US4722828A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High-temperature fabricable nickel-iron aluminides
Assignee: Lockheed Martin Energy Systems Inc
•
Filing: 1985-05-06
•
Granted: 1988-02-02
•
Expires: 2005-05-06
Abstract
Abstract Nickel-iron aluminides are described that are based on Ni3Al, and have significant iron content, to which additions of hafnium, boron, carbon and cerium are made resulting in Ni3Al base alloys that can be fabricated at higher temperatures than similar alloys previously developed. Further addition of molybdenum improves oxidation and cracking resistance. These alloys possess the advantages of ductility, hot fabricability, strength, and oxidation resistance.
Inventors
- 👤 Chain T. Liu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:18
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/007
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
60 words
A nickel-iron aluminide consisting essentially of: a Ni 3 Al base; a sufficient concentration of a Group IVb element or mixtures thereof to increase high temperature strength; a sufficient concentration of material selected from the group consisting of iron and a rare earth element or mixtures thereof to increase hot fabricability; and a sufficient concentration of boron to increase ductility.
Claim 2
Dependent Claim
60 words
A nickel-iron aluminide consisting essentially of: a Ni 3 Al base; a sufficient concentration of a Group IVb element or mixtures thereof to increase high temperature strength; a sufficient concentration of material selected from the group consisting of iron and a rare earth element or mixtures thereof to increase hot fabricability; and a sufficient concentration of boron to increase ductility.
Claim 3
Dependent Claim
21 words
The nickel-iron aluminide of claim 1 wherein said concentration of iron is in the range of 14.5 to 17.5 weight percent.
Claim 4
Dependent Claim
37 words
The nickel-iron aluminide of claim 2 having a sufficient amount of molybdenum to effect a reduction in oxidation of said nickeliron aluminide and a sufficient amount of carbon to reduce cracking due to the addition of molybdenum.
Claim 5
Dependent Claim
34 words
The nickel-iron aluminide of claim 2 wherein said Group IVb element is selected from the group consisting of hafnium, zirconium and mixtures thereof and present in the amount of less than 1 weight percent.
Claim 6
Dependent Claim
25 words
The nickel-iron aluminide of claim 2 wherein said rare earth element is cerium present in the amount of from no more than 0.01 weight percent.
Claim 7
Dependent Claim
19 words
The nickel-iron aluminide of claim 2 wherein boron is present in an amount from 0.01 to 0.05 weight percent.
Claim 8
Dependent Claim
34 words
The nickel-iron aluminide of claim 2 having the composition of 10.2 weight percent aluminum, 16.6 weight percent iron, 0.9 weight percent hafnium, 0.015 weight percent boron, 0.005 weight percent cerium and the balance nickel.
Claim 9
Dependent Claim
33 words
The nickel-iron aluminide of claim 3 wherein said molybdenum is present in an amount of not more than 4 weight percent and said carbon is present in not more than 0.01 weight percent.
Claim 10
Dependent Claim
41 words
The nickel-iron aluminide of claim 3 having the composition 10.0 weight percent aluminum, 15.8 weight percent iron, 0.9 weight percent hafnium, 3.7 weight percent molybdenum, 0.015 weight percent boron, 0.005 weight percent cerium, 0.06 weight percent carbon and the balance nickel.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-01 | 1991-08-03 | 1992-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-01 | 1995-08-03 | 1996-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-01 | 1999-08-03 | 2000-02-02 | $7700.00 | Window Closed / Lapsed |