Method of reheating preforms for forming blow molded hot fillable containers
Assignee: Graham Packaging Pet Technologies Inc
•
Filing: 1986-06-24
•
Granted: 1988-03-15
•
Expires: 2006-06-24
Abstract
Abstract A hybrid reheating of polyester preforms which are to be stretch blown into containers wherein the reheating coupled with the controlled quick initiation of the blow stretch operation after final reheating produces a container which may be filled with a hot fill without there being any disadvantageous shrinkage of the container. The reheating is by way of a specific combination of quartz oven reheating and radio frequency reheating together with specific equilibrations of the temperature cross sectionally of the preform body. Polyester preforms may be reheated to a cross sectional center temperature ranging from 225° F. to 260° F. and stretch blow molded without undesirable surface crystallization occuring while the ability of the container to be filled with a hot filled substantially without shrinkage is increased.
Inventors
- 👤 Wayne N. Collette
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:49
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/42; B29C49/64; B29C49/6409; B29C35/00; B29C35/02; B29C35/08; B29C35/12; B29C49/6418; B29C49/6472; B29C49/648; B29K; B29K2067/00; B29K2667/00; B29K2995/00; B29K2995/0012; B29K2995/0017; Y; Y10; Y10S; Y10S264/00; Y10S264/46
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
166 words
A method of reheating a polyester preform for blow molding, said method comprising the steps of heating said polyester preform in a quartz infrared heater oven to a generally customary temperature for blow molding wherein the temperature of an outside surface of the preform is materially higher than the temperature of an inside surface of a like portion of the preform, transferring the reheated preform to a radio frequency heater and further heating the preform wherein the inside surface of the preform is heated at a greater rate than the outside surface of the preform until the temperature of the inside of the preform at least approaches the temperature of the outside, then transferring the thus heated preform to a blow mold for blow molding with the temperature of both the inside surface and the outside surface of the preform being above the temperature wherein crystallization would occur if the preform were heated to such temperature utilizing either quartz infrared heating or radio frequency heating independently.
Claim 2
Independent Claim
166 words
A method of reheating a polyester preform for blow molding, said method comprising the steps of heating said polyester preform in a quartz infrared heater oven to a generally customary temperature for blow molding wherein the temperature of an outside surface of the preform is materially higher than the temperature of an inside surface of a like portion of the preform, transferring the reheated preform to a radio frequency heater and further heating the preform wherein the inside surface of the preform is heated at a greater rate than the outside surface of the preform until the temperature of the inside of the preform at least approaches the temperature of the outside, then transferring the thus heated preform to a blow mold for blow molding with the temperature of both the inside surface and the outside surface of the preform being above the temperature wherein crystallization would occur if the preform were heated to such temperature utilizing either quartz infrared heating or radio frequency heating independently.
Claim 3
Dependent Claim
28 words
A method according to claim 1 wherein there is a partial equilibration of outside surface and inside surface temperatures during transfer of the preform to the blow mold.
Claim 4
Dependent Claim
88 words
A method according to claim 2 wherein during said heating of the preform utilizing said quartz infrared heater the temperature of the preform inside surface remains below the temperature of the center of the preform, during said radio frequency heating of the preform the temperature of the inside surface of the preform but remains below the temperature of the outside surface of the preform, and during said partial equilibration the temperature of the inside surface of the preform exceeds the temperature of the outside surface of the preform.
Claim 5
Dependent Claim
23 words
A method according to claim 3 wherein during said partial equilibration the temperature of the inside surface of the preform continues to increase.
Claim 6
Dependent Claim
34 words
A method according to claim 3 wherein during said partial equilibration the temperature of the inside surface of the preform continues to increase while the temperature of the outside surface of the preform decreases.
Claim 7
Dependent Claim
22 words
A method according to claim 3 wherein during said partial equilibration the temperature of the center of the preform continues to increase.
Claim 8
Dependent Claim
33 words
A method according to claim 3 wherein during said partial equilibration the temperature of the center of the preform continues to increase and approaches the temperature of the outside surface of the preform.
Claim 9
Dependent Claim
21 words
A method according to claim 2 wherein said quartz infrared heating is performed in two steps separated by an equilibration step.
Claim 10
Dependent Claim
26 words
A method according to claim 2 wherein the ratio of quartz infrared heating time to radio frequency time to equilibration time ranges from 10:1:1 to 20:1:10.
Claim 11
Dependent Claim
27 words
A method according to claim 2 wherein the ratio of quartz infrared heating time to radio frequency time to equilibration time is on the order of 15:1:3.
Claim 12
Dependent Claim
21 words
A method according to claim 2 wherein said equilibration occurs as the heated preform is being transferred to a molding position.
Claim 13
Dependent Claim
38 words
A method according to claim 1 wherein there is a partial equilibration of outside surface and inside surface temperatures during transfer of the preform to the blow mold with the temperature of the center of the preform increasing.
Claim 14
Dependent Claim
38 words
A method according to claim 1 wherein there is a partial equilibration of outside surface and inside surface temperatures during transfer of the preform to the blow mold with the temperature of the inside surface continuing to increase.
Claim 15
Dependent Claim
50 words
A method according to claim 1 wherein there is a partial equilibration of outside surface and inside surface temperatures during transfer of the preform to the blow mold with both the temperature of the center of the preform and the temperature of the inside of the preform continuing to increase.
Claim 16
Dependent Claim
61 words
A method according to claim 1 wherein during said heating of the preform utilizing said quartz infrared heater the temperature of the preform inside surface remains below the temperature of the center of the preform, and during said radio frequency heating of the preform the temperature of the inside surface of the preform rises above the average temperature of the preform.
Claim 17
Dependent Claim
73 words
A method according to claim 1 wherein during said heating of the preform utilizing said quartz infrared heater the temperature of the preform inside surface remains below the temperature of the center of the preform, and during said radio frequency heating of the preform the temperature of the inside surface of the preform rises above the average temperature of the preform but remains below the temperature of the outside surface of the preform.
Claim 18
Dependent Claim
33 words
A method according to claim 1 wherein the heated preform when presented to a blow mold has an inside surface temperature which is the greatest and a center temperature which is the least.
Claim 19
Dependent Claim
27 words
A method according to claim 1 wherein the temperature of the heated preform at the cross sectional center is on the order of 225° to 260° F.
Claim 20
Dependent Claim
52 words
A method according to claim 1 wherein the temperature of the heated preform at the cross sectional center is on the order of 225° to 260° F. as compared to a permissible central preform temperature of 200° to 210° F. for quartz heating and 210° to 220° F. for radio frequency heating.
Claim 21
Dependent Claim
34 words
A method according to claim 1 wherein said reheating method is particularly adapted for use in reheating a preform which is to be blow molded into a container which has acceptable hot fill performance.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-15 | 1991-09-14 | 1992-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-15 | 1995-09-14 | 1996-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-15 | 1999-09-14 | 2000-03-15 | $7700.00 | Window Closed / Lapsed |