Process for production of continuous inorganic fibers and apparatus therefor
Assignee: Nitivy Co Ltd
•
Filing: 1986-01-02
•
Granted: 1988-02-09
•
Expires: 2006-01-02
Abstract
Abstract A process for the production of continuous inorganic fibers is disclosed which comprises causing a spinning dope composed of a water-soluble organic polymer, a water-soluble inorganic salt capable of forming a refractory inorganic oxide, additives, and water and adjusted to a viscosity of 200 to 2000 poises at 20° C. to be dry spun by the use of a spinning nozzle containing a plurality of spinnerets each provided on the spinning dope outlet side of a nozzle plate with a protuberance having a wall thickness of not more than 0.5 mm at the tip thereof and subjecting the spun threads of the spinning dope to a thermal treatment. An apparatus for working the process is also disclosed which is provided with a spinning nozzle having a plurality of spinnerets bored through a nozzle plate and severally through protuberances formed on the spinning dope outlet side of the nozzle plate in such a manner that the walls of the protuberances surrounding the spinnerets have a thickness of not more than 0.5 mm at the tips of the protuberances and the spinnerets so piercing the protuberances are radially constricted on the spinning dope outlet side.
Inventors
- 👤 Mitsuo Yamashita
- 👤 Akihisa Shirasaka
- 👤 Ichiro Nagashima
- 👤 Katunosin Isogai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:30
CPC Classifications
D; D01; D01D; D01D4/00; D01D4/02; C; C04; C04B; C04B35/00; C04B35/622; C04B35/62227; C04B35/62231; C04B35/62236; C04B35/6225
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
253 words
A method for the production of continuous inorganic fibers whereby the spinning dope does not adhere to the nozzle plate, which comprises the steps of dry spinning a spinning dope composed of a water-soluble organic polymer, a water-soluble inorganic salt capable of forming a refractory inorganic oxide, one or more additives selected from the group consisting of chlorides, sulfates, nitrates, acetates, and formates of magnesium, chromium, nickel, iron, cobalt, and yttrium, and oxides of silicon, and water, and adjusted to a viscosity of 700 to 2000 poises at 20° C., with a spinning nozzle having a plurality of spinnerets formed in a nozzle plate and each provided on the spinning dope outlet side of said nozzle plate with a protuberance having a wall thickness of not more than 0.5 mm at the leading end thereof, wherein said spinnerets have dimensions such that the ratio of length to inside diameter is in the range of 2.0 to 40, wherein the length L of said protuberances from the surface of said nozzle plate is not less than 0.5 times the outside diameter D of said protuberances at the leading ends thereof and wherein the outside diameter D' of said protuberances at the basal portions thereof and the outside diameter D of said protuberances at the leading ends thereof are such that the magnitude of (D'-D)/2 is within the length L of said protuberances from the surface of said nozzle plate, and subsequently subjecting the resultant spun threads of said spinning dope to a thermal treatment.
Claim 2
Independent Claim
253 words
A method for the production of continuous inorganic fibers whereby the spinning dope does not adhere to the nozzle plate, which comprises the steps of dry spinning a spinning dope composed of a water-soluble organic polymer, a water-soluble inorganic salt capable of forming a refractory inorganic oxide, one or more additives selected from the group consisting of chlorides, sulfates, nitrates, acetates, and formates of magnesium, chromium, nickel, iron, cobalt, and yttrium, and oxides of silicon, and water, and adjusted to a viscosity of 700 to 2000 poises at 20° C., with a spinning nozzle having a plurality of spinnerets formed in a nozzle plate and each provided on the spinning dope outlet side of said nozzle plate with a protuberance having a wall thickness of not more than 0.5 mm at the leading end thereof, wherein said spinnerets have dimensions such that the ratio of length to inside diameter is in the range of 2.0 to 40, wherein the length L of said protuberances from the surface of said nozzle plate is not less than 0.5 times the outside diameter D of said protuberances at the leading ends thereof and wherein the outside diameter D' of said protuberances at the basal portions thereof and the outside diameter D of said protuberances at the leading ends thereof are such that the magnitude of (D'-D)/2 is within the length L of said protuberances from the surface of said nozzle plate, and subsequently subjecting the resultant spun threads of said spinning dope to a thermal treatment.
Claim 3
Dependent Claim
41 words
A method according to claim 1, wherein said water-soluble organic polymer is one member or a mixture of two or more members selected from the group consisting of polyvinyl alcohol, partially saponified polyvinyl alcohol, polyethylene oxide, polyvinyl pyrrolidone, polyacrylates, and polyacrylamides.
Claim 4
Dependent Claim
34 words
A method according to claim 2, wherein said partially saponified polyvinyl alcohol has a saponification degree in the range of 80 to 97 mol % and an average polymerization degree of 1000 to 2500.
Claim 5
Dependent Claim
46 words
A method according to claim 1, wherein said water-soluble inorganic salt capable of forming a refractory inorganic oxide is one member or a mixture of two or more members selected from the group consisting of basic chlorides, basic acetates, and basic nitrates of aluminum and zirconium.
Claim 6
Dependent Claim
29 words
A method according to claim 4, wherein said basic chloride of aluminum is aluminum oxychloride represented by the rational formula of Al 2 (OH) n Cl m (wherein n+m=6).
Claim 7
Dependent Claim
22 words
A method according to claim 5, wherein said aluminum oxychloride has an Al/Cl molar ratio in the range of 1.7 to 2.1.
Claim 8
Dependent Claim
23 words
A method according to claim 1, wherein said oxide of silicon is a colloidal solution having finely divided SiO 2 dispersed in water.
Claim 9
Dependent Claim
68 words
A method according to claim 1, wherein said water-soluble organic polymer, said water-soluble inorganic salt capable of forming a refractory inorganic oxide, and said additive are used in proportions such that said water-soluble organic polymer accounts for 5 to 30% by weight of the total of said three components and said water-soluble inorganic salt and said additive jointly account for the balance to make up 100% by weight.
Claim 10
Dependent Claim
50 words
A method according to claim 1, wherein said spinning dope is an aqueous solution containing said additive in a proportion of not more than 30% by weight based on the amount of said water-soluble inorganic salt capable of forming a refractory inorganic oxide (both as oxide) in said spinning dope.
Claim 11
Dependent Claim
24 words
A method according to claim 1, wherein said spinning dope for dry spinning has a viscosity of 700 to 1400 poises at 20° C.
Claim 12
Dependent Claim
33 words
A method according to claim 1, wherein the viscosity of said spinning dope is adjusted by subjecting said mixed aqueous solution containing the components of said spinning dope to concentration under a vacuum.
Claim 13
Dependent Claim
51 words
A method according to claim 1, wherein the viscosity of said spinning dope is adjusted by first subjecting said mixed aqueous solution of the components of said spinning dope to concentration under a vacuum and subsequently allowing the concentrated aqueous solution to age at a temperature of 20° to 60° C.
Claim 14
Dependent Claim
24 words
A method according to claim 11, wherein said concentration under a vacuum is carried out in the presence of an alcohol type defoaming agent.
Claim 15
Dependent Claim
25 words
A method according to claim 1, wherein said spinnerets are bored through protuberances and are provided on the spinning dope outlet side with constricted portions.
Claim 16
Dependent Claim
26 words
A method according to claim 1, wherein the wall thickness of protuberances at the leading ends thereof is in the range of 0.02 to 0.2 mm.
Claim 17
Dependent Claim
29 words
A method according to claim 1, wherein said spinning dope is fed to said spinning nozzle with a pressure in the range of 1 to 30 Kg/cm 2 .
Claim 18
Dependent Claim
24 words
A method according to claim 1, wherein said spinning dope is dry spun at a temperature in the range of 30° to 90° C.
References Cited (Backward Citations)
US888260A
Cited
US1310509A
Cited
US1672644A
Cited
US2034009A
Cited
US2544763A
Cited
US2925412A
Cited
US3210451A
Cited
US3176342A
Cited
GB1107861A
Cited
US3379811A
Cited
US3465618A
Cited
US3456292A
Cited
US3469280A
Cited
GB1208717A
Cited
GB1360200A
Cited
US3842151A
Cited
US3950478A
Cited
US3952078A
Cited
DE2324599A1
Cited
GB1400982A
Cited
GB1470292A
Cited
US4126656A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-08 | 1991-08-10 | 1992-02-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-08 | 1995-08-10 | 1996-02-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-08 | 1999-08-10 | 2000-02-09 | $7700.00 | Window Closed / Lapsed |