Removing metal precipitates from semiconductor devices
Assignee: Delphi Technologies Inc
•
Filing: 1986-10-15
•
Granted: 1988-03-22
•
Expires: 2006-10-15
Abstract
Abstract Rapid thermal annealing, involving rapid heating to a temperature of between 550 degrees C. and 750 degree C. for between 30 and 90 seconds and rapid cooling, is used to dissolve the precipitates of transition metals which tend to occur in a silicon wafer and to keep such metals in solution after cooling. Such annealing can be used in the manufacture of bipolar transistors to limit the emitter-collector shorting caused by metallic precipitates. It is also useful more generally to improve the leakage current of p-n junctions either in diodes or as parts of bipolar or field-effect transistors.
Inventors
- 👤 Douglas R. Sparks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:38
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
70 words
A process of making a silicon wafer of a silicon device essentially free of transition metal precipitates which comprises the steps of heating the wafer rapidly to a temperature of between 550-750 degrees C., maintaining such temperatures for between 30-90 seconds, rapidly cooling the wafer for quenching the transition metal atoms in solution, and thereafter avoiding conditions in the further processing under which the metal atoms can reform into precipitates.
Claim 2
Dependent Claim
70 words
A process of making a silicon wafer of a silicon device essentially free of transition metal precipitates which comprises the steps of heating the wafer rapidly to a temperature of between 550-750 degrees C., maintaining such temperatures for between 30-90 seconds, rapidly cooling the wafer for quenching the transition metal atoms in solution, and thereafter avoiding conditions in the further processing under which the metal atoms can reform into precipitates.
Claim 3
Dependent Claim
38 words
The process of claim 1 in which the wafer is heated to said temperature from room temperature within approximately five to ten seconds and is cooled from said temperature to room temperature within approximately five to ten seconds.
Claim 4
Dependent Claim
18 words
The process of claim 1 in which such heating and cooling steps are repeated multiple times in succession.
Claim 5
Dependent Claim
14 words
The process of claim 2 in which said temperature is about 600 degrees Centigrade.
Claim 6
Dependent Claim
78 words
In the manufacture of a diffused base silicon junction transistor which involves successive base and emitter diffusion steps into a silicon wafer, the improvement which comprises a first rapid thermal annealing step before the emitter diffusion step to dissolve metal precipitates in the silicon wafer, a second rapid thermal annealing step after the emitter diffusion step, and subsequently avoiding heating the wafer under conditions apt to lead to the reformation of the metal precipitates in the silicon wafer.
Claim 7
Dependent Claim
78 words
In the manufacture of a diffused base silicon junction transistor which involves successive base and emitter diffusion steps into a silicon wafer, the improvement which comprises a first rapid thermal annealing step before the emitter diffusion step to dissolve metal precipitates in the silicon wafer, a second rapid thermal annealing step after the emitter diffusion step, and subsequently avoiding heating the wafer under conditions apt to lead to the reformation of the metal precipitates in the silicon wafer.
Claim 8
Dependent Claim
53 words
The improvement of claim 5 further characterized in that said rapid annealing steps involve heating the wafer in a few seconds to a temperature between 550 degrees C. and 750 degrees C., holding the wafer at such temperature for between thirty and ninety seconds, and cooling to room temperature in a few seconds.
Claim 9
Dependent Claim
28 words
The improvement of claim 5 in which the heating step occurs within approximately five to ten seconds and the cooling step occurs within approximately five to ten seconds.
Claim 10
Dependent Claim
39 words
The improvement of claim 5 in the manufacture of a diffused base silicon transistor which includes a silicon wafer which is gold-doped and the improvement is designed to maintain the gold in solution than as precipitates in the silicon.
Claim 11
Dependent Claim
14 words
The improvement of claim 7 in which said temperature is about 600 degrees Centigrade.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-22 | 1991-09-21 | 1992-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-22 | 1995-09-21 | 1996-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-22 | 1999-09-21 | 2000-03-22 | $7700.00 | Window Closed / Lapsed |