Abstract
Abstract The intumescent material of this invention comprises a filled polyorganosiloxane composition that is elastomeric in the cured form and up to 70 parts by weight per 100 parts by weight of said composition of hollow, thermoplastic microspheres filled with a volatile liquid. The materials are particularly useful as flame and smoke barriers in passages of partitions that are traversed by thermoplastic articles such as pipes and conduits, and can optionally contain chemical blowing agents.
Inventors
- 👤 John E. Dietlein
- 👤 Thomas C. Hampton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 08:40
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/14; C08J9/141; C08K; C08K9/00; C08K9/10; C09; C09K; C09K21/00; C09K21/14; C08J2383/00; C08J2383/04; Y; Y10; Y10S; Y10S521/00; Y10S521/907
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
77 words
An intumescent material capable of forming and maintaining a barrier to the transmission of flame and smoke, said material comprising 100 parts by weight of a curable, filled polyorganosiloxane composition which is convertible upon curing to a flame retardant elastomer; and from 1 to 70 parts by weight of expandable hollow microspheres formed from a thermoplastic organic polymer and containing therein a liquid having a boiling point of from 50° to about 200° C. under atmospheric pressure.
Claim 2
Dependent Claim
77 words
An intumescent material capable of forming and maintaining a barrier to the transmission of flame and smoke, said material comprising 100 parts by weight of a curable, filled polyorganosiloxane composition which is convertible upon curing to a flame retardant elastomer; and from 1 to 70 parts by weight of expandable hollow microspheres formed from a thermoplastic organic polymer and containing therein a liquid having a boiling point of from 50° to about 200° C. under atmospheric pressure.
Claim 3
Dependent Claim
66 words
A material according to claim 1 where said polyorganosiloxane composition comprises a polydiorganosiloxane wherein the repeating units are of the formula RR'SiO, where R and R' represent identical or different monovalent hydrocarbon or monovalent halogenated hydrocarbon radicals, a curing agent for said polydiorganosiloxane and at least one filler, and the boiling point of said organic liquid is from 50 to 200 degrees C. under atmospheric pressure.
Claim 4
Dependent Claim
79 words
A material according to claim 2 where the R and R' radicals of said polydiorganosiloxane are individually selected from the group consisting of alkyl radicals containing from 1 to 4 carbon atoms, alkenyl containing 2 or 3 carbon atoms, fluoroalkyl containing from 1 to 4 carbon atoms and phenyl, the filler comprises at least one member selected from the group consisting of silica, quartz and alkali metal silicates, and the polyorganosiloxane composition includes at least one flame retarding agent.
Claim 5
Dependent Claim
35 words
A material according to claim 3 where R is methyl and R' is either methyl or 3,3,3-trifluoropropyl and the flame retarding agent comprises platinum, a platinum compound, a metal oxide or a hydrated metal oxide.
Claim 6
Dependent Claim
39 words
A material according to claim 4 where said flame retarding agent comprises the combination of platinum or a platinum compound with at least one member selected from the group consisting of carbon black, hydrated alumina and hydrated cerric oxide.
Claim 7
Dependent Claim
46 words
A material according to claim 3 where said polydiorganosiloxane contains two vinyl radicals per molecule, said curing agent is a polyorganohydrogensiloxane containing an average of at least three silicon bonded hydrogen atoms per molecule and the composition includes a catalytically effective amount of a hydrosilation catalyst.
Claim 8
Dependent Claim
14 words
A material according to claim 6 where said hydrosilation catalyst is a platinum compound.
Claim 9
Dependent Claim
14 words
A material according to claim 3 where said curing agent is an organic peroxide.
Claim 10
Dependent Claim
37 words
A material according to claim 3 where the concentration of said microspheres constitutes from 10 to 50 parts by weight per 100 parts by weight of said composition and said polyorganosiloxane composition contains a chemical blowing agent.
Claim 11
Dependent Claim
18 words
A material composition according to claim 9 where said blowing agent is an alkali metal carbonate or bicarbonate.
Claim 12
Dependent Claim
42 words
A material according to claim 10 where blowing agent is sodium bicarbonate and said polyorganosiloxane composition is in the form of a putty or paste that remains in an uncured form until exposed to a temperature of at least 150 degrees C.
References Cited (Backward Citations)
CA715140A
Cited
CA758370A
Cited
US3317455A
Cited
US3429838A
Cited
US3553002A
Cited
US4072635A
Cited
US4000108A
Cited
US4031059A
Cited
US3923705A
Cited
US3983082A
Cited
US4273879A
Cited
US4433022A
Cited
US4433069A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-11 | 1991-07-13 | 1992-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-11 | 1995-07-13 | 1996-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-11 | 1999-07-13 | 2000-01-12 | $7700.00 | Window Closed / Lapsed |