Cathodic electrode
Assignee: 3M Co
•
Filing: 1986-03-24
•
Granted: 1988-04-05
•
Expires: 2006-03-24
Abstract
Abstract A polymer bonded sheet product suitable for use as a cathodic electrode in a non-aqueous battery system wherein the cathodic electrode is a microporous sheet composed of from 2-30 weight percent polyethylene, 70-98 weight percent of electrically conductive and electrochemically active particulate material and from 0 to 5 weight percent of a plasticizer for the polyethylene.
Inventors
- 👤 Menahem Anderman
- 👤 Steven L. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 23:39
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/13; H01M4/136; H01M10/00; H01M10/05; H01M10/052; H01M4/36; H01M4/58; H01M4/581; H01M4/5815; H01M4/62; H01M4/621; H01M4/624; H01M4/625; H01M50/00; H01M50/40; H01M50/489; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
133 words
A cathodic electrode suitable for use in a non-aqueous battery system comprising at least one substantially homogeneous, microporous sheet product having a composition of from about 70-98 weight percent of particulate material comprising titanium disulfide having an average particle size of less than about 20 microns with said particulate material having up to about 30 weight percent of a conductive diluent having an average particle size of from 1 to 100 millimicrons, from about 2-30 weight percent of high density polyethylene having a weight average molecular weight of from about 150,000 to 5,000,000 and from 0 to about 5 weight percent of an organic plasticizer for said polyethylene; and a current collector composed of a conductive material, said collector being in intimate contact with each of said at least one microporous sheet product.
Claim 2
Dependent Claim
133 words
A cathodic electrode suitable for use in a non-aqueous battery system comprising at least one substantially homogeneous, microporous sheet product having a composition of from about 70-98 weight percent of particulate material comprising titanium disulfide having an average particle size of less than about 20 microns with said particulate material having up to about 30 weight percent of a conductive diluent having an average particle size of from 1 to 100 millimicrons, from about 2-30 weight percent of high density polyethylene having a weight average molecular weight of from about 150,000 to 5,000,000 and from 0 to about 5 weight percent of an organic plasticizer for said polyethylene; and a current collector composed of a conductive material, said collector being in intimate contact with each of said at least one microporous sheet product.
Claim 3
Dependent Claim
32 words
The electrode of claim 1 wherein the current collector is in the form of a screen, grid, expanded metal, foil or woven or nonwoven fabric formed from carbon or a conductive metal.
Claim 4
Dependent Claim
89 words
The electrode of claim 2 wherein the particulate material is composed of at least about 70 weight percent titanium disulfide, up to about 30 weight percent of a conductive diluent having an average particle size of from 1 to 100 millimicrons, and up to about 30 weight percent of at least one metal chalcogenide wherein the metal is selected from vanadium, hafnium, niobium, zirconium, tantalum mixtures of said metals with each other and with other metals, titanium selenide, titanium telluride, vanadium oxide, chromium oxide, molybdenum oxide and mixtures thereof.
Claim 5
Dependent Claim
21 words
The electrode of claim 3 wherein the polyethylene has a weight average molocular weight of from about 200,000 to about 500,000.
Claim 6
Dependent Claim
49 words
In a secondary non-aqueous battery comprising at least one pair of electrodes composed of anodic electrode and a cathodic electrode and a non-aqueous electrolyte composition, said anodic electrode formed from an alkali metal, wherein the improvement comprises having the cathodic electrode consist essentially of the product of claim 4.
Claim 7
Dependent Claim
49 words
In a secondary non-aqueous battery comprising at least one pair of electrodes composed of anonic electrode and a cathodic electrode and a non-aqueous electrolyte composition, said anodic electrode formed from an alkali metal, wherein the improvement comprises having the cathodic electrode consist essentially of the product of claim 2.
Claim 8
Dependent Claim
48 words
The electrode of claim 3 wherein the polyethylene is composed of a major amount of a polyethylene having a weight average molecular weight of at least 250,000 and a minor amount of a polyethylene having a weight average molecular weight of from about 100,000 to less than 250,000.
Claim 9
Dependent Claim
49 words
In a secondary non-aqueous battery comprising at least one pair of electrodes composed of anodic electrode and a cathodic electrode and a non-aqueous electrolyte composition, said anodic electrode formed from an alkali metal, wherein the improvement comprises having the cathodic electrode consist essentially of the product of claim 7.
Claim 10
Dependent Claim
33 words
The electrode of claim 3 composed of two sheet products and having the current collector therebetween; said sheet products forming a substantially unitary structure of total thickness of less than about 50 mils.
Claim 11
Dependent Claim
48 words
In a secondary non-aqueous battery comprising at least one pair of electrodes composed of anodic electrode and a cathodic electrode and anon-aqueous electrolyte composition, said anodic electrode formed from an alkali metal, wherein the improvement comprises having the cathodic electrode consist essentially of the product of claim 5.
Claim 12
Dependent Claim
58 words
The electrode of claim 1 wherein up to about 30 weight percent of said particulate material is selected from titanium selenide, titanium telluride, vanadium oxide, chromium oxide, molybdenum oxide and at least one metal chalcogenide wherein the metal is selected from vanadium, hafnium, niobium, zirconium, tantalum and mixtures of said metals with each other and with other metals.
Claim 13
Dependent Claim
49 words
In a secondary non-aqueous battery comprising at least one pair of electrodes composed of anodic electrode and a cathodic electrode and a non-aqueous electrolyte composition, said anodic electrode formed from an alkali metal, wherein the improvement comprises having the cathodic electrode consist essentially of the product of claim 3.
Claim 14
Dependent Claim
49 words
In a secondary non-aqueous battery comprising at least one pair of electrodes composed of anodic electrode and a cathodic electrode and a non-aqueous electrolyte composition, said anodic electrode formed from an alkali metal, wherein the improvement comprises having the cathodic electrode consist essentially of the product of claim 1.
Claim 15
Dependent Claim
134 words
A substantially homogeneous, microporous sheet product suitable for use in forming a cathodic polymer bonded electrode comprising (a) from 70-98 weight percent of particulate material comprising titanium disulfide having an average particle size of less than about 20 microns; said particulate material having up to about 30 weight percent of a conductive diluent having an average particle size of from about 1 to 100 millimicrons; (b) from about 2-30 weight percent of high density polyethylene having a weight average molecular weight of from about 200,000 to about 5,000,000; and (c) from 0 to 5 weight percent of an organic plasticizer for said polyethylene; said sheet having a void volume of at least about 15 volume percent and capable of exhibiting conductivity of at least about 0.15 reciprocal ohm-cm when placed in an electrical circuit.
Claim 16
Dependent Claim
134 words
A substantially homogeneous, microporous sheet product suitable for use in forming a cathodic polymer bonded electrode comprising (a) from 70-98 weight percent of particulate material comprising titanium disulfide having an average particle size of less than about 20 microns; said particulate material having up to about 30 weight percent of a conductive diluent having an average particle size of from about 1 to 100 millimicrons; (b) from about 2-30 weight percent of high density polyethylene having a weight average molecular weight of from about 200,000 to about 5,000,000; and (c) from 0 to 5 weight percent of an organic plasticizer for said polyethylene; said sheet having a void volume of at least about 15 volume percent and capable of exhibiting conductivity of at least about 0.15 reciprocal ohm-cm when placed in an electrical circuit.
Claim 17
Dependent Claim
61 words
The sheet of claim 14 wherein the particulate material further comprises up to about 30 weight percent of said particulate material composed of at least one metal chalcogenide wherein the metal is selected from vanadium, hafnium, niobium, zirconium, tantalum mixtures of said metals with each other and with other metals, titanium selenide, titanium telluride, vanadium oxide, molybdenum oxide and mixtures thereof.
Claim 18
Dependent Claim
21 words
The sheet of claim 15 wherein the polyethylene has a weight average molecular weight of from about 200,000 to about 500,000.
Claim 19
Dependent Claim
48 words
The sheet of claim 15 wherein the polyethylene is composed of a major amount of a polyethylene having a weight average molecular weight of at least 250,000 and a minor amount of a polyethylene having a weight average molecular weight of from about 100,000 to less than 250,000.
References Cited (Backward Citations)
US3060254A
Cited
US3099586A
Cited
US3351495A
Cited
US3814339A
Cited
US3898099A
Cited
US4124747A
Cited
US4091176A
Cited
US4169816A
Cited
US4223080A
Cited
US4322317A
Cited
US4562113A
Cited
US4550064A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-05 | 1991-10-05 | 1992-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-05 | 1995-10-05 | 1996-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-05 | 1999-10-05 | 2000-04-05 | $7700.00 | Window Closed / Lapsed |