Foamed metal and method of producing same
Assignee: KOZO IIZUKA DIRECTOR-GENERAL OF AGENCY OF INDUSTRIAL SCIENCE AND TECHNOLOGY 3-1 KASUMIGASEKI 1-CHOME CHIYODA-KU TOKYO JAPAN
•
Filing: 1986-07-18
•
Granted: 1987-12-15
•
Expires: 2006-07-18
Abstract
Abstract A foamed metal which has an apparent specific gravity of from 0.2 to 0.8 and comprises an aggregate of polygonal closed cells of from 2 to 10 mm in average diameter. The foamed metal is not only light in weight, free of directionality and structurally strong but also excellent in sound-absorbing and electromagnetic shielding properties, and is useful as constructional, structural or functional material. A method for producing the foamed material comprises adding calcium as a thickening agent to molten aluminum or alloy thereof in an amount of from 0.2 to 8% by weight, followed by agitating to adjust the viscosity of the melet, then adding from 1 to 3% by weight of powdered titanium hydride as a foaming agent to the melt, and agitating the melt to effect foaming.
Inventors
- 👤 Shigeru Akiyama
- 👤 Hidetoshi Ueno
- 👤 Koji Imagawa
- 👤 Akira Kitahara
- 👤 Sumio Nagata
- 👤 Kazuo Morimoto
- 👤 Tooru Nishikawa
- 👤 Masao Itoh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:21
CPC Classifications
H; H05; H05K; H05K9/00; H05K9/0073; H05K9/0081; H05K9/0086; C; C22; C22C; C22C1/00; C22C1/08; C22C1/083; E; E04; E04B; E04B1/00; E04B1/62; E04B1/74; E04B1/82; E04B1/84; E04B1/86; B; B22; B22F; B22F3/00; B22F3/10; B22F3/11; B22F3/1103; B22F2003/1106; E04B2001/8414; E04B2001/8457; E04B2001/8461; E04B2001/8476; E04B2001/848; E04B2001/8495; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12479; Y10T428/24; Y10T428/24273
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
281 words
A method of producing a foamed metal having an apparent specific gravity of from 0.2 to 0.8 and comprising an aggregate of uniform size and uniformly dispersed of polygonal closed cells having an average diameter of from 2 to 10 mm, which comprises adding in a mold a foaming agent and a thickener to a molten metal and agitating the melt, said molten metal being aluminum or an alloy thereof, said thickener being elemental calcium and said foaming agent being titanium hydride, wherein said thickener is added to said molten metal in an amount of from 0.2 to 8% by weight, the melt is agitated to adjust the viscosity of said melt, then powdered titanium hydride is added to the melt in an amount of from 1 to 3% by weight, and the melt is agitated to effect foaming, wherein before said addition of said thickener the entire body of a mold is heated to a temperature not lower than the melting point of said metal to be foamed, thereafter in the process of growth of the foam the mold is closed in the condition in which an air release port is provided, air inside said mold is released to the exterior by expansion of a multiplicity of bubbles generated on thermal decomposition of the foaming agent, said molten metal is permitted to fill up the interior of said mold to close said release port thereby hermetically sealing said mold, the internal pressure of said bubbles in said hermetically sealed mold is increased to form a uniform cellular structure under the balanced internal pressures of said bubbles, the heating of said mold is stopped to cool and solidify said foamed metal.
Claim 2
Independent Claim
281 words
A method of producing a foamed metal having an apparent specific gravity of from 0.2 to 0.8 and comprising an aggregate of uniform size and uniformly dispersed of polygonal closed cells having an average diameter of from 2 to 10 mm, which comprises adding in a mold a foaming agent and a thickener to a molten metal and agitating the melt, said molten metal being aluminum or an alloy thereof, said thickener being elemental calcium and said foaming agent being titanium hydride, wherein said thickener is added to said molten metal in an amount of from 0.2 to 8% by weight, the melt is agitated to adjust the viscosity of said melt, then powdered titanium hydride is added to the melt in an amount of from 1 to 3% by weight, and the melt is agitated to effect foaming, wherein before said addition of said thickener the entire body of a mold is heated to a temperature not lower than the melting point of said metal to be foamed, thereafter in the process of growth of the foam the mold is closed in the condition in which an air release port is provided, air inside said mold is released to the exterior by expansion of a multiplicity of bubbles generated on thermal decomposition of the foaming agent, said molten metal is permitted to fill up the interior of said mold to close said release port thereby hermetically sealing said mold, the internal pressure of said bubbles in said hermetically sealed mold is increased to form a uniform cellular structure under the balanced internal pressures of said bubbles, the heating of said mold is stopped to cool and solidify said foamed metal.
Claim 3
Dependent Claim
70 words
A sound absorbing plate consisting of an open cell foamed metal produced by providing through-holes in cell walls of a foamed metal having an apparent specific gravity of from 0.2 to 0.8 and comprising an aggregate of uniform size and uniformly dispersed of polygonal closed cells having an average diameter of from 2 to 10 mm so as to communicate both sides of said foamed metal plate to each other.
Claim 4
Dependent Claim
70 words
A sound absorbing plate consisting of an open cell foamed metal produced by providing through-holes in cell walls of a foamed metal having an apparent specific gravity of from 0.2 to 0.8 and comprising an aggregate of uniform size and uniformly dispersed of polygonal closed cells having an average diameter of from 2 to 10 mm so as to communicate both sides of said foamed metal plate to each other.
Claim 5
Dependent Claim
68 words
An electromagnetic shielding material consisting of a foamed metal plate having an apparent specific gravity of from 0.2 to 0.8 and comprising an aggregate of uniform size and uniformly dispersed of polygonal closed cells having an average diameter of from 2 to 10 mm, provided with through-holes, wherein the diameter of the through-holes communicating both sides of said plate to each other is not larger than 5 mm.
Claim 6
Dependent Claim
68 words
An electromagnetic shielding material consisting of a foamed metal plate having an apparent specific gravity of from 0.2 to 0.8 and comprising an aggregate of uniform size and uniformly dispersed of polygonal closed cells having an average diameter of from 2 to 10 mm, provided with through-holes, wherein the diameter of the through-holes communicating both sides of said plate to each other is not larger than 5 mm.
References Cited (Backward Citations)
US2751289A
Cited
US2983597A
Cited
US3300296A
Cited
US3617364A
Cited
US3816952A
Cited
US3711363A
Cited
US3708380A
Cited
US3839080A
Cited
JPS49259A
Cited
GB2102808A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-14 | 1991-06-15 | 1991-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-14 | 1995-06-15 | 1995-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-14 | 1999-06-15 | 1999-12-15 | $7700.00 | Window Closed / Lapsed |