, and Y is alkoxy, hydrogen, or an organofunctional radical selected from the group consisting of terminally unsaturated alkenyl radicals and radicals of the general formula ZR'"--, where R'" represents alkylene containing at least 3 carbon atoms and Z represents acryloxy, methacryloxy, glycidoxy, mercapto, amino and N-aminoalkylamino.
Claim 11
Dependent Claim
51 words
A method according to claim 8 where said composition is curable by a platinum catalyzed hydrosilation reaction, said catalyst is a titanium compound, X is alkoxy, Y is vinyl, allyl or hydrogen, and the molar ratio of said first organosilicon compound to said second organosilicon compound is from 0.1 to 7.
Claim 12
Dependent Claim
75 words
A method according to claim 9 where said second organosilicon compound is selected from the group consisting of vinyltrialkoxysilanes, allyltrialkoxysilanes, and reaction products of (1) silanes of the formula (R") n Si(OR*) 4 -- n , where n is 0 or 1, R* is methyl or ethyl, and R" is methyl, ethyl or (R*O) 3 SiCH 2 CH 2 --, with 2) an organohydrogensiloxane or an alcohol containing at least one terminally unsaturated alkenyl radical.
Claim 13
Dependent Claim
79 words
A method according to claim 10 where said first organosilicon compound is 1,2-bis(trimethoxysilyl)ethane, said second organosilicon compound is selected from the group consisting of vinyltrimethoxysilane, allyltrimethoxysilane, reaction products of the mono- or diallyl ether of trimethylolpropane with an organosilicon compound selected from the group consisting of methyltrimethoxysilane methyl orthosilicate and 1,2-bis(trimethoxysilyl)ethane, the curable polyorganosiloxane is a vinyl terminated polydiorganosiloxane and the curing agent is an organohydrogensiloxane containing an average of at least three silicon bonded hydrogen atoms per molecule.
Claim 14
Dependent Claim
133 words
A method according to claim 8 where said second organosilicon compound is selected from the group consisting of (a) silanes of the general formula Y a SiX.sub.(4-a) or Y a R"SiX.sub.(3-a) and partial hydrolysis products of said silanes, where a represents an integer from 1 to 3, inclusive, and R" represents a monovalent hydrocarbon radical containing from 1 to about 8 carbon atoms, (b) reaction products of said silanes with at least one polyorganosiloxane containing an average of two or more silicon atoms per molecule that are linked by oxygen atoms, the remaining valences of the silicon atoms being satisfied by Y groups and monovalent hydrocarbon radicals, and (c) reaction products of said polyorganosiloxanes with organic compounds containing at least one Y group and at least one group that reacts with said polyorganosiloxane.
References Cited (Backward Citations)
US3509081A
Cited
US3699072A
Cited
US3772066A
Cited
GB1524790A
Cited
US4087585A
Cited
US4311739A
Cited
US4245079A
Cited
US4525400A
Cited
US4460639A
Cited
US4652624A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-12 | 1991-10-12 | 1992-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-12 | 1995-10-12 | 1996-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-12 | 1999-10-12 | 2000-04-12 | $7700.00 | Window Closed / Lapsed |