Polyolefin blends containing reactive agents
Assignee: DuPont Canada Inc
•
Filing: 1986-06-11
•
Granted: 1988-04-12
•
Expires: 2006-06-11
Abstract
Abstract A polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a second polyethylene, is disclosed. The first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, and the second polyethylene is a copolymer of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 , especially at least 0.910 g/cm 3 , and a melt index of at least 40 dg/min. The density of the second polyethylene is at least about 0.005 g/cm 3 lower than that of the first polyethylene and the melt index of the second polyethylene is at least 10 dg/min. higher than that of the first polyethylene. The composition of the second polyethylene contains an agent that is capable of reacting with polyolefins that are in a molten state. Such agents are selected from the group consisting of cross-linking agents and modifying agents, and mixtures thereof. In an alternative embodiment, the second polyethylene has a shear viscosity that is not more than 30% of that of the first polyethylene at 200° C. and a shear rate of 400 sec -1 ; in this regard, the first and second polyethylene may be more broadly defined as being homopolymers and copolymers of hydrocarbon alpha-olefins having 2-10 carbon atoms. The blends may be used in a wide variety of processes, including blow-moulding processes, film and pipe extrusion processes, sheet thermoforming processes and rotational moulding processes.
Inventors
- 👤 George White
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:42
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0807; C08L23/0815; C08K; C08K5/00; C08K5/04; C08K5/14; C08L2205/00; C08L2205/02; C08L2205/025; C08L2312/00
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
135 words
A polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyolefin and a minor portion of particles of a composition of a normally solid second polyolefin, said polyolefins being selected from the group consisting of homopolymers and copolymers consisting of hydrocarbon alpha-olefins having 2-10 carbon atoms, said second polyolefin having a shear viscosity that is not more than 30% of that of said first polyolefin when measured at 200° C. and a shear rate of 400 sec -1 , said composition being a composition of the second polyolefin and a reactive agent, and mixtures thereof, said reactive agent being capable of reacting with said polyolefins in a molten state. The ratio of the weight of the first polyolefin to the second polyolefin in said blend being from 10:1 to 100:1.
Claim 2
Dependent Claim
135 words
A polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyolefin and a minor portion of particles of a composition of a normally solid second polyolefin, said polyolefins being selected from the group consisting of homopolymers and copolymers consisting of hydrocarbon alpha-olefins having 2-10 carbon atoms, said second polyolefin having a shear viscosity that is not more than 30% of that of said first polyolefin when measured at 200° C. and a shear rate of 400 sec -1 , said composition being a composition of the second polyolefin and a reactive agent, and mixtures thereof, said reactive agent being capable of reacting with said polyolefins in a molten state. The ratio of the weight of the first polyolefin to the second polyolefin in said blend being from 10:1 to 100:1.
Claim 3
Dependent Claim
22 words
The blend of claim 1 in which the shear viscosity of the second polyolefin is 5-15% of that of the first polyolefin.
Claim 4
Dependent Claim
14 words
The blend of claim 1 in which the reactive agent is a cross-linking agent.
Claim 5
Dependent Claim
18 words
The blend of claim 1 in which the reactive agent is an unsturated organic acid or derivative thereof.
Claim 6
Dependent Claim
37 words
The blend of claim 1 in which the first and second polyolefins are each selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin.
Claim 7
Dependent Claim
180 words
A polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a normally solid second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index of at least 40 dg/min., said second polyethylene having a shear viscosity that is not more than 30% of that of said first polyethylene when measured at 200° C. and at a shear rate of 400 sec-1, said composition being a composition of the second polyethylene and a reactive agent, and mixtures thereof, said reactive agent being capable of reacting with said polyethylenes in a molten state. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 8
Dependent Claim
180 words
A polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a normally solid second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index of at least 40 dg/min., said second polyethylene having a shear viscosity that is not more than 30% of that of said first polyethylene when measured at 200° C. and at a shear rate of 400 sec-1, said composition being a composition of the second polyethylene and a reactive agent, and mixtures thereof, said reactive agent being capable of reacting with said polyethylenes in a molten state. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 9
Dependent Claim
22 words
The blend of claim 6 in which the shear viscosity of the second polyolefin is 5-15% of that of the first polyolefin.
Claim 10
Dependent Claim
20 words
The blend of claim 6 in which the density of the second polyethylene is at least 0.910 g/cm 3 .
Claim 11
Dependent Claim
14 words
The blend of claim 6 in which the reactive agent is a cross-linking agent.
Claim 12
Dependent Claim
18 words
The blend of claim 6 in which the reactive agent is an unsaturated organic acid or derivative thereof.
Claim 13
Dependent Claim
14 words
The blend of claim 9 in which, the first polyethylene contains a co-curing agent.
Claim 14
Dependent Claim
26 words
The blend of claim 6 in which the ratio of the first polyethylene to the second polyethylene is in the range of from 50:1 to 100:1.
Claim 15
Dependent Claim
186 words
A polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index in the range of 40-200 dg/min., the density of the second polyethylene being at least about 0.005 g/cm 3 lower than that of the first polyethylene and the melt index of the second polyethylene being at least 10 dg/min. higher than that of the first polyethylene, said composition being a composition of second polyethylene and a reactive agent, and mixtures thereof, said reactive agent being capable of reacting with said polyethylenes in a molten state. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 16
Dependent Claim
186 words
A polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index in the range of 40-200 dg/min., the density of the second polyethylene being at least about 0.005 g/cm 3 lower than that of the first polyethylene and the melt index of the second polyethylene being at least 10 dg/min. higher than that of the first polyethylene, said composition being a composition of second polyethylene and a reactive agent, and mixtures thereof, said reactive agent being capable of reacting with said polyethylenes in a molten state. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 17
Dependent Claim
24 words
The blend of claim 13 in which the melt index of the second polyethylene is 20 dg/min. higher than that of the first polyethylene.
Claim 18
Dependent Claim
24 words
The blend of claim 13 in which the melt index of the second polyethylene is 40-60 dg/min. higher than that of the first polyethylene.
Claim 19
Dependent Claim
20 words
The blend of claim 13 in which the density of the second polyethylene is at least 0.910 g/cm 3 .
Claim 20
Dependent Claim
27 words
The blend of claim 13 in which the density of the second polyethylene is at least 0.008 g/cm 3 lower than the density of the first polyethylene.
Claim 21
Dependent Claim
162 words
A process for the manufacture of articles from a polyolefin and a reactive agent capable of reacting with the polyolefin in a molten state, comprising feeding to melt processing apparatus a polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyolefin and a minor portion of particles of a composition of a normally solid second polyolefin, said polyolefins being selected from the group consisting of homopolymers and copolymers consisting of hydrocarbon alpha-olefins having 2-10 carbon atoms, said second polyolefin having a shear viscosity that is not more than 30% of that of said first polyolefin when measured at 200° C. and a shear rate of 400 sec-1, said composition being a composition of the second polyolefin and a reactive agent, and mixtures thereof, melting and admixing said blend and forming an article from the resultant blend. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 22
Dependent Claim
162 words
A process for the manufacture of articles from a polyolefin and a reactive agent capable of reacting with the polyolefin in a molten state, comprising feeding to melt processing apparatus a polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyolefin and a minor portion of particles of a composition of a normally solid second polyolefin, said polyolefins being selected from the group consisting of homopolymers and copolymers consisting of hydrocarbon alpha-olefins having 2-10 carbon atoms, said second polyolefin having a shear viscosity that is not more than 30% of that of said first polyolefin when measured at 200° C. and a shear rate of 400 sec-1, said composition being a composition of the second polyolefin and a reactive agent, and mixtures thereof, melting and admixing said blend and forming an article from the resultant blend. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 23
Dependent Claim
22 words
The process of claim 18 in which the shear viscosity of the second polyolefin is 5-15% of that of the first polyolefin.
Claim 24
Dependent Claim
14 words
The process of claim 18 in which the reactive agent is a cross-linking agent.
Claim 25
Dependent Claim
18 words
The process of claim 18 in which the reactive agent is an unsaturated organic acid or derivative thereof.
Claim 26
Dependent Claim
37 words
The process of claim 18 in which the first and second polyolefins are each selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin.
Claim 27
Dependent Claim
209 words
A process for the manufacture of articles from a polyolefin and a reactive agent capable of reacting with the polyolefin in a molten state, comprising feeding to melt processing apparatus a polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a normally solid second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index of at least 40 dg/min, said second polyethylene having a shear viscosity that is not more than 50% of that of said first polyethylene when measured at 200° C. and at a shear rate of 400 sec-1, said composition being a composition of the second polyethylene and a reactive agent, and mixtures thereof, melting and admixing said blend and forming an article from the resultant blend. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 28
Dependent Claim
209 words
A process for the manufacture of articles from a polyolefin and a reactive agent capable of reacting with the polyolefin in a molten state, comprising feeding to melt processing apparatus a polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a normally solid second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index of at least 40 dg/min, said second polyethylene having a shear viscosity that is not more than 50% of that of said first polyethylene when measured at 200° C. and at a shear rate of 400 sec-1, said composition being a composition of the second polyethylene and a reactive agent, and mixtures thereof, melting and admixing said blend and forming an article from the resultant blend. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 29
Dependent Claim
25 words
The process of claim 23 in which the shear viscosity of the second polyethylene is not more than 30% of that of the first polyethylene.
Claim 30
Dependent Claim
22 words
The process of claim 23 in which the shear viscosity of the second polyethylene is 5-15% of that of the first polyethylene.
Claim 31
Dependent Claim
19 words
The process of claim 23 which the density of the second polyethylene is at least 0.910 g/cm 3 .
Claim 32
Dependent Claim
215 words
A process for the manufacture of articles from a polyolefin and a reactive agent capable of reacting with the polyolefin in a molten state, comprising feeding to melt processing apparatus a polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index in the range of 40-200 dg/min., the density of the second polyethylene being at least about 0.005 g/cm 3 lower than that of the first polyethylene and the melt index of the second polyethylene being at least 10 dg/min. higher than that of the first polyethylene, said composition being a composition of second polyethylene and a reactive agent, and mixtures thereof, melting and admixing said blend and forming an article from the resultant blend. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 33
Dependent Claim
215 words
A process for the manufacture of articles from a polyolefin and a reactive agent capable of reacting with the polyolefin in a molten state, comprising feeding to melt processing apparatus a polyolefin blend comprising, in physical admixture, a major portion of particles of a first polyethylene and a minor portion of particles of a composition of a second polyethylene, in which the first polyethylene is selected from the group consisting of homopolymers of ethylene and copolymers of ethylene and at least one C 4 -C 10 higher alpha-olefin, said second polyethylene being a copolymer consisting of ethylene and at least one C 4 -C 10 higher alpha-olefin having a density of at least 0.890 g/cm 3 and a melt index in the range of 40-200 dg/min., the density of the second polyethylene being at least about 0.005 g/cm 3 lower than that of the first polyethylene and the melt index of the second polyethylene being at least 10 dg/min. higher than that of the first polyethylene, said composition being a composition of second polyethylene and a reactive agent, and mixtures thereof, melting and admixing said blend and forming an article from the resultant blend. The ratio of the weight of the first polyethylene to the second polyethylene in said blend being from 10:1 to 100:1.
Claim 34
Dependent Claim
38 words
The process of claim 22 which the rate of extrusion of polyolefin so as to form the article is higher than the rate would be for extrusion of the same polyolefin in the absence of the reactive agent.
Claim 35
Dependent Claim
15 words
The process of claim 28 in which the process is a blown film extrusion process.
Claim 36
Dependent Claim
51 words
A blend of claim 1 in which at least one of the major portion and the minor portion contains a fluorinated elastomer processing aid, the polyolefin of each of said major portion and said minor portion being a copolymer of ethylene and at least one C 4 -C 10 higher alpha-olefin.
Claim 37
Dependent Claim
61 words
A blend of claim 1 in which at least one of the major portion and the minor portion contains a fluorinated elastomer processing aid and in which the reactive agent is a cross-linking agent, the polyolefin of each of said major portion and said minor portion being a copolymer of ethylene and a least one C 4 -C 10 higher alpha-olefin.
Claim 38
Dependent Claim
51 words
A blend of claim 6 in which at least one of the major portion and the minor portion contains a fluorinated elastomer processing aid, the polyolefin of each of said major portion and said minor portion being a copolymer of ethylene and at least one C 4 -C 10 higher alpha-olefin.
Claim 39
Dependent Claim
61 words
A blend of claim 6 in which at least one of the major portion and the minor portion contains a fluorinated elastomer processing aid and in which the reactive agent is a cross-linking agent, the polyolefin of each of said major portion and said minor portion being a copolymer of ethylene and a least one C 4 -C 10 higher alpha-olefin.
References Cited (Backward Citations)
US3125547A
Cited
US4267080A
Cited
US4338227A
Cited
US4368280A
Cited
US4390666A
Cited
US4397992A
Cited
US4678834A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-12 | 1991-10-12 | 1992-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-12 | 1995-10-12 | 1996-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-12 | 1999-10-12 | 2000-04-12 | $7700.00 | Window Closed / Lapsed |