Process for producing a plastic laminate of low density polymeric material and high density polymeric material and laminate made thereof
Assignee: Individual
•
Filing: 1985-12-16
•
Granted: 1987-12-29
•
Expires: 2005-12-16
Abstract
Abstract A process and apparatus are disclosed for producing a plastics laminate material comprising a lamina of low density foamed polymeric material such as a non-cross linked polyethylene foam and a lamina of high density non-foamed polymeric material such as high density polyethylene, wherein the low density lamina is of at least 50 times greater thickness than the high density lamina, characterised in that the individual laminae are physically bonded between nip rollers at critical conditions of elevated pressure (e.g. 40 to 50 p.s.i.) and temperature (e.g. 125° C. to 150° C.) to bring about a very strong bond such that the bonded laminae do not readily peel apart. Temperature is particularly critical and should be brought close to and not substantially above the tackifying temperature of the low density foamed material. Air is preferably entrapped between the laminae during the process. The high density lamina is preferably pre-heated to increase its malleability prior to bonding with the low density lamina. The finished laminate may be used as a protective packaging material in sheet or bag form.
Inventors
- 👤 Paul Burke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:14
CPC Classifications
B; B32; B32B; B32B37/00; B32B37/14; B32B37/16; B32B37/20; B32B37/203; B32B27/00; B32B27/06; B32B27/08; B32B27/065; B32B5/00; B32B5/18; B32B7/00; B32B7/04; B32B7/12; B32B2305/00; B32B2305/02; B32B2305/022; B32B2307/00; B32B2307/70; B32B2307/72; B32B2307/722; B32B2309/00; B32B2309/02; B32B2309/12; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1016; Y10T156/1025; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/2457; Y10T428/24628; Y10T428/24661; Y10T428/24669; Y10T428/24694; Y10T428/24942; Y10T428/2495; Y10T428/249921; Y10T428/249953; Y10T428/249976; Y10T428/249977; Y10T428/249987; Y10T428/249991; Y10T428/249992; Y10T428/249993
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
128 words
A process for producing a plastics laminate material comprising a lamina of foamed low density polymeric material and a lamina of non-foamed high density polymeric material wherein the low density lamina is of at least 50 times greater thickness than the high density lamina, wherein the process comprises the steps of advancing the high density lamina over the low density lamina and bringing the laminae together between a pair of nip rollers under pressure, applying heat at a temperature within the range of 125° C. to 150° C. to the roller which contacts the high density lamina to bring about a strong peelable bond between the laminae, advancing the bonded laminate away from the nip rollers and allowing sufficient time for the laminate to cool to ambient temperature.
Claim 2
Dependent Claim
128 words
A process for producing a plastics laminate material comprising a lamina of foamed low density polymeric material and a lamina of non-foamed high density polymeric material wherein the low density lamina is of at least 50 times greater thickness than the high density lamina, wherein the process comprises the steps of advancing the high density lamina over the low density lamina and bringing the laminae together between a pair of nip rollers under pressure, applying heat at a temperature within the range of 125° C. to 150° C. to the roller which contacts the high density lamina to bring about a strong peelable bond between the laminae, advancing the bonded laminate away from the nip rollers and allowing sufficient time for the laminate to cool to ambient temperature.
Claim 3
Dependent Claim
29 words
A process as claimed in claim 1 including the step of indirectly pre-heating the high density lamina to increase its malleability with heating means upstream of the nip rollers.
Claim 4
Dependent Claim
49 words
A plastics laminate material comprising a lamina of foamed closed cell non cross-linked low density polyethylene peelably bonded by heat and pressure to a lamina of high density polyethylene wherein the low density polyethylene lamina is of at least 50 times greater thickness than the high density polyethylene lamina.
Claim 5
Dependent Claim
49 words
A plastics laminate material comprising a lamina of foamed closed cell non cross-linked low density polyethylene peelably bonded by heat and pressure to a lamina of high density polyethylene wherein the low density polyethylene lamina is of at least 50 times greater thickness than the high density polyethylene lamina.
Claim 6
Dependent Claim
25 words
A plastics laminate material as claimed in claim 3 wherein air is entrapped between the low density polyethylene lamina and the high density polyethylene lamina.
Claim 7
Dependent Claim
100 words
A process for producing a plastic laminate material comprising the steps of advancing a first lamina of foamed low density polymeric material having a predetermined tackifying temperature and a second lamina of non-foamed high density polymeric material in overlying relation to each other; heating the first and second laminae to a temperature sufficient to effect a physical adhesion between the laminae without substantially exceeding the tackifying temperature of the first lamina; pressing the heated laminae together to effect bonding of the laminae together; and thereafter cooling the bonded laminae for a time sufficient to set the bond between the laminae.
Claim 8
Dependent Claim
100 words
A process for producing a plastic laminate material comprising the steps of advancing a first lamina of foamed low density polymeric material having a predetermined tackifying temperature and a second lamina of non-foamed high density polymeric material in overlying relation to each other; heating the first and second laminae to a temperature sufficient to effect a physical adhesion between the laminae without substantially exceeding the tackifying temperature of the first lamina; pressing the heated laminae together to effect bonding of the laminae together; and thereafter cooling the bonded laminae for a time sufficient to set the bond between the laminae.
Claim 9
Dependent Claim
36 words
A process as set forth in claim 5 wherein a strong physical bond is produced between the laminae characterized in that the individual lamina can only be peeled cleanly apart upon application of a substantial force.
Claim 10
Dependent Claim
21 words
A process as set forth in claim 5 wherein the first lamina is heated to a temperature of about 150° C.
Claim 11
Dependent Claim
23 words
A process as set forth in claim 7 wherein the laminae are pressed together at a pressure of from 40 to 80 psi.
Claim 12
Dependent Claim
39 words
A process as set forth in claim 5 wherein the first laminae is heated to a temperature of from 125° C. to 150° C. and the laminae are pressed together at a pressure of from 40 to 80 psi.
Claim 13
Dependent Claim
36 words
A process as set forth in claim 5 wherein the first lamina has a melting point of about 170° to 180° C. and the second lamina has a melting point of about 200° to 210° C.
Claim 14
Dependent Claim
30 words
A process as set forth in claim 5 which further comprises the step of corrugating the second lamina prior to being pressed against the first lamina to trap air therebetween.
Claim 15
Dependent Claim
47 words
A plastic laminate comprising a first lamina of foamed low density polymeric material; a second corrugated lamina of non-foamed high density polymeric material bonded directly to said first lamina; said first lamina having a thickness at least fifty times greater than the thickness of said second laminae.
Claim 16
Dependent Claim
47 words
A plastic laminate comprising a first lamina of foamed low density polymeric material; a second corrugated lamina of non-foamed high density polymeric material bonded directly to said first lamina; said first lamina having a thickness at least fifty times greater than the thickness of said second laminae.
Claim 17
Dependent Claim
31 words
A plastic laminate as set forth in claim 12 wherein the bond between said laminae is characterized in that the individual lamina are physically adhered to each other without molecular fusion.
Claim 18
Dependent Claim
16 words
A plastic laminate as set forth in claim 12 wherein each lamina is made of polyethylene.
Claim 19
Dependent Claim
39 words
A plastic laminate as set forth in claim 12 wherein said first lamina has a melting point of from 170° C. to 180° C. and said second laminate has a melting point of from 200° C. to 210° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-28 | 1991-06-29 | 1991-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-28 | 1995-06-29 | 1995-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-28 | 1999-06-29 | 1999-12-29 | $7700.00 | Window Closed / Lapsed |