Corrosion resistant, coated metal laminate, its preparation and coating materials
Assignee: Nippon Paint Co Ltd
•
Filing: 1986-05-28
•
Granted: 1988-01-12
•
Expires: 2006-05-28
Abstract
Abstract Corrosive resistant, coated laminate consisting of metal substrate, anti-corrosive layer and paint layer, which is characterized by the fact that the anti-corrosive layer is formed by a composition containing, as essential components, at least one hexa-valent chromium containing chromium compound having a solubility of 20 to 10-5 and aqueous silica and/or aqueous resin as binder, and as optional component, a water soluble chromium compound having a solubility of more than 20, and the paint layer is free from chromium compound. The laminate is excellent, inter alia, in adhesion of coating and anti-corrosive property. The invention also provides a coated metal plate having excellent corrosion resistance and continuous spot weldability.
Inventors
- 👤 Tamotsu Sobata
- 👤 Masaaki Takimoto
- 👤 Yuichi Yoshida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:35
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/05; C23C22/06; C23C22/24; B; B23; B23K; B23K35/00; B23K35/22; B23K35/226; C09; C09D; C09D5/00; C09D5/08; C09D5/082; C09D5/084; C09D5/10; C23C22/73; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24934; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/27; Y10T428/273; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
154 words
A coating composition suitable for precoating a metal comprising, as solid, (A) 10 to 35% by weight of at least one binder resin whose aromatic ring content in its molecule is less than 50% by weight and which is selected from the group consisting of epoxy resin, alkyd resin, acryl resin, melamine resin, urethane resin, phenol resin, vinyl resin, polyvinyl butyral resin, polyvinyl acetate resin, chlorinated rubber, oil-free polyester resin, phthalic acid resin, styrene resin and polyolefin resin, (B) 4 to 50% by weight of polyethylene wax capable of being decomposed exothermically at 300° to 500° C., and (C) 15 to 86% by weight of electrically conductive pigment having a mean diameter of less than 20 microns, which is selected from the group consisting of stainless steel, gold, silver, cadmium, aluminum, zinc, tin, copper and graphite powders; iron, nickel, titanium, tungsten, niobium and manganese carbides; and ferromanganese, ferromolybdenum, ferrosilicon, ferrochromium, ferrotitanium and ferrosphosphorous ferroalloys.
Claim 2
Dependent Claim
154 words
A coating composition suitable for precoating a metal comprising, as solid, (A) 10 to 35% by weight of at least one binder resin whose aromatic ring content in its molecule is less than 50% by weight and which is selected from the group consisting of epoxy resin, alkyd resin, acryl resin, melamine resin, urethane resin, phenol resin, vinyl resin, polyvinyl butyral resin, polyvinyl acetate resin, chlorinated rubber, oil-free polyester resin, phthalic acid resin, styrene resin and polyolefin resin, (B) 4 to 50% by weight of polyethylene wax capable of being decomposed exothermically at 300° to 500° C., and (C) 15 to 86% by weight of electrically conductive pigment having a mean diameter of less than 20 microns, which is selected from the group consisting of stainless steel, gold, silver, cadmium, aluminum, zinc, tin, copper and graphite powders; iron, nickel, titanium, tungsten, niobium and manganese carbides; and ferromanganese, ferromolybdenum, ferrosilicon, ferrochromium, ferrotitanium and ferrosphosphorous ferroalloys.
Claim 3
Dependent Claim
39 words
The composition according to claim 1 wherein the polyethylene wax is in the form of powder having a mean diameter of less than 50 microns, the molecular weight of the polyethylene being in the range of 1,000 to 10,000.
Claim 4
Dependent Claim
27 words
The composition according to claim 2 wherein the polyethylene has a specific gravity of at least 0.94 and an acidity of not more than 15 KOH mg/g.
Claim 5
Dependent Claim
268 words
A coating composition suitable for precoating a metal comprising, as solid, (A) 10 to 35% by weight of at least one binder resin whose aromatic ring content in its molecule is less than 50% by weight and which is selected from the group consisting of epoxy resin, alkyd resin, acryl resin, melamine resin, urethane resin, phenol resin, vinyl resin, polyvinyl butyral resin, polyvinyl acetate resin, chlorinated rubber, oil-free polyester resin, phthalic acid resin, styrene resin and polyolefin resin, (B) 4 to 30% by weight of polyethylene wax capable of being decomposed exothermically at 300° to 500° C., (C) 15 to 85% by weight of electrically conductive pigment which is essentially of di-iron phosphide and has a mean diameter of less than 20 microns, (D) 1 to 71% by weight of iron phosphide decomposition inhibitor whose aqueous suspension has a pH of 6 to 13 and which is selected from the group consisting of alkaline earth metal petroleum sulfonates, zinc chromate, zinc potassium chromate, lead chromate, basic lead chromate, calcium chromate, strontium chromate, zinc phosphate, iron phosphate, aluminum tripolyphosphate, lead silicate, talc, calcium carbonate, silica and zinc powder wherein the amount of zinc powder is less than the iron phosphide amount, and (E) 0 to 70% by weight of other inorganic pigment selected from the group consisting of zinc chromate, lead chromate, calcium chromate, strontium chromate, zinc phosphate, iron phosphate, aluminium tripolyphosphate, lead silicate, silica, calcium carbonate, talc, alumina, chromium oxide, iron oxide and lead oxide, provided that the total amount of (C), (D) and (E) is 35 to 86% by weight of the total solids of the composition.
Claim 6
Dependent Claim
268 words
A coating composition suitable for precoating a metal comprising, as solid, (A) 10 to 35% by weight of at least one binder resin whose aromatic ring content in its molecule is less than 50% by weight and which is selected from the group consisting of epoxy resin, alkyd resin, acryl resin, melamine resin, urethane resin, phenol resin, vinyl resin, polyvinyl butyral resin, polyvinyl acetate resin, chlorinated rubber, oil-free polyester resin, phthalic acid resin, styrene resin and polyolefin resin, (B) 4 to 30% by weight of polyethylene wax capable of being decomposed exothermically at 300° to 500° C., (C) 15 to 85% by weight of electrically conductive pigment which is essentially of di-iron phosphide and has a mean diameter of less than 20 microns, (D) 1 to 71% by weight of iron phosphide decomposition inhibitor whose aqueous suspension has a pH of 6 to 13 and which is selected from the group consisting of alkaline earth metal petroleum sulfonates, zinc chromate, zinc potassium chromate, lead chromate, basic lead chromate, calcium chromate, strontium chromate, zinc phosphate, iron phosphate, aluminum tripolyphosphate, lead silicate, talc, calcium carbonate, silica and zinc powder wherein the amount of zinc powder is less than the iron phosphide amount, and (E) 0 to 70% by weight of other inorganic pigment selected from the group consisting of zinc chromate, lead chromate, calcium chromate, strontium chromate, zinc phosphate, iron phosphate, aluminium tripolyphosphate, lead silicate, silica, calcium carbonate, talc, alumina, chromium oxide, iron oxide and lead oxide, provided that the total amount of (C), (D) and (E) is 35 to 86% by weight of the total solids of the composition.
Claim 7
Dependent Claim
39 words
The composition according to claim 4 wherein the polyethylene wax is in the form of powder having a mean diameter of less than 50 microns, the molecular weight of the polyethylene being in the range of 1,000 to 10,000.
Claim 8
Dependent Claim
29 words
The composition according to claim 4 wherein the total of amount of (C), (D) and (E) is 35 to 70% by weight of the total solids of the composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-11 | 1991-07-13 | 1992-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-11 | 1995-07-13 | 1996-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-11 | 1999-07-13 | 2000-01-12 | $7700.00 | Window Closed / Lapsed |