Abstract A method is disclosed for making a dual microstructure titanium based engine valve, wherein a first zone of the valve contains essentially a mixture of fine, equiaxed alpha and transformed beta crystalline grains which exhibit high tensile strength and high fatigue resistance, and a second zone of the valve which contains essentially a colony type microstructure exhibiting resistance to high temperature creep. The method comprises: (a) preparing a valve stock of forgeable mixed phase alpha/beta titanium based material; (b) hot working said first zone at a temperature below the beta transus temperature, (c) forging said second zone and, either simultaneously with said forging or subsequent thereto, heat treating said second zone at a temperature above (e.g., 25°-200° F. above) the beta transus temperature for a period of time to achieve beta processing followed by cooling to 1400° F. at a rate of 0.1°-10.0° F./second; and (d) heat treating, immediately subsequent to either step (b) or step (c), at least the first zone at a temperature below the beta transus temperature (e.g., 25°-200° F. below) for a period of time to achieve alpha/beta processing.
A unitary dual microstructure engine valve construction consisting of a titanium alloy body having (i) a stem portion with a fine grained, equiaxed mixture of alpha titanium regions and titanium colony microstructure regions exhibiting, at a temperature of 1400° F., a tensile strength of at least 20 ksi and a fatigue strength of at least 10 ksi; and (ii) a head portion with only a substantially uniform titanium colony microstructure region exhibiting a creep resistance, at a temperature of 1400° F., of only 1.0% strain under 4 ksi for at least 100 hours.
Claim 2
Dependent Claim
93 words
A unitary dual microstructure engine valve construction consisting of a titanium alloy body having (i) a stem portion with a fine grained, equiaxed mixture of alpha titanium regions and titanium colony microstructure regions exhibiting, at a temperature of 1400° F., a tensile strength of at least 20 ksi and a fatigue strength of at least 10 ksi; and (ii) a head portion with only a substantially uniform titanium colony microstructure region exhibiting a creep resistance, at a temperature of 1400° F., of only 1.0% strain under 4 ksi for at least 100 hours.
Claim 3
Dependent Claim
57 words
The engine valve construction of claim 1, in which said stem is connected to said head by a fillet portion, the fillet portion consisting of the same mixed regions as said stem, and the fillet portion exhibiting at 1400° F. a tensile strength of at least 20 ksi and a fatigue strength of at least 10 ksi.