Deposition of films of cubic boron nitride and nitrides of other group III elements
Assignee: Individual
•
Filing: 1985-08-12
•
Granted: 1987-12-22
•
Expires: 2005-08-12
Abstract
Abstract Process for producing cubic boron nitride films on a substrate by activated dissociation reduction-reaction. Boric acid in the condensed state is evaporated in a vacuum chamber from a resistance-heated evaporation source and ammonia gas is introduced into the chamber. The vapor of the boric acid and the molecules of the ammonia gas are ionized by a beam of low-energy electrons in the reaction zone between the resistance-heated evaporation source and the substrate. The ammonia gas reacts with the boric acid in a two-step process in which (1) the boric acid is reduced by the atomic hydrogen formed by the dissociation of ammonia, and (2) the resulting boron atoms react with the nitrogen atoms released by the dissociation of ammonia to form boron nitride which deposits as a film onthe substrate. This film has the cubic boron nitride structure and is ready for use without requiring post-deposition heat treatment.
Inventors
- 👤 Kasturi L. Chopra
- 👤 Roitan F. Bunshah
- 👤 Chandra V. Deshpandey
- 👤 Vasant D. Vankar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:16
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/0641; C23C14/0647; C23C14/22; C23C14/24; C23C14/32
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
226 words
A process for depositing a film of a nitride of a Group III element in the periodic table of elements on a substrate, comprising the steps of supporting the substrate in a vacuum; evaporating an easily evaporable compound containing a Group III element in the condensed state selected from the group consisting of boric acid and organometallic compounds of aluminum, indium and gallium, by a resistance-heated evaporation source to produce a vapor of said compound or its dissociated products in a zone between the resistance-heated evaporation source and the substrate; introducing ammonia gas into said zone; extracting low-energy electrons from a heated emitter by a d.c. electric field directed across the path of said vapor in said zone, which electric field is produced by applying an electric potential between the emitter and the anode of about 20 to 200 volts; directing a beam of the low-energy electrons laterally through said zone for colliding with the ammonia gas and said vapor to produce ions of ammonia and said vapor and energetic neutral atoms which react with each other and with atoms of ammonia and said vapor in said zone, resulting in a deposit of a nitride of a Group III element on the substrate; and providing a magnetic field surrounding the beam of low-energy electrons so as to increase the collision probability with atoms of the reactants.
Claim 2
Dependent Claim
226 words
A process for depositing a film of a nitride of a Group III element in the periodic table of elements on a substrate, comprising the steps of supporting the substrate in a vacuum; evaporating an easily evaporable compound containing a Group III element in the condensed state selected from the group consisting of boric acid and organometallic compounds of aluminum, indium and gallium, by a resistance-heated evaporation source to produce a vapor of said compound or its dissociated products in a zone between the resistance-heated evaporation source and the substrate; introducing ammonia gas into said zone; extracting low-energy electrons from a heated emitter by a d.c. electric field directed across the path of said vapor in said zone, which electric field is produced by applying an electric potential between the emitter and the anode of about 20 to 200 volts; directing a beam of the low-energy electrons laterally through said zone for colliding with the ammonia gas and said vapor to produce ions of ammonia and said vapor and energetic neutral atoms which react with each other and with atoms of ammonia and said vapor in said zone, resulting in a deposit of a nitride of a Group III element on the substrate; and providing a magnetic field surrounding the beam of low-energy electrons so as to increase the collision probability with atoms of the reactants.
Claim 3
Dependent Claim
33 words
The process of claim 1 including directing the beam of electrons from a heated cathode to an anode separate from the substrate, with an electric potential connected between the cathode and the anode.
Claim 4
Dependent Claim
27 words
The process of claim 1 with the substrate located above the resistance-heated evaporation source so that said vapor moves upward from the evaporation source toward the substrate.
Claim 5
Dependent Claim
14 words
The process of claim 1 including introducing an inert gas with the ammonia gas.
Claim 6
Dependent Claim
13 words
The process of claim 1 including introducing argon gas with the ammonia gas.
Claim 7
Dependent Claim
25 words
The process of claim 2 including heating the substrate to a predetermined temperature to control the electrical, mechanical and optical properties of the deposited film.
Claim 8
Dependent Claim
27 words
The process of claim 2 including producing low-energy electrons by applying an electrical potential between the cathode and the anode of about 20 to about 200 volts.
Claim 9
Dependent Claim
26 words
The process of claim 2 including producing low-energy electrons by applying an electric potential between the cathode and the anode in the order of 40 volts.
Claim 10
Dependent Claim
34 words
The process of claim 1 in which the Group III element is boron, said compound is Boric Acid (H 3 BO 3 ), and the deposit is of cubic boron nitride on the substrate.
Claim 11
Dependent Claim
33 words
The process of claim 9 including directing the beam of electrons from a heated cathode to an anode separate from the substrate, with an electric potential connected between the cathode and the anode.
Claim 12
Dependent Claim
27 words
The process of claim 9 with the substrate located above the resistance-heated evaporation source so that said vapor moves upward from the evaporation source toward the substrate.
Claim 13
Dependent Claim
14 words
The process of claim 9 including introducing an inert gas with the ammonia gas.
Claim 14
Dependent Claim
13 words
The process of claim 9 including introducing argon gas with the ammonia gas.
Claim 15
Dependent Claim
25 words
The process of claim 10 including heating the substrate to a predetermined temperature to control the electrical, mechanical and optical properties of the deposited film.
Claim 16
Dependent Claim
27 words
The process of claim 10 including producing low-energy electrons by applying an electric potential between the cathode and the anode of about 20 to about 200 volts.
Claim 17
Dependent Claim
26 words
The process of claim 10 including producing low-energy electrons by applying an electric potential between the cathode and the anode in the order of 40 volts.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-21 | 1991-06-22 | 1991-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-21 | 1995-06-22 | 1995-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-21 | 1999-06-22 | 1999-12-22 | $7700.00 | Window Closed / Lapsed |