Porous material and tubular filter made of said material
Assignee: Ceraver SA
•
Filing: 1984-10-18
•
Granted: 1988-02-09
•
Expires: 2004-10-18
Abstract
Abstract A porous material made from sintered inorganic particles. It has an open pososity of 30% to 40% by volume, a permeability to water at 20° ranging from 0.6 to 60 m 3 /h.m 2 .bar for a wall thickness of 2 cm as the average pore diameter varies from 2 to 20 microns and a crushing resistance, measured under conditions of isostatic compression, of 4×10 8 to 5×10 8 N/m 2 .
Inventors
- 👤 Alain Auriol
- 👤 Jacques Gillot
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:53
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/02; B01D71/024; B01D39/00; B01D39/14; B01D39/20; B01D39/2068; B01D39/2072; B01D39/2075; B01D71/025; C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/622; C04B35/626; C04B35/62605; C04B35/62645; C04B35/62665; C04B38/00; C04B2111/00; C04B2111/00474; C04B2111/00612; C04B2111/00793; C04B2201/00; C04B2235/00; C04B2235/02; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/5463; C04B2235/5472; C04B2235/60; C04B2235/602; C04B2235/6021; C04B2235/70; C04B2235/94; C04B2235/96
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
68 words
A porous material formed of sintered alumina particles, of a purity at least equal to 99.9% by weight, said material having an open porosity of 30% to 40% by volume, pores of average diameter of between 2 to 20 microns and wherein said porous material is resistant to crushing, having a crushing strength measured under conditions of isostatic compression of 4×10 8 to 5×10 8 N/m 2 .
Claim 2
Dependent Claim
68 words
A porous material formed of sintered alumina particles, of a purity at least equal to 99.9% by weight, said material having an open porosity of 30% to 40% by volume, pores of average diameter of between 2 to 20 microns and wherein said porous material is resistant to crushing, having a crushing strength measured under conditions of isostatic compression of 4×10 8 to 5×10 8 N/m 2 .
Claim 3
Dependent Claim
24 words
A porous material according to claim 1, characterized in that its bending strength lies in the range 2.5 to 3.5×10 7 N/m 2 .
Claim 4
Dependent Claim
47 words
A porous material according to claim 2, characterized in that it has a permeability to water at 20° C. ranging from 0.6 to 60 m 3 /h.m 2 .bar for a wall thickness of 1 centimeter as the average pore diameter ranges from 2 to 20 microns.
Claim 5
Dependent Claim
32 words
A porous material according to any one of claims 1 or 3, characterized in that it is made up from a mixture of metallic oxides including more than 20% by weight alumina.
Claim 6
Dependent Claim
139 words
A tubular filter comprising a thick porous support layer formed of sintered alumina particles of a purity at least equal to 99.9% by weight, said alumina having an open porosity of 30% to 40% by volume, the average diameter of the pores being between 2 and 20 microns and having having a resistance to crushing, measured under conditions of isostatic compression of 4×10 8 to 5×10 8 N/m 2 , and at least one thin porous filter layer formed from inorganic particles which are sintered to one another and to the inside or outside surface of the support layer, the pores of the filter layer having a diameter of less than 10 microns and being finer than the pores of the support layer, and wherein the radial thickness of each filter layer does not exceed several tens of microns.
Claim 7
Dependent Claim
139 words
A tubular filter comprising a thick porous support layer formed of sintered alumina particles of a purity at least equal to 99.9% by weight, said alumina having an open porosity of 30% to 40% by volume, the average diameter of the pores being between 2 and 20 microns and having having a resistance to crushing, measured under conditions of isostatic compression of 4×10 8 to 5×10 8 N/m 2 , and at least one thin porous filter layer formed from inorganic particles which are sintered to one another and to the inside or outside surface of the support layer, the pores of the filter layer having a diameter of less than 10 microns and being finer than the pores of the support layer, and wherein the radial thickness of each filter layer does not exceed several tens of microns.
Claim 8
Dependent Claim
25 words
A tubular filter according to claim 5, characterized in that the average pore diameter of the layer having the finest pores is about 0.2 microns.
Claim 9
Dependent Claim
44 words
A tubular filter according to claim 5 or 6, characterized in that the support layer includes at least two sublayers having pores of different diameters and connected by sintering, the sublayer having the finest pores disposed between the filter layer(s) and the other sublayers.
Claim 10
Dependent Claim
27 words
A tubular filter according to claim 5, characterized in that the ratio between its outside diameter and its radial thickness lies in the range 4 to 20.
Claim 11
Dependent Claim
36 words
A tubular filter according to claim 5, characterized in that its resistance to internal pressure ranges from 30 bars to 240 bars as the ratio of outside diameter to radial thickness ranges from 20 to 4.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-08 | 1991-08-10 | 1992-02-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-08 | 1995-08-10 | 1996-02-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-08 | 1999-08-10 | 2000-02-09 | $7700.00 | Window Closed / Lapsed |