US4711702A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Protective containerboard
Assignee: Caraustar Industries Inc
•
Filing: 1985-09-25
•
Granted: 1987-12-08
•
Expires: 2005-09-25
Abstract
Abstract Antistatic cartons of containerboard having 0.3 to 3.5 percent by weight conductive carbon for protecting electrostatic discharge sensitive devices. The containerboard is made from an alkaline pulp which eliminates acid contamination, increases shelf life, provides Mullen burst strength in the linerboard which exceeds 90(±1) pounds per square inch. The surface resistivity is in the range of from 10 3 to 10 9 ohms per square. The carton includes conductive adhesives to insure dissipation of any static charges.
Inventors
- 👤 Paul F. Hood
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 00:55
CPC Classifications
H; H05; H05K; H05K9/00; H05K9/0073; H05K9/0079; H01; H01B; H01B1/00; H01B1/20; H01B1/24
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
116 words
A containerboard of improved strength for protecting electrostatic discharge sensitive devices against static electricity damage, electromagnetic damage and physical damage; said containerboard being formed from an alkaline pulp, including a mixture of beaten cellulosic fibrous material, alkylketene dimer size and uncombined carbon powder and being characterized, when measured from a sample having a caliper of 10(±1) mils, by the following properties: wherein said alkylketene dimer is present in an amount sufficient to fix said uncombined carbon powder within the range of from 0.3 to 3.5 percent by weight, a Mullen burst strength which exceeds 90(±1) pounds per square inch and a surface resistivity within the range of from 10 3 to 10 9 ohms per square.
Claim 2
Dependent Claim
116 words
A containerboard of improved strength for protecting electrostatic discharge sensitive devices against static electricity damage, electromagnetic damage and physical damage; said containerboard being formed from an alkaline pulp, including a mixture of beaten cellulosic fibrous material, alkylketene dimer size and uncombined carbon powder and being characterized, when measured from a sample having a caliper of 10(±1) mils, by the following properties: wherein said alkylketene dimer is present in an amount sufficient to fix said uncombined carbon powder within the range of from 0.3 to 3.5 percent by weight, a Mullen burst strength which exceeds 90(±1) pounds per square inch and a surface resistivity within the range of from 10 3 to 10 9 ohms per square.
Claim 3
Dependent Claim
21 words
The containerboard of claim 1 in which the ring crush test indicates a resistance to failure in excess of 60(±1) pounds.
Claim 4
Dependent Claim
20 words
The containerboard of claim 1 in which the average stretch of the material before failure exceeds 2.5 per cent extension.
Claim 5
Dependent Claim
22 words
The containerboard of claim 1 in which the surface resistivity is within the range 10 3 - 10 5 ohms per square.
Claim 6
Dependent Claim
25 words
The containerboard of claim 1 in which components of linerboard and corrugating medium are adhesively joined by means of an adhesive having conductive material additions.
Claim 7
Dependent Claim
41 words
The containerboard of claim 5 in which the adhesive having conductive material additions is a vinamyl waterproof adhesive with high amylose content and a conductive polymer within the range of 15 to 35 percent by weight of the total starch solids.
Claim 8
Dependent Claim
14 words
The containerboard of claim 6 in which the conductive polymer is polydimethyldiallyl ammonium chloride.
Claim 9
Dependent Claim
26 words
The containerboard of claim 5 in which a manufacturer's joint of conductive glue and a plurality of scored fold lines are provided to define a carton.
Claim 10
Dependent Claim
27 words
The containerboard of claim 8 with a manufacturer's joint of conductive glue in which the conductive glue is white glue to which is added a conductive polymer.
Claim 11
Dependent Claim
14 words
The containerboard of claim 9 in which the conductive polymer is polydimethyldiallyl ammonium chloride.
Claim 12
Independent Claim
137 words
A method of making alkaline containerboard of improved strength having a surface resistivity within the range of from about 10 3 to about 10 9 ohms per square for producing containers for protecting electrostatic discharge sensitive devices against static electricity damage, electromagnetic damage and physical damange, comprising the steps of: (a) beating a cellulosic fibrous material with adjustment of the pH to bout 8.5; (b) adding alkylketene dimer size and conductive carbon powder sufficient to provide a surface resistivity within the range of from about 10 3 to about 10 9 ohms per square, of the containerboard to be produced, and beating to produce a homogeneous uncombined carbon-loaded pulp, said alkylketene dimer size being present in an amount sufficient to fix said carbon powder to provide said resistivity; and (c) making a containerboard sheet from said pulp.
Claim 13
Independent Claim
137 words
A method of making alkaline containerboard of improved strength having a surface resistivity within the range of from about 10 3 to about 10 9 ohms per square for producing containers for protecting electrostatic discharge sensitive devices against static electricity damage, electromagnetic damage and physical damange, comprising the steps of: (a) beating a cellulosic fibrous material with adjustment of the pH to bout 8.5; (b) adding alkylketene dimer size and conductive carbon powder sufficient to provide a surface resistivity within the range of from about 10 3 to about 10 9 ohms per square, of the containerboard to be produced, and beating to produce a homogeneous uncombined carbon-loaded pulp, said alkylketene dimer size being present in an amount sufficient to fix said carbon powder to provide said resistivity; and (c) making a containerboard sheet from said pulp.
Claim 14
Dependent Claim
89 words
The pulp produced by the process comprising the steps of: (a) beating a cellulosic fibrous material with adjustment of the pH to about 8.5; and (b) adding alkylketene dimer size and conductive carbon powder sufficient to provide a surface resistivity within the range of from about 10 3 to about 10 9 ohms per square, of the containerboard to be produced, and beating to produce a homogeneous uncombined carbon-loaded pulp, said alkylketene dimer size being present in an amount sufficient to fix said carbon powder to provide said resistivity.
Claim 15
Dependent Claim
89 words
The pulp produced by the process comprising the steps of: (a) beating a cellulosic fibrous material with adjustment of the pH to about 8.5; and (b) adding alkylketene dimer size and conductive carbon powder sufficient to provide a surface resistivity within the range of from about 10 3 to about 10 9 ohms per square, of the containerboard to be produced, and beating to produce a homogeneous uncombined carbon-loaded pulp, said alkylketene dimer size being present in an amount sufficient to fix said carbon powder to provide said resistivity.
References Cited (Backward Citations)
US4559103A
Cited
US4606790A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-07 | 1991-06-08 | 1991-12-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-07 | 1995-06-08 | 1995-12-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-07 | 1999-06-08 | 1999-12-08 | $7700.00 | Window Closed / Lapsed |