US4737199A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Machinable ductile or semiductile cast iron and method
Assignee: Ford Global Technologies LLC
•
Filing: 1985-12-23
•
Granted: 1988-04-12
•
Expires: 2005-12-23
Abstract
Abstract A method is disclosed which comprises: (a) forming a ferrous alloy melt consisting essentially of by weight, 3-4% carbon, 2.0-3.0% silicon, 0.1-0.9% manganese, up to 0.02% phosphorus, up to 0.002% sulphur, up to 1% contaminants or impurities, 0-0.4% molybdenum, 0-3.0% nickel or copper, and the reminder essentially iron, the melt being subjected to a graphite modifying agent in an amount and for a period of time effective to form either ductile or semiductile iron upon solidification; (b) heat treating the solidification of said melt by austempering to form a matrix consisting substantially of high carbon austenite and ferrite and a cell boundary having unreacted low carbon austenite; (c) heating said austempered iron to a pearlite forming temperature (1200°-1300° F.) and holding (2-5 minutes) at said temperature to permit the unreacted low carbon austenite to form pearlite; and (d) cooling said heat treated iron to room temperature.
Inventors
- 👤 Bela V. Kovacs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 05:24
CPC Classifications
C; C21; C21D; C21D5/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
150 words
A method of making a high strength, readily machinable ductile or semiductile cast iron, comprising: (a) forming a ferrous alloy melt consisting essentially of, by weight, 3-4% carbon, 2.0-3.0% silicon, 0.9% manganese, up to 0.02% phosphorous, up to 0.002% sulphur, up to 1% contaminants or impurities, 0-0.4% molybdenum, 0-3.0% nickel or copper, and the remainder essentially iron, said melt being subjected to a graphite modifying agent in an amount and for a period of time effective to form either ductile or semiductile iron upon solidification; (b) heat treating the solidification of said melt by austempering to form a matrix consisting substantially of high carbon austenite, ferrite, and a cell boundary having unreacted low carbon austenite; (c) heating said austempered iron to a pearlite forming temperature and holding at said temperature to permit the unreacted low carbon austenite to form pearlite; and (d) cooling said heat treated iron to room temperature.
Claim 2
Independent Claim
150 words
A method of making a high strength, readily machinable ductile or semiductile cast iron, comprising: (a) forming a ferrous alloy melt consisting essentially of, by weight, 3-4% carbon, 2.0-3.0% silicon, 0.9% manganese, up to 0.02% phosphorous, up to 0.002% sulphur, up to 1% contaminants or impurities, 0-0.4% molybdenum, 0-3.0% nickel or copper, and the remainder essentially iron, said melt being subjected to a graphite modifying agent in an amount and for a period of time effective to form either ductile or semiductile iron upon solidification; (b) heat treating the solidification of said melt by austempering to form a matrix consisting substantially of high carbon austenite, ferrite, and a cell boundary having unreacted low carbon austenite; (c) heating said austempered iron to a pearlite forming temperature and holding at said temperature to permit the unreacted low carbon austenite to form pearlite; and (d) cooling said heat treated iron to room temperature.
Claim 3
Dependent Claim
52 words
The method as in claim 1, in which step (b) comprises heating to the temperature level of 1550°-1625° F. and holding said temperature for a period of time of 1.5 to 4 hours, downquenching to the temperature range of 460°-800° F. and holding at said latter temperature for 0.5 to 4 hours.
Claim 4
Dependent Claim
19 words
The method as in claim 2, in which said downquenching is at a rate of at least 550° F./minute.
Claim 5
Dependent Claim
25 words
The method as in claim 1, in which step (c) comprises heating to a temperature level of 1200°-1300° F. for a period of 3-5 minutes.
Claim 6
Dependent Claim
39 words
A cast iron made by the process of claim 1, the cast iron being characterized by a matrix of high carbon austenite and ferrite and 2-10% by volume pearlite and is subtantially devoid of unreacted low carbon retained austenite.
Claim 7
Dependent Claim
43 words
The cast iron as in claim 5, in which said iron has a yield strength of at least 90,000 psi, a tensile strength of at least 135 psi, an elongation of at least 5%, and a hardness of no greater than 290 BHN.
Claim 8
Dependent Claim
55 words
The cast iron as in claim 5, which has a machinability characteristic such that it can be machined with no greater than 0.001 inches of wear when cutting at a speed of 500 sfm, depth of cut of 0.06 inch, and a feed rate of 0.01 inch per revolution for a period of 0.5 hours.
References Cited (Backward Citations)
US3421886A
Cited
US3549431A
Cited
US3860457A
Cited
SU753923A1
Cited
US4227924A
Cited
DE2853870A1
Cited
JPS55152149A
Cited
JPS5893854A
Cited
EP0090654A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-12 | 1991-10-12 | 1992-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-12 | 1995-10-12 | 1996-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-12 | 1999-10-12 | 2000-04-12 | $7700.00 | Window Closed / Lapsed |