Method of implanting spatially controlled P-N junctions by focused ion beams containing at least two species
Assignee: Hitachi Ltd
•
Filing: 1986-04-15
•
Granted: 1987-12-29
•
Expires: 2006-04-15
Abstract
Abstract A desired part of a workpiece is irradiated with a focused ion beam which contains at least two species of impurity ions to-be-implanted exhibiting different spacial distributions of ion current densities. Thus, regions respectively implanted with different species of impurity ions can be formed in a predetermined positional relationship at high precision.
Inventors
- 👤 Shoji Shukuri
- 👤 Masao Tamura
- 👤 Yasuo Wada
- 👤 Yoshihisa Fujisaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:02
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10D; H10D84/00; H10D84/01; H10D84/02; H10D84/05; H10P30/202; H10P30/206; H10P30/21
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
75 words
A method of manufacturing a semiconductor device comprising the step of irradiating a desired part of a workpiece with a focused ion beam which contains at least two species of impurity ions to be simultaneously implanted, thereby to simultaneously implant said at least two species of impurity ions into said desired part, the at least two species having spatial distributions of ion current density within the focused ion beam that are different from each other.
Claim 2
Independent Claim
75 words
A method of manufacturing a semiconductor device comprising the step of irradiating a desired part of a workpiece with a focused ion beam which contains at least two species of impurity ions to be simultaneously implanted, thereby to simultaneously implant said at least two species of impurity ions into said desired part, the at least two species having spatial distributions of ion current density within the focused ion beam that are different from each other.
Claim 3
Dependent Claim
47 words
A method of manufacturing a semiconductor device as defined in claim 1, wherein said at least two species of impurity ions afford conductivity types opposite to each other within a semiconductor material, whereby at least one p-n junction is formed at said desired part of the workpiece.
Claim 4
Dependent Claim
36 words
A method of manufacturing a semiconductor device as defined in claim 1, wherein a liquid metal ion source for said focused ion beam is an alloy which contains the at least two species of impurities to-be-ion-implanted.
Claim 5
Dependent Claim
55 words
A method of manufacturing a semiconductor device as defined in claim 1, wherein a region into which a first species of impurity ions in said at least two species of impurity ions are implanted has a predetermined positional relation to a region into which a second specifies of impurity ions in the same are implanted.
Claim 6
Dependent Claim
39 words
A method of manufacturing a semiconductor device as defined in claim 1, wherein the step of irradiating includes a sub-step of forming a single mass spectrum containing said at least two species of impurity ions to be simultaneously implanted.
Claim 7
Dependent Claim
32 words
A method of manufacturing a semiconductor device as defined in claim 1, wherein the step of irradiating includes vector-scanning and projecting the focused ion beam on said desired part of the workpiece.
Claim 8
Dependent Claim
52 words
A method of manufacturing a semiconductor device as defined in claim 1, wherein the at least two species of impurity ions are simultaneously implanted into said desired part so as to provide impurity doped regions in which the lateral concentration distributions of the at least two species of impurity ions are different.
Claim 9
Dependent Claim
32 words
A method of manufacturing a semiconductor device as defined in claim 1, wherein the step of irradiating includes raster-scanning and projecting the focused ion beam on said desired part of the workpiece.
Claim 10
Dependent Claim
59 words
A method of manufacturing a semiconductor device as defined in claim 5, wherein said sub-step of forming a single mass spectrum includes forming an initial ion beam including said at least two species of impurity ions, said initial ion beam comprised of a plurality of proximate spectra, and turning said plurality of proximate spectra into said single mass spectrum.
Claim 11
Dependent Claim
47 words
A method of manufacturing a semiconductor device as defined in claim 8, wherein said at least two species of impurity ions afford conductivity types opposite to each other within a semiconductor material, whereby, due to said raster-scanning and projecting, periodic p-n junctions are formed in the workpiece.
Claim 12
Dependent Claim
69 words
A method of manufacturing a semiconductor device as defined in claim 9, wherein an ion beam containing at least said at least two species of impurity ions is passed through a mass separator prior to contacting said desired part of a workpiece, and wherein said turning said plurality of proximate spectra into said single mass spectrum includes accelerating the ions, in their direction of travel, in the mass separator.
Claim 13
Independent Claim
141 words
A method of manufacturing an optical guide layer of a semiconductor laser, comprising the steps of growing a layer of semiconductor material for said optical guide layer on an active layer of said semiconductor laser; and irradiating said layer of semiconductor material with a focused ion beam containing at least two species of impurity ions to be simultaneously implanted, so as to simultaneously implant the at least two species in the layer of semiconductor material, the at least two species having spatial distributions of ion current density within the focused ion beam that is different from each other, the at least two species of impurity ions affording conductivity types opposite to each other within said layer of semiconductor material, and the irradiating including raster-scanning the focused ion beam so as to provide periodic p-n junctions in said layer of semiconductor material.
Claim 14
Independent Claim
141 words
A method of manufacturing an optical guide layer of a semiconductor laser, comprising the steps of growing a layer of semiconductor material for said optical guide layer on an active layer of said semiconductor laser; and irradiating said layer of semiconductor material with a focused ion beam containing at least two species of impurity ions to be simultaneously implanted, so as to simultaneously implant the at least two species in the layer of semiconductor material, the at least two species having spatial distributions of ion current density within the focused ion beam that is different from each other, the at least two species of impurity ions affording conductivity types opposite to each other within said layer of semiconductor material, and the irradiating including raster-scanning the focused ion beam so as to provide periodic p-n junctions in said layer of semiconductor material.
Claim 15
Dependent Claim
34 words
A method of manufacturing an optical guide layer of a semiconductor laser as defined in claim 12, wherein said active layer is of undoped InGaAs, and said layer of semiconductor material is N-type InGaAs.
Claim 16
Dependent Claim
61 words
A method of manufacturing an optical guide layer of a semiconductor laser as defined in claim 12, comprising the further steps of forming a clad layer on the irradiated layer of semiconductor material, so as to provide a laminate structure, and forming a pair of electrodes respectively on opposed exposed surfaces of said laminate structure, whereby a semiconductor laser is formed.
Claim 17
Dependent Claim
36 words
A method of manufacturing an optical guide layer of a semiconductor laser as defined in claim 13, wherein said step of growing said layer of semiconductor material includes epitaxially growing said layer on said active layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-28 | 1991-06-29 | 1991-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-28 | 1995-06-29 | 1995-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-28 | 1999-06-29 | 1999-12-29 | $7700.00 | Window Closed / Lapsed |