US4713877A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of forming permanent magnets within a motor yoke
Assignee: Ford Motor Co
•
Filing: 1986-02-05
•
Granted: 1987-12-22
•
Expires: 2006-02-05
Abstract
Abstract A method of forming a 360° ceramic permanent magnet by utilizing a hot isostatic pressing technique on a ceramic preform paterial cylindrically formed and placed inside a deformable metal housing having an inner diameter that is approximately the same but only slightly larger than the outer diameter of the preform. A solid steel mandrel is provided in the center diameter of the hollow cylindrical preform. Crystal alignment and densification of the ceramic material is achieved by using the hot isostatic pressing technique applied to the outside of the housing, preform and mandrel assembly.
Inventors
- 👤 Edward H. Abbott
- 👤 Robert H. Erickson
- 👤 William F. Horn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 02:50
CPC Classifications
H; H01; H01F; H01F41/00; H01F41/02; H01F41/0253; H01F41/026; H02; H02K; H02K15/00; C; C04; C04B; C04B35/00; C04B35/01; C04B35/26; C04B35/2683; C04B35/622; C04B35/626; C04B35/63; C04B35/638; C04B35/64; C04B35/645; C04B35/6455; C04B37/00; C04B37/02; C04B37/021; H02K1/00; H02K1/06; H02K1/12; H02K1/17; H02K15/02; H02K15/03; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/658; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/40; C04B2237/405; C04B2237/406; C04B2237/50; C04B2237/52; C04B2237/525; C04B2237/56; C04B2237/567; C04B2237/76; C04B2237/765; C04B2237/84; Y; Y10; Y10S; Y10S264/00; Y10S264/58; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49009; Y10T29/4902; Y10T29/49075; Y10T29/49076
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
166 words
A method of forming multipoled ring magnets comprising the steps of: preparing a predetermined mixture of a ceramic hexaferrite platelet material; forming said mixture into a predetermined hollow cylindrical shape; providing a cylindrical metal housing of predetermined dimensions wherein the inside diameter is slightly larger than the outside diameter of said cylindrically formed mixture; placing said cylindrically formed mixture into said housing; providing a cylindrical mandrel having a predetermined outer diameter that is slightly less than that of the index diameter of said cylindrical mixture; evacuating volatile gases from said housing; hermetically sealing said housing containing said ceramic material mixture and said mandrel; applying inert gas at predetermined pressure and temperature to said sealed housing for a predetermined period of time to effect densification and platelet alignment of said ceramic material mixture; allowing said sealed housing to cool; removing said mandrel; cutting said housing, bearing the densified ceramic magnetic material, into predetermined lengths and magnetically charging the densified ceramic magnetic material to form multipoled ring magnets.
Claim 2
Independent Claim
166 words
A method of forming multipoled ring magnets comprising the steps of: preparing a predetermined mixture of a ceramic hexaferrite platelet material; forming said mixture into a predetermined hollow cylindrical shape; providing a cylindrical metal housing of predetermined dimensions wherein the inside diameter is slightly larger than the outside diameter of said cylindrically formed mixture; placing said cylindrically formed mixture into said housing; providing a cylindrical mandrel having a predetermined outer diameter that is slightly less than that of the index diameter of said cylindrical mixture; evacuating volatile gases from said housing; hermetically sealing said housing containing said ceramic material mixture and said mandrel; applying inert gas at predetermined pressure and temperature to said sealed housing for a predetermined period of time to effect densification and platelet alignment of said ceramic material mixture; allowing said sealed housing to cool; removing said mandrel; cutting said housing, bearing the densified ceramic magnetic material, into predetermined lengths and magnetically charging the densified ceramic magnetic material to form multipoled ring magnets.
Claim 3
Dependent Claim
22 words
A method as in claim 1, wherein said hexaferrite platelet material is selected from the group consisting of strontium, barium, and lead.
Claim 4
Dependent Claim
21 words
A method as in claim 2, wherein said hexaferrite material is a powder having grain sizes of less than 2 microns.
Claim 5
Dependent Claim
27 words
A method as in claim 2, wherein said temperature is applied within a range of from 1,600°-1,800° F. at a pressure in a range of 10,000-15,000 psi.
Claim 6
Dependent Claim
19 words
A method as in claim 2, further including a step of removing said housing from said densified ceramic material.
Claim 7
Dependent Claim
33 words
A method as in claim 1, wherein said step of applying pressure and heat to said sealed housing compressibly deforms said housing to conform to the densified shape of said ceramic magnetic material.
Claim 8
Independent Claim
222 words
A method of integrally forming a 360° cylindrical permanent motor magnet within a yoke comprising the steps of: forming a predetermined proportionate mixture of ceramic hexaferrite platelet magnet material into a hollow cylindrical shape having predetermined outer and inner diameter dimensions; providing a deformable hollow cylindrical metal container having an inner diameter that is only slightly larger than the outer diameter of said formed ceramic material mixture; providing a solid mandrel with a diameter that is only slightly smaller than the inner diameter of said formed ceramic material mixture; inserting said formed ceramic material mixture into said cylindrical container and said mandrel into said formed ceramic material mixture; hermetically sealing said container; isostatically applying heat and pressure to said sealed container at predetermined levels for a predetermined period of time to effect densification of said ceramic magnet material; cooling said sealed container; removing said mandrel from said densified ceramic magnetic material; and electromagnetically charging said densified ceramic material, after removal of said mandrel to define a plurality of poles to thereby provide a multipoled 360° cylindrical permanent magnet; wherein said sealed container is compressibly deformed against said densified ceramic magnetic material by said isostatic step and said 360° cylindrical magnet is integrally formed and held by compression in said deformed cylindrical container suitable for use as a yoke in a motor configuration.
Claim 9
Independent Claim
222 words
A method of integrally forming a 360° cylindrical permanent motor magnet within a yoke comprising the steps of: forming a predetermined proportionate mixture of ceramic hexaferrite platelet magnet material into a hollow cylindrical shape having predetermined outer and inner diameter dimensions; providing a deformable hollow cylindrical metal container having an inner diameter that is only slightly larger than the outer diameter of said formed ceramic material mixture; providing a solid mandrel with a diameter that is only slightly smaller than the inner diameter of said formed ceramic material mixture; inserting said formed ceramic material mixture into said cylindrical container and said mandrel into said formed ceramic material mixture; hermetically sealing said container; isostatically applying heat and pressure to said sealed container at predetermined levels for a predetermined period of time to effect densification of said ceramic magnet material; cooling said sealed container; removing said mandrel from said densified ceramic magnetic material; and electromagnetically charging said densified ceramic material, after removal of said mandrel to define a plurality of poles to thereby provide a multipoled 360° cylindrical permanent magnet; wherein said sealed container is compressibly deformed against said densified ceramic magnetic material by said isostatic step and said 360° cylindrical magnet is integrally formed and held by compression in said deformed cylindrical container suitable for use as a yoke in a motor configuration.
Claim 10
Dependent Claim
35 words
A method as in claim 7, wherein said cooled magnet material within said container is cut to predetermined lengths whereby each piece is suitable for use as a one piece yoke and motor magnet assembly.
References Cited (Backward Citations)
US2048161A
Cited
US2513227A
Cited
US2854412A
Cited
US3083310A
Cited
US3956440A
Cited
US3766642A
Cited
US3830743A
Cited
US3884823A
Cited
US4062922A
Cited
US4104787A
Cited
US4533407A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-21 | 1991-06-22 | 1991-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-21 | 1995-06-22 | 1995-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-21 | 1999-06-22 | 1999-12-22 | $7700.00 | Window Closed / Lapsed |