Method for making an electrically heatable windshield

Claim 1

A method of manufacturing a curved windshield with an electrically conductive film thereon which comprises the steps of: placing an electrically conductive film on a flat glass sheet; placing an oxidizable metal layer on said electrically conductive film, said oxidizable metal layer being of such thickness that when the flat glass sheet is subjected to a heating operation of a specific predetermined time and temperature for the purpose of bending the same, said oxidizable metal layer will be oxidized throughout its width as the heating of the glass sheet is being terminated; placing an oxidized metal layer on said oxidizable metal layer; cutting a glass templet from the resulting coated glass sheet; applying electrically conductive bus bars to said electrically conductive film on said glass templet; drying said bus bars to bond said bus bars to said electrically conductive film on said glass templet; cutting a glass templet from an uncoated glass sheet; uniting said coated and uncoated glass templet in a manner such that said coating on said coated glass templet is exposed to the ambient; heating said glass templet to a temperature whereat said united glass templets are bendable using said specific time and temperature; reverse bending said united glass templets, said oxidation of said oxidizable metal layer during said heating of said united glass templets protecting said electrically conductive film; placing a laminating interlayer between said glass templets with the coating on the coated glass templet being placed in contact with the laminating interlayer; and laminating said glass templets with said laminating interlayer thereby to achieve a shaped laminated windshield which is heatable by the flow of electrical energy therethrough.

Claim 2

A method of manufacturing a curved windshield with an electrically conductive film thereon which comprises the steps of: placing an electrically conductive film on a flat glass sheet; placing an oxidizable metal layer on said electrically conductive film, said oxidizable metal layer being of such thickness that when the flat glass sheet is subjected to a heating operation of a specific predetermined time and temperature for the purpose of bending the same, said oxidizable metal layer will be oxidized throughout its width as the heating of the glass sheet is being terminated; placing an oxidized metal layer on said oxidizable metal layer; cutting a glass templet from the resulting coated glass sheet; applying electrically conductive bus bars to said electrically conductive film on said glass templet; drying said bus bars to bond said bus bars to said electrically conductive film on said glass templet; cutting a glass templet from an uncoated glass sheet; uniting said coated and uncoated glass templet in a manner such that said coating on said coated glass templet is exposed to the ambient; heating said glass templet to a temperature whereat said united glass templets are bendable using said specific time and temperature; reverse bending said united glass templets, said oxidation of said oxidizable metal layer during said heating of said united glass templets protecting said electrically conductive film; placing a laminating interlayer between said glass templets with the coating on the coated glass templet being placed in contact with the laminating interlayer; and laminating said glass templets with said laminating interlayer thereby to achieve a shaped laminated windshield which is heatable by the flow of electrical energy therethrough.