Magnetic recording disk and sputtering process and apparatus for producing same
Assignee: Cyberdisk Inc
•
Filing: 1985-11-12
•
Granted: 1988-04-05
•
Expires: 2005-11-12
Abstract
Abstract The improved memory disk of the present invention comprises a substrate coated with chromium with preferably a layer of cobalt/nickel as the magnetic layer sealed with a protective coating of carbon. As a result of circumferential texturing, a circular anisotropic crystal growth has occurred during the sputtering with a circumferential alignment that provides an improved memory disk having a reduced amplitude modulation, an improved squareness of the hysteresis loop, e.g. lower switching field distribution and a high production relatively low cost production system. As a result, a higher recording linear bit density due to the high coercivity and low switching field distribution can be experienced with the magnetic disk of the present invention.
Inventors
- 👤 Virgle L. Hedgcoth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:18
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/64; G11B5/72; G11B5/73; G11B5/7368; G11B5/7373; G11B5/84; G11B5/851; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10S428/922; Y10S428/9265; Y10S428/928; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12806; Y10T428/12826; Y10T428/12847; Y10T428/12854; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
129 words
A magnetic thin film recording disk comprising: a flat smooth substrate characterized by a physically abraded surface having a uniform series of physical circumferential texturing of hills and valleys prior to any sputtering operation to encourage a circular anisotropic orientation of crystal growth during sputtering, the hill to valley distance being approximately 200 Angstroms; a thin film nucleating layer having a thickness within a range of 1000 to 5000 Angstroms disposed on the substrate; a thin film magnetic layer disposed on the nucleating layer with a circular anisotropic orientation of crystal growth within the range of 200 to 1500 Angstroms of thickness and reflected from one of cobalt, a cobalt/nickel alloy, a cobalt/chromium alloy and a cobalt/vanadium alloy; and a thin film protective coatng disposed on the magnetic layer.
Claim 2
Dependent Claim
129 words
A magnetic thin film recording disk comprising: a flat smooth substrate characterized by a physically abraded surface having a uniform series of physical circumferential texturing of hills and valleys prior to any sputtering operation to encourage a circular anisotropic orientation of crystal growth during sputtering, the hill to valley distance being approximately 200 Angstroms; a thin film nucleating layer having a thickness within a range of 1000 to 5000 Angstroms disposed on the substrate; a thin film magnetic layer disposed on the nucleating layer with a circular anisotropic orientation of crystal growth within the range of 200 to 1500 Angstroms of thickness and reflected from one of cobalt, a cobalt/nickel alloy, a cobalt/chromium alloy and a cobalt/vanadium alloy; and a thin film protective coatng disposed on the magnetic layer.
Claim 3
Dependent Claim
104 words
A magnetic thin film recording disk comprising: a flat smooth substrate characterized by a physically abraded surface having a uniform series of physical circumferential texturing of hills and valleys prior to any sputtering operation to encourage a circular anisotropic orientation of crystal growth during sputtering, the hill to valley distance being no greater than 500 Angstroms; a thin film nucleating layer disposed on the substrate; a thin film magnetic layer disposed on the nucleating layer with a circular anisotropic orientation of crystal growth within the range of 200 to 1500 Angstroms of thickness; and a thin film protective coating disposed on the magnetic layer.
Claim 4
Dependent Claim
104 words
A magnetic thin film recording disk comprising: a flat smooth substrate characterized by a physically abraded surface having a uniform series of physical circumferential texturing of hills and valleys prior to any sputtering operation to encourage a circular anisotropic orientation of crystal growth during sputtering, the hill to valley distance being no greater than 500 Angstroms; a thin film nucleating layer disposed on the substrate; a thin film magnetic layer disposed on the nucleating layer with a circular anisotropic orientation of crystal growth within the range of 200 to 1500 Angstroms of thickness; and a thin film protective coating disposed on the magnetic layer.
Claim 5
Dependent Claim
15 words
The invention of claim 2 wherein the nucleating layer is selected from chromium and titanium.
Claim 6
Dependent Claim
25 words
The invention of claim 2 wherein the magnetic layer is selected from one of cobalt, a cobalt/nickel alloy, a cobalt/chromum alloy and a cobalt/vanadium alloy.
Claim 7
Dependent Claim
22 words
The invention of claim 2 wherein the protective coating is selected from one of carbon, titanium carbide, boron carbide and tungsten carbide.
Claim 8
Dependent Claim
22 words
The invention of claim 2 wherein the physical abrading provides a radial roughness factor within the range of 50 to 500 angstrom.
Claim 9
Dependent Claim
26 words
The invention of claim 2 wherein the nucleating layer source is chromium, the magnetic layer source is a cobalt/nickel al-oy and the protective coating is carbon.
Claim 10
Dependent Claim
56 words
The invention of claim 7 wherein the thin film layers have a physical characteristic resulting from a direct current planar magnetron sputtering source process in a plasma gas within the pressure range of 2×10 -2 torr and 4×10 -2 torr to provide collisional scattering of sputtered atoms to avoid low angle of incidence of film nucleation.
Claim 11
Dependent Claim
14 words
The invention of claim 8 wherein the radial roughness factor is approximately 200 angstroms.
Claim 12
Dependent Claim
55 words
The invention of claim 9 wherein the protective coating of carbon has a layer thickness within the range of 200 to 800 angstrom, the nucleating layer of the chromium layer is within the range of 1000 to 5000 angstroms and the magnetic layer of cobalt/nickel alloy is within the range of 200 to 1500 angstroms.
Claim 13
Dependent Claim
16 words
The invention of claim 10 wherein the magnetic disk switching field distribution is less than 0.20.
Claim 14
Dependent Claim
108 words
In a magnetic thin film recording disk, the improvement comprising: a flat smooth substrate characterized by a physically abraded surface having a uniform series of physical circumferential texturing of hills and valleys prior to any sputtering operation to encourage a circular anisotropic orientation of crystal growth during sputtering, the hill to valley distance being no greater than 500 Angstroms; a thin film nucleating layer havng a thickness within the range of 1000 to 5000 Angstroms disposed on the substrate; and a thin film magnetic layer disposed on the nucleating layer with a circular anisotropic orientation of crystal growth within the range of 200 to 1500 Angstroms of thickness.
Claim 15
Dependent Claim
108 words
In a magnetic thin film recording disk, the improvement comprising: a flat smooth substrate characterized by a physically abraded surface having a uniform series of physical circumferential texturing of hills and valleys prior to any sputtering operation to encourage a circular anisotropic orientation of crystal growth during sputtering, the hill to valley distance being no greater than 500 Angstroms; a thin film nucleating layer havng a thickness within the range of 1000 to 5000 Angstroms disposed on the substrate; and a thin film magnetic layer disposed on the nucleating layer with a circular anisotropic orientation of crystal growth within the range of 200 to 1500 Angstroms of thickness.
Claim 16
Dependent Claim
22 words
The invention of claim 12 wherein the protective coating is selected from one of carbon, titanium carbide, boron carbide and tungsten carbide.
Claim 17
Dependent Claim
26 words
The invention of claim 12 wherein the nucleating layer source is chromium, the magnetic layer source is a cobalt/nickel alloy and the protective coating is carbon.
Claim 18
Dependent Claim
15 words
The invention of claim 14 wherein the peak to valley distance is approximately 200 Angstroms.
Claim 19
Dependent Claim
23 words
The invention of claim 15 wherein the protective coating of carbon has a layer thickness within the range of 200 to 800 Angstroms.
References Cited (Backward Citations)
US3161946A
Cited
US3019125A
Cited
US3342632A
Cited
US3515606A
Cited
US3520664A
Cited
US3787237A
Cited
US3516860A
Cited
US3996095A
Cited
US4079169A
Cited
JPS5418125A
Cited
US4245008A
Cited
US4254189A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-05 | 1991-10-05 | 1992-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-05 | 1995-10-05 | 1996-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-05 | 1999-10-05 | 2000-04-05 | $7700.00 | Window Closed / Lapsed |