Electrically conductive polyethylene foam
Assignee: KAY-FRIES Inc
•
Filing: 1986-04-30
•
Granted: 1988-01-12
•
Expires: 2006-04-30
Abstract
Abstract An electrically conductive polyethylene foam which is in the form of a profile, e.g. a sheet, having a closed cell foam structure and exhibiting a surface resistivity of not more than 10 5 ohms/square. The sheet is prepared by a continuous method wherein an extruded, foamable, non-crosslinked preform containing a mixture of polyethylene, ethylene copolymer, chemical blowing agent, crosslinking agent and conductive carbon black is heated to produce the foam.
Inventors
- 👤 Nicholas J. Leonardi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 04:04
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; C08J9/10; B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/505; B29C70/00; B29C70/88; B29C70/882; C08K; C08K3/00; C08K3/02; C08K3/04; H; H01; H01B; H01B1/00; H01B1/20; H01B1/24; B29K; B29K2105/00; B29K2105/04; B29K2105/24; B29K2995/00; B29K2995/0003; B29K2995/0005; C08J2323/00; C08J2323/02; Y; Y10; Y10S; Y10S264/00; Y10S264/18
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
174 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet having a closed cell foam structure and exibiting a surface resistivity of not more than 10 5 ohms/square, which comprises extruding a resinous composition containing per 100 parts by weight of a mixture containing about 100-0% by weight of polyethylene and about 100-0% by weight of an ethylene copolymer, 12 to 20 parts by weight of conductive carbon black, 2 to 15 parts by weight of a chemical blowing agent and 0.1 to 1.5 parts by weight of a crosslinking agent, said polyethylene having a melt index of about 10-40 and the ethylene copolymer having a melt index of about 10-40, to produce a non-crosslinked, non-foamed sheet preform at a temperature above the melt temperature of the resinous composition and below the decomposition temperatures of the crosslinking agent and the blowing agent, and then heating the sheet preform to higher temperatures than the extrusion temperature to activate the crosslinking agent and the blowing agent to thereby effect crosslinking and foaming of the composition.
Claim 2
Independent Claim
174 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet having a closed cell foam structure and exibiting a surface resistivity of not more than 10 5 ohms/square, which comprises extruding a resinous composition containing per 100 parts by weight of a mixture containing about 100-0% by weight of polyethylene and about 100-0% by weight of an ethylene copolymer, 12 to 20 parts by weight of conductive carbon black, 2 to 15 parts by weight of a chemical blowing agent and 0.1 to 1.5 parts by weight of a crosslinking agent, said polyethylene having a melt index of about 10-40 and the ethylene copolymer having a melt index of about 10-40, to produce a non-crosslinked, non-foamed sheet preform at a temperature above the melt temperature of the resinous composition and below the decomposition temperatures of the crosslinking agent and the blowing agent, and then heating the sheet preform to higher temperatures than the extrusion temperature to activate the crosslinking agent and the blowing agent to thereby effect crosslinking and foaming of the composition.
Claim 3
Dependent Claim
78 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet according to claim 1, wherein said resinous compostion consists essentially of, per 100 parts by weight of a mixture consisting essentially of about 20-80% by weight of polyethylene and about 80-20% by weight of the ethylene copolymer, 12 to 20 parts by weight of conductive carbon black, 0.1 to 1.5 by weight of the crosslinking agent and 2 to 15 parts by weight the chemical blowing agent.
Claim 4
Dependent Claim
62 words
A method for producing an electrically conductive crosslinked polyethylene foam strut according to claim 2, wherein the ethylene copolymer is a copolymer prepared from a monomeric mixture containing at least 60% by weight of ethylene and at least 5% by weight of an ethylenically unsaturated monomer copolymerizable with ethylene and capable of providing a copolymer that increases the flexibility of the polyethylene.
Claim 5
Dependent Claim
42 words
A method for producing an electrically conductive crosslinked polyethylene foam, sheet according to claim 2, wherein the ethylene copolymer is a copolymer prepared from a monomeric mixture containing at least 60% by weight of ethylene and 5-40% by weight of vinyl acetate.
Claim 6
Dependent Claim
40 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet according to claim 2, wherein the polyethylene has a melt index of from 15 to 30 and the ethylene copolymer has a melt index of from 20 to 25.
Claim 7
Dependent Claim
49 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet according to claim 1, wherein the resinous composition is extruded at a temperature of from 125° C. to 160° C. and the sheet preform is heated in a step-wise manner wherein each successive step has a higher temperature.
Claim 8
Dependent Claim
53 words
A method for producing an electrically conductive polyethylene foam sheet according to claim 6, wherein the sheet preform is heated in a multi-zone oven divided into three zones, the first zone having a temperature of from 175° to 200° C., and the third zone having a temperature of from 220° to 240° C.
Claim 9
Dependent Claim
58 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet according to claim 1, wherein the resinous composition is extruded from an extruder unit to form the sheet preform and said sheet preform, upon being heated to higher temperatures than the extrusion temperature, forms a sheet having a thickness of from 1/4 to 5/8 of an inch.
Claim 10
Dependent Claim
62 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet according to claim 1 further comprising preparing said resinous composition by premixing the conductive carbon black, the crosslinking agent and the blowing agent with a portion of the polyethylene and/or the ethylene copolymer to form pellets and thereafter admixing the pellets with additional polyethylene and/or ethylene copolymer within the extruder unit.
Claim 11
Dependent Claim
52 words
A method for producing an electrically conductive crosslinked polyethylene foam sheet according to claim 1 wherein the resinous composition is extruded from an extruder unit, the head pressure of the extruded unit being maintained from 1300 to 2000 psi at a flow rate of the resinous composition of 500 pounds per hour.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-11 | 1991-07-13 | 1992-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-11 | 1995-07-13 | 1996-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-11 | 1999-07-13 | 2000-01-12 | $7700.00 | Window Closed / Lapsed |