US4720397A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Rapid dissolving polymer compositions and uses therefor
Assignee: General Technology Applications Inc
•
Filing: 1985-12-12
•
Granted: 1988-01-19
•
Expires: 2005-12-12
Abstract
Abstract A particulate, free-flowing and rapid dissolving polymer composition is prepared by comminuting a high molecular weight thermoplastic or viscoelastic polymer at a temperature below its glass transition temperature while maintaining the polymer in an inert environment. A finely divided, solid coating agent is mingled with the comminuted polymer while maintaining the polymer particles in a cold and inert atmosphere. The particles of coating agent form a protective shell around each polymer particle by tumble mixing the components while raising the temperature of the mixture. The polymer composition finds use as a drag reducing agent; as an anti-misting agent; to enhance the efficiency of oil skimming processes and devices; and for the preparation of polymer solutions for other uses.
Inventors
- 👤 Dion P. O'Mara
- 👤 Albert F. Hadermann
- 👤 Jerry C. Trippe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:21
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/32; C02; C02F; C02F1/00; C02F1/68; C02F1/681; C08; C08J; C08J3/00; C08J3/02; C08J3/09; C08J3/11; C08J3/12; C08J3/124; C10; C10L; C10L1/00; C10L1/10; C10L1/14; C10L1/16; C10L1/1625; C10L1/1633; C10L1/20; C10L1/206; C10L1/207; Y; Y10; Y10T; Y10T137/00; Y10T137/0318; Y10T137/0391; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2998; Y10T428/31504; Y10T428/3154; Y10T428/31544; Y10T428/31855; Y10T428/31931
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
206 words
A process for preparing a rapid dissolving polymer composition, said polymer characterized by reactivity of newly cleaved polymer surfaces which, if allowed to react with oxygen or water vapor would hinder dissolution of the polymer in a solvent, said process comprising: comminuting a soluble polymer at a temperature below its glass transition temperature to form clean-surfaced particles thereof while maintaining the polymer in an inert and non-reactive atmosphere, said atmosphere consisting essentially of nitrogen, argon and mixtures thereof; commingling a solid particulate coating agent with said polymer particles while maintaining the polymer particles at a temperature below the glass transition temperature of said polymer and in said inert and non-reactive atmosphere, said coating agent being non-reactive toward said polymer and having a median particle diameter less than one-tenth the median diameter of said polymer particles; admixing said polymer particles and said coating agent particles while raising the temperature of said mixture to and above the glass transition temperature of said polymer and while maintaining said mixture in said inert gaseous atmosphere whereby there is obtained a particulate composition having a polymer particle core surrounded by a multi-layered shell of particulate coating agent; the interstices around said core and within said shell filled with said inert gas.
Claim 2
Dependent Claim
206 words
A process for preparing a rapid dissolving polymer composition, said polymer characterized by reactivity of newly cleaved polymer surfaces which, if allowed to react with oxygen or water vapor would hinder dissolution of the polymer in a solvent, said process comprising: comminuting a soluble polymer at a temperature below its glass transition temperature to form clean-surfaced particles thereof while maintaining the polymer in an inert and non-reactive atmosphere, said atmosphere consisting essentially of nitrogen, argon and mixtures thereof; commingling a solid particulate coating agent with said polymer particles while maintaining the polymer particles at a temperature below the glass transition temperature of said polymer and in said inert and non-reactive atmosphere, said coating agent being non-reactive toward said polymer and having a median particle diameter less than one-tenth the median diameter of said polymer particles; admixing said polymer particles and said coating agent particles while raising the temperature of said mixture to and above the glass transition temperature of said polymer and while maintaining said mixture in said inert gaseous atmosphere whereby there is obtained a particulate composition having a polymer particle core surrounded by a multi-layered shell of particulate coating agent; the interstices around said core and within said shell filled with said inert gas.
Claim 3
Dependent Claim
29 words
The process of claim 1 wherein liquid nitrogen is used to chill said polymer below its glass transition temperature and wherein said inert and non-reactive atmosphere comprises nitrogen gas.
Claim 4
Dependent Claim
27 words
The process of claim 2 wherein said polymer comprises a natural or synthetic thermoplastic which imparts viscoelastic properties to a solution of said polymer in a solvent.
Claim 5
Dependent Claim
17 words
The process of claim 3 wherein the median polymer particle diameter is less than about 0.075 mm.
Claim 6
Dependent Claim
22 words
The process of claim 3 wherein the median particle diameter of said coating agent ranges from about 0.1 to about 10 micrometers.
Claim 7
Dependent Claim
38 words
The process of claim 3 wherein said polymer is selected from the group consisting of polyisobutylene, polyisoprene, polyalpha-olefins, polybutadiene, copolymers of styrene and butadiene, copolymers of ethylene and butene-1, copolymers of vinylidene fluoride and hexafluoropropylene and mixtures thereof.
Claim 8
Dependent Claim
30 words
The process of claim 3 wherein said coating agent is selected from the group consisting of amorphous silicon dioxide, kaolin clay, calcined kaolin clay, graphite, Teflon powder and tricalcium phosphate.
Claim 9
Dependent Claim
23 words
The process of claim 3 wherein said coating agent particles make up from about 20% to about 75% by weight of the composition.
Claim 10
Dependent Claim
20 words
The process of claim 3 wherein the comminution of said polymer is carried out in a liquid nitrogen-chilled impact mill.
Claim 11
Dependent Claim
22 words
The process of claim 3 wherein said polymer particles and said coating agent particles are admixed in a batch fashion by tumbling.
Claim 12
Dependent Claim
42 words
The process of claim 10 wherein said mixing is carried out in a rotating V-type blender while heat transfer from the atmosphere through the blender shell warms the polymer-coating agent mixture to a temperature above the glass transition temperature of the polymer.
Claim 13
Dependent Claim
28 words
The process of claim 3 wherein said polymer is polyisobutylene and wherein said coating agent is selected from the group consisting of tricalcium phosphate, kaolin clay and graphite.
Claim 14
Dependent Claim
12 words
The process of claim 12 wherein said coating agent is tricalcium phosphate.
Claim 15
Dependent Claim
20 words
The process of claim 3 wherein said polymer is a fluorinated elastomer and wherein said coating agent is Teflon powder.
Claim 16
Independent Claim
107 words
A method for preserving clean surfaces on freshly comminuted polymer particles said polymer characterized by reactivity of newly cleaved polymer surfaces which, if allowed to react with oxygen and water vapor would hinder dissolution of the polymer in a solvent, which comprises: preventing the reaction of water vapor and oxygen with active sites on cleaved surfaces of said clean surfaced polymer particles by maintaining said particles within an oxygen and water vapor-free inert atmosphere during and after comminution and, while maintaining said inert atmosphere around said polymer particles, encapsulating said particles within a protective particulate shell which is resistant to the passage of air and water vapor.
Claim 17
Independent Claim
107 words
A method for preserving clean surfaces on freshly comminuted polymer particles said polymer characterized by reactivity of newly cleaved polymer surfaces which, if allowed to react with oxygen and water vapor would hinder dissolution of the polymer in a solvent, which comprises: preventing the reaction of water vapor and oxygen with active sites on cleaved surfaces of said clean surfaced polymer particles by maintaining said particles within an oxygen and water vapor-free inert atmosphere during and after comminution and, while maintaining said inert atmosphere around said polymer particles, encapsulating said particles within a protective particulate shell which is resistant to the passage of air and water vapor.
Claim 18
Dependent Claim
26 words
The method of claim 15 wherein said protective shell is wet by and allows rapid passage of a liquid which is a solvent for said polymer.
Claim 19
Dependent Claim
19 words
The method of claim 16 wherein said polymer is soluble in and imparts viscoelastic properties to a liquid hydrocarbon.
Claim 20
Dependent Claim
18 words
The method of claim 17 wherein said polymer is polyisobutylene and wherein said protective shell is tricalcium phosphate.
References Cited (Backward Citations)
CA675522A
Cited
US3351601A
Cited
US3528841A
Cited
US3632369A
Cited
US4066539A
Cited
US4345013A
Cited
US4584244A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-18 | 1991-07-20 | 1992-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-18 | 1995-07-20 | 1996-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-18 | 1999-07-20 | 2000-01-19 | $7700.00 | Window Closed / Lapsed |