Wear resistant coating and process
Assignee: Wall Colmonoy Corp
•
Filing: 1987-05-04
•
Granted: 1988-03-15
•
Expires: 2007-05-04
Abstract
Abstract A composite article comprising a metallic substrate having an improved ductile wear and corrosion resistant surface coating thereon and metallurgically bonded thereto in which the coating comprises a nickel-chromium-tungsten base alloy matrix having uniformly dispersed therethrough a plurality of primary wear resistant particles such as tungsten carbide, for example, and secondary chromium and/or tungsten carbide crystals. The invention further encompasses the method of making the composite article by applying a particulated mixture of the metal alloy and primary wear resistant particles preferably by the Plasma Transferred Arc technique on the surface of a metallic substrate.
Inventors
- 👤 Samuel C. DuBois
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 18:04
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/02; C23C4/04; C23C4/06
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
183 words
A method of applying a wear and corrosion resistant alloy layer on a metallic substrate which comprises the steps of forming a powder mixture containing about 40% to about 85% by weight of prealloyed particles and about 60% to about 15% by weight of primary wear resistant particles, said prealloyed particles containing from about 0.5% to about 1.7% by weight carbon, about 22% to about 36% by weight chromium, about 0.5% to about 2% by weight boron, about 1% to about 2.8% by weight silicon, up to a maximum of about 5% by weight iron, about 3% to about 14% by weight tungsten, up to a maximum of about 2% by weight cobalt, up to a maximum of about 2% by weight of conventional residuals and impurities and the balance comprising nickel; heating said powder mixture to a temperature of at least about 2,350° F. and effecting a melting of said prealloyed particles and applying the heated said powder mixture in the presence of an inert gas atmosphere to a metallic substrate in the form of a layer and thereafter cooling said layer.
Claim 2
Independent Claim
183 words
A method of applying a wear and corrosion resistant alloy layer on a metallic substrate which comprises the steps of forming a powder mixture containing about 40% to about 85% by weight of prealloyed particles and about 60% to about 15% by weight of primary wear resistant particles, said prealloyed particles containing from about 0.5% to about 1.7% by weight carbon, about 22% to about 36% by weight chromium, about 0.5% to about 2% by weight boron, about 1% to about 2.8% by weight silicon, up to a maximum of about 5% by weight iron, about 3% to about 14% by weight tungsten, up to a maximum of about 2% by weight cobalt, up to a maximum of about 2% by weight of conventional residuals and impurities and the balance comprising nickel; heating said powder mixture to a temperature of at least about 2,350° F. and effecting a melting of said prealloyed particles and applying the heated said powder mixture in the presence of an inert gas atmosphere to a metallic substrate in the form of a layer and thereafter cooling said layer.
Claim 3
Dependent Claim
26 words
The method as described in claim 1 in which the step of heating and applying said powder mixture is performed by a plasma transferred arc system.
Claim 4
Dependent Claim
25 words
The method as described in claim 1 including the further step of applying a plurality of said layer in overlying relationship on the metallic substrate.
Claim 5
Dependent Claim
93 words
The method as defined in claim 1 in which said prealloyed powder particles contain about 0.9% to about 1.3% by weight carbon, about 27% to about 31% by weight chromium, about 1% to about 1.5% by weight boron, about 1.5% to about 2.25% by weight silicon, up to a maximum of about 3% by weight iron, about 6% to about 9% by weight tungsten, up to a maximum of about 0.2% by weight cobalt, up to a maximum of about 0.5% by weight of conventional residuals and impurities and the balance comprising nickel.
Claim 6
Dependent Claim
78 words
The method as defined in claim 1 in which said prealloyed powder particles contain about 1.1% by weight carbon, about 29% by weight chromium, about 1.3% by weight boron, about 1.95% by weight silicon, up to a maximum of about 2% by weight iron, about 7.5% by weight tungsten, up to a maximum of about 0.2% by weight cobalt, up to a maximum of about 0.5% by weight of conventional residuals and impurities and the balance comprising nickel.
Claim 7
Dependent Claim
32 words
The method as defined in claim 1 in which said primary wear resistant particles are selected from the group consisting of tungsten carbide, chromium boride, chromium carbide, titanium carbide and mixtures thereof.
Claim 8
Dependent Claim
26 words
The method as described in claim 1 in which the step of heating said powder mixture is performed to a temperature up to about 7,000° F.
Claim 9
Dependent Claim
32 words
The method as described in claim 1 in which the metallic substrate is selected from the group consisting of SAE 4140 steels, SAE 4130 steels, 400 martensitic and 300 austenitic stainless steels.
Claim 10
Dependent Claim
17 words
The method as described in claim 1 in which said primary wear resistant particles comprise tungsten carbide.
Claim 11
Dependent Claim
28 words
The method as described in claim 1 in which the particles of said powder mixture are of a size ranging from about 80 up to about 325 mesh.
Claim 12
Dependent Claim
27 words
The method as described in claim 1 in which the particles of said powder mixture are of a size ranging from about 100 to about 270 mesh.
Claim 13
Dependent Claim
29 words
The method as described in claim 1 in which the step of applying the heated said particles is performed to produce a layer up to about 0.0625 inch thick.
Claim 14
Dependent Claim
38 words
The method as described in claim 1 in which the step of applying the heated said particles is performed to apply a plurality of successive overlying layers of a combined thickness up to about 0.125 inch or greater.
Claim 15
Dependent Claim
63 words
A composite article having a wear and corrosive resistant layer on at least a portion of the surface thereof produced by the method of claim 1 in which said layer is characterized by a nickel-chromium-tungsten base alloy matrix metallurgically bonded to the substrate having substantially uniformly distributed therethrough said primary wear resistant particles in combination with secondary chromium carbide and/or tungsten carbide crystals.
Claim 16
Dependent Claim
161 words
A powder mixture adapted for application by the Plasma Transferred Arc technique to a metallic substrate for forming a metallurgically bonded wear and corrosive resistant layer comprising a nickel-chromium-tungsten base alloy matrix having substantially uniformly dispersed therethrough primary wear resistant particles in combination with secondary chromium carbide and/or tungsten carbide crystals comprising a mixture containing about 40% to about 85% by weight of prealloyed particles and about 60% to about 15% by weight primary wear resistant particles, said prealloyed particles containing from about 0.5% to about 1.7% by weight carbon, about 22% to about 36% by weight chromium, about 0.5% to about 2% by weight boron, about 1% to about 2.8% by weight silicon, up to a maximum of about 5% by weight iron, about 3% to about 14% by weight tungsten, up to a maximum of about 2% by weight cobalt, up to a maximum of about 2% by weight of conventional residuals and impurities and the balance comprising nickel.
Claim 17
Dependent Claim
161 words
A powder mixture adapted for application by the Plasma Transferred Arc technique to a metallic substrate for forming a metallurgically bonded wear and corrosive resistant layer comprising a nickel-chromium-tungsten base alloy matrix having substantially uniformly dispersed therethrough primary wear resistant particles in combination with secondary chromium carbide and/or tungsten carbide crystals comprising a mixture containing about 40% to about 85% by weight of prealloyed particles and about 60% to about 15% by weight primary wear resistant particles, said prealloyed particles containing from about 0.5% to about 1.7% by weight carbon, about 22% to about 36% by weight chromium, about 0.5% to about 2% by weight boron, about 1% to about 2.8% by weight silicon, up to a maximum of about 5% by weight iron, about 3% to about 14% by weight tungsten, up to a maximum of about 2% by weight cobalt, up to a maximum of about 2% by weight of conventional residuals and impurities and the balance comprising nickel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-15 | 1991-09-14 | 1992-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-15 | 1995-09-14 | 1996-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-15 | 1999-09-14 | 2000-03-15 | $7700.00 | Window Closed / Lapsed |