US4729972A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High toughness ceramics and process for the preparation thereof
Assignee: Hitachi Ltd
•
Filing: 1986-01-06
•
Granted: 1988-03-08
•
Expires: 2006-01-06
Abstract
Abstract The present invention relates to a sintered product containing silicon carbide as a main component which comprises a phase(a) containing at least one metal selected from among Al, Sc, Y and rare earth elements and oxygen, a particle phase(b) comprising at least one metal carbide selected from among carbides of Ti, Zr, Hf, Va, Nb, Ta, W and the like, a composite particle phase(c) comprising said phase(a) and said phase(b) surrounding the phase(a) and silicon carbide matrix(d) in which the above phase(a), (b) and (c) are dispersed. The silicon carbide sintered product of the present invention exhibits a remarkably high strength and a remarkably high toughness which have not been attained up to this time, so that it can form various heat-resistant structural materials having a high reliability.
Inventors
- 👤 Hironori Kodama
- 👤 Akihiro Gotoo
- 👤 Tadahiko Miyoshi
- 👤 Hiroshi Sakamoto
- 👤 Takaaki Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:03
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/575
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
115 words
A high toughness ceramic consisting essentially of 0.05 to 10 volume % of a phase (a) of at least one of a silicate or an oxide of at least one element selected from the group consisting of aluminum, scandium, yttrium and a rare earth element, 5 to 40 volume % of a particle phase (b) of at least one metal carbide other than silicon carbide, 5 to 30 volume % of a composite particle phase (c) of a portion of said phase (a) and said particle phase (b) surrounding said portion of the phase (a) and a balance of a silicon carbide matrix (d) in which the above phases (a), (b) and (c) are dispersed.
Claim 2
Dependent Claim
115 words
A high toughness ceramic consisting essentially of 0.05 to 10 volume % of a phase (a) of at least one of a silicate or an oxide of at least one element selected from the group consisting of aluminum, scandium, yttrium and a rare earth element, 5 to 40 volume % of a particle phase (b) of at least one metal carbide other than silicon carbide, 5 to 30 volume % of a composite particle phase (c) of a portion of said phase (a) and said particle phase (b) surrounding said portion of the phase (a) and a balance of a silicon carbide matrix (d) in which the above phases (a), (b) and (c) are dispersed.
Claim 3
Dependent Claim
37 words
A high toughness ceramic as set forth in claim 1, wherein the phase (a) consists essentially of a silicate of at least one element selected from the group consisting of aluminum, scandium, yttrium and rare earth elements.
Claim 4
Dependent Claim
21 words
A high toughness ceramic as set forth in claim 2, wherein the particle phase (a) consists essentially of a silicate glass.
Claim 5
Dependent Claim
25 words
A high toughness ceramic as set forth in claim 1, wherein the particle phase (b) has an average particle size of 1 to 20 μm.
Claim 6
Dependent Claim
25 words
A high toughness ceramic as set forth in claim 1, wherein the silicon carbide matrix(d) has an average particle size of 0.2 to 5 μm.
Claim 7
Dependent Claim
45 words
A high toughness ceramic as set forth in claim 1, wherein the composite particle phase (c) which has an average particle size of 30 to 150 μm is present in an amount of at least 50% by volume of total amount of particle phase (c).
Claim 8
Dependent Claim
61 words
A high toughness ceramic as set forth in claim 1, wherein the composite particle phase (c) is present in an amount of 5 to 30% by volume in the ceramic and at least 50% by volume of the total amount of particle phase (b) is present as the composite particle phase (c) having average particle size of 30 to 150 μm.
Claim 9
Dependent Claim
28 words
A high toughness ceramic as set forth in claim 1, wherein the phase (a) consists essentially of an oxide of aluminum, scandium, yttrium or a rare earth metal.
Claim 10
Dependent Claim
51 words
A high toughness ceramic as set forth in claim 1, wherein the phase (a) consists essentially of aluminum oxide or yttrium oxide and the particle phase (b) consists essentially of a carbide of at least one element selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum and wolfram.
Claim 11
Dependent Claim
33 words
A high toughness ceramic as set forth in claim 7, wherein the phase (a) consists essentially of yttrium oxide and the particle phase (b) consists essentially of a carbide of titanium and/or vanadium.
Claim 12
Dependent Claim
192 words
A process for the preparation of a high toughness ceramic which comprises hot-pressing a mixture consisting essentially of (1) at least one metal selected from the group consisting of aluminum, scandium, yttrium and rare earth elements or a hydride, carbide, nitride, silicide or oxide thereof, (2) at least one metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, and wolfram or a hydride, nitride, silicide or oxide thereof having an average particle size of 5 to 100 μm and (3) a silicon carbide powder having an average particle size of 0.1 to 2 μm, to a temperature of 1900° to 2300° C. either under vacuum or in an inert gas atmosphere, and thereafter cooling said mixture, wherein said mixture is selected such that said high toughness ceramic obtained contains 0.05 to 10 volume % of oxide or silicate of at least one metal selected from the group consisting of aluminum, scandium, yttrium and rare earth elements, 5 to 40 volume % of carbide of at least one metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum and wolfram, and the remainder being silicon carbide.
Claim 13
Dependent Claim
192 words
A process for the preparation of a high toughness ceramic which comprises hot-pressing a mixture consisting essentially of (1) at least one metal selected from the group consisting of aluminum, scandium, yttrium and rare earth elements or a hydride, carbide, nitride, silicide or oxide thereof, (2) at least one metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, and wolfram or a hydride, nitride, silicide or oxide thereof having an average particle size of 5 to 100 μm and (3) a silicon carbide powder having an average particle size of 0.1 to 2 μm, to a temperature of 1900° to 2300° C. either under vacuum or in an inert gas atmosphere, and thereafter cooling said mixture, wherein said mixture is selected such that said high toughness ceramic obtained contains 0.05 to 10 volume % of oxide or silicate of at least one metal selected from the group consisting of aluminum, scandium, yttrium and rare earth elements, 5 to 40 volume % of carbide of at least one metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum and wolfram, and the remainder being silicon carbide.
Claim 14
Dependent Claim
54 words
A process for the preparation of a high toughness ceramic as set forth in claim 11, which comprises adding a metallic yttrium and a metallic titanium and/or metallic vanadium to the silicon carbide, hot-pressing the obtained mixture while heating to a temperature of 2000° to 2200° C. and immediately and slowly cooling the mixture.
Claim 15
Dependent Claim
24 words
A high toughness ceramic as set forth in claim 1, wherein said phase (a) fills grain boundaries between particles of said particle phase (b).
Claim 16
Dependent Claim
25 words
A high toughness ceramic as set forth in claim 1, wherein said high toughness ceramic has a toughness of at least 10 MN/m 3/2 .
Claim 17
Dependent Claim
25 words
A high toughness ceramic as set forth in claim 14, wherein said high toughness ceramic has a strength of at least 30 KG/mm 2 .
Claim 18
Dependent Claim
49 words
A process for the preparation of a high toughness ceramic as set forth in claim 11, wherein said mixture is hot-pressed while increasing the temperature of said mixture at a rate of 20° to 40° C./min. to a temperature of 2000° to 2200° C. and immediately cooling the mixture.
Claim 19
Dependent Claim
29 words
A process for the preparation of a high toughness ceramic as set forth in claim 16, wherein said mixture is cooled at a rate of 20° to 40° C./min.
Claim 20
Dependent Claim
146 words
A process for the preparation of a high toughness ceramic as set forth in claim 11, wherein said mixture is selected such that said high toughness ceramic obtained consists essentially of 0.05 to 10 volume % of oxide of at least one metal selected from the group consisting of aluminum, scandium, yttrium and rare earth elements, 5 to 40 volume % of carbide of at least one metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum and wolfram, the remainder being silicon carbide, and wherein at least a portion of said oxide of at least one metal selected from the group consisting of aluminum, scandium, yttrium and rare earth elements fills grain boundaries between particles of at least a portion of said carbide of at least one metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum and wolfram.
Claim 21
Dependent Claim
9 words
The product formed by the process of claim 11.
Claim 22
Dependent Claim
9 words
The product formed by the process of claim 12.
Claim 23
Dependent Claim
9 words
The product formed by the process of claim 16.
Claim 24
Dependent Claim
9 words
The product formed by the process of claim 17.
Claim 25
Dependent Claim
9 words
The product formed by the process of claim 18.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-08 | 1991-09-07 | 1992-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-08 | 1995-09-07 | 1996-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-08 | 1999-09-07 | 2000-03-08 | $7700.00 | Window Closed / Lapsed |