Organosiloxane foams
Assignee: Dow Corning France SAS
•
Filing: 1986-11-10
•
Granted: 1988-01-12
•
Expires: 2006-11-10
Abstract
Abstract The specification is directed to polysiloxane foams. There are disclosed compositions capable of curing at room temperature which comprise a hydroxypolysiloxane, an alkylhydrogen polysiloxane, a tin compound as catalyst and finely divided filler. According to the invention storage stability of these foam forming polysiloxane compositions is improved by use as filler of silica which has been pretreated to render is hydrophobic. The subject compositions may comprise two components which do not require individual mixing prior to mixing together of the components. The compositions may be packaged in any convenient manner. The compositions may be used for a variety of purposes, for example to provide medical dressings.
Inventors
- 👤 David Pocknell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:19
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/14; C08J2383/00; C08J2383/04; Y; Y10; Y10S; Y10S528/00; Y10S528/901
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
247 words
A foamable composition comprising an organosilicon polymer including siloxane units providing a silicon-bonded hydroxyl group, an organosilicon polymer including siloxane units having a silicon-bonded hydrogen atom, a catalyst and finely divided filler material, the organosilicon polymers being such that they are capable of chemical reaction at room temperature in presence of the catalyst whereby hydrogen is evolved to cause the composition to foam and the composition becomes cured thus to provide a resilient foam characterised in that the foamable composition consists essentially of (a) 100 parts by weight α,ω-di-hydroxy polysiloxane having a viscosity in the range 0.5 to 25 Pa.s at 25° C., (b) 5 to 35 parts by weight trialkyl-siloxy endblocked alkylhydrogen polysiloxane, (c) 0 to 60 parts by weight of a low molecular weight di-hydroxy polysiloxane containing no more than 25 R 2 SiO units wherein R represents a lower alkyl group of 1 to 6 carbon atoms or a phenyl group, (d) 0 to 7 parts by weight of a cross-linking agent capable of combining with three or more hydroxy polysiloxane molecules, (e) 0 to 20 parts by weight of a monohydroxy silanol or siloxanol, (f) 5 to 35 parts by weight of finely divided filler which includes a major amount of silica which has been treated to render it hydrophobic, (g) 3 to 8 percent by weight of the ingredients (a) to (f) of a tin salt of a carboxylic acid as catalyst, optionally in admixture with material intended to provide propellant gas.
Claim 2
Dependent Claim
247 words
A foamable composition comprising an organosilicon polymer including siloxane units providing a silicon-bonded hydroxyl group, an organosilicon polymer including siloxane units having a silicon-bonded hydrogen atom, a catalyst and finely divided filler material, the organosilicon polymers being such that they are capable of chemical reaction at room temperature in presence of the catalyst whereby hydrogen is evolved to cause the composition to foam and the composition becomes cured thus to provide a resilient foam characterised in that the foamable composition consists essentially of (a) 100 parts by weight α,ω-di-hydroxy polysiloxane having a viscosity in the range 0.5 to 25 Pa.s at 25° C., (b) 5 to 35 parts by weight trialkyl-siloxy endblocked alkylhydrogen polysiloxane, (c) 0 to 60 parts by weight of a low molecular weight di-hydroxy polysiloxane containing no more than 25 R 2 SiO units wherein R represents a lower alkyl group of 1 to 6 carbon atoms or a phenyl group, (d) 0 to 7 parts by weight of a cross-linking agent capable of combining with three or more hydroxy polysiloxane molecules, (e) 0 to 20 parts by weight of a monohydroxy silanol or siloxanol, (f) 5 to 35 parts by weight of finely divided filler which includes a major amount of silica which has been treated to render it hydrophobic, (g) 3 to 8 percent by weight of the ingredients (a) to (f) of a tin salt of a carboxylic acid as catalyst, optionally in admixture with material intended to provide propellant gas.
Claim 3
Dependent Claim
171 words
A foamable composition according to claim 1 further characterized in that said (a), (c) and (e) are composed of one or more siloxane units according to the general formula ##STR6## in which each R represents a lower alkyl group of 1 to 6 carbon atoms or a phenyl group and n has the value of 1, 2 or 3; said (c) contains no more than 25 R 2 SiO units; said (b) is composed of a mixture of trialkyl-siloxy end-blocked alkylhydrogen polysiloxanes having a viscosity of from 0.0001 to 0.1 Pa.s at 25° C. and are composed of endblocking siloxane units according to the general formula R 3 SiO 1/2 and a combination of R 2 SiO and RHSiO units where the majority of the latter two siloxane units are RHSiO units; and said (d) is a crosslinking agent selected from the group consisting of an alkoxysilanes, an organosilane or a condensation products of alkoxysilane, and mixtures of both wherein each such crosslinking agent contains at least three silicon-bonded alkoxy radicals.
Claim 4
Dependent Claim
47 words
A foamable composition according to claim 2 wherein there is present from 5 to 20 parts of (b), from 10 to 30 parts of (c), from 3 to 5 parts of (d), from 5 to 15 parts of (e) and from 5 to 15 parts of (f).
Claim 5
Dependent Claim
38 words
A foamable composition according to claim 1 further characterised in that the filler consists of a product of the treatment of silica with hexamethyl disilazane and has a surface area between about 100 and 250 m 2 /g.
Claim 6
Dependent Claim
171 words
A foamable composition according to claim 4 further characterized in that said (a), (c) and (e) are composed of one or more siloxane units according to the general formula ##STR7## in which each R represents a lower alkyl group of 1 to 6 carbon atoms or a phenyl group and n has the value of 1, 2 or 3; said (c) contains no more than 25 R 2 SiO units; said (b) is composed of a mixture of trialkyl-siloxy end-blocked alkylhydrogen polysiloxanes having a viscosity of from 0.0001 to 0.1 Pa.s at 25° C. and are composed of endblocking siloxane units according to the general formula R 3 SiO 1/2 and a combination of R 2 SiO and RHSiO units where the majority of the latter two siloxane units are RHSiO units; and said (d) is a crosslinking agent selected from the group consisting of alkoxysilanes, an organosilane or a condensation products of an alkoxysilane, and mixtures of both wherein each such crosslinking agent contains at least three silicon-bonded alkoxy radicals.
Claim 7
Dependent Claim
47 words
A foamable composition according to claim 5 wherein there is present from 5 to 20 parts of (b), from 10 to 30 parts of (c), from 3 to 5 parts of (d), from 5 to 15 parts of (e) and from 5 to 15 parts of (f).
References Cited (Backward Citations)
US2875163A
Cited
FR1185508A
Cited
GB867619A
Cited
US3428580A
Cited
US3516951A
Cited
US4157426A
Cited
US4189545A
Cited
GB2065661A
Cited
US4529741A
Cited
US4547529A
Cited
US4550125A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-11 | 1991-07-13 | 1992-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-11 | 1995-07-13 | 1996-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-11 | 1999-07-13 | 2000-01-12 | $7700.00 | Window Closed / Lapsed |