Diesel exhaust gas catalyst
Assignee: KAT-TEC GESELLSCHAFT fur KATALYSATORTECHNIK MBH
•
Filing: 1986-02-07
•
Granted: 1987-12-01
•
Expires: 2006-02-07
Abstract
Abstract A catalyst for the reaction of hydrocarbons and gases and for the reduction of nitric oxides, includes the active substance thorium oxide in addition to LaCoO 3 . The catalyst has as the wash coat oxide-ceramic materials and spinels of the oxides of magnesium, aluminum, titanium and zirconium, with an addition of cerium oxide and lanthanum oxide, and preformed and acid-solubilized LaCoO 3 as the active substance. The catalyst is formed without the active substance LaCoO 3 for use as a high-temperature combustion catalyst. A process and apparatus is set forth for the application of the catalyst for after-burning of exhaust gases from diesel engines, with catalyst filler layers eccentrically disposed with respect to each other for the adsorption of soot particles, and with a catalyst honeycomb for after-burning and nitric oxide-reduction. The after-burning device is suitable also as a muffler.
Inventors
- 👤 Christian Koch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:50
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/83; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01D53/8643; B01D53/8646; B01D53/865; Y; Y10; Y10S; Y10S502/00; Y10S502/525
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
30 words
A catalyst for converting hydrocarbons, nitric oxides, and combustion gases comprising: LaCoO 3 serving as a catalyst component, and thorium oxide serving as both a catalyst component and a stabilizer.
Claim 2
Dependent Claim
30 words
A catalyst for converting hydrocarbons, nitric oxides, and combustion gases comprising: LaCoO 3 serving as a catalyst component, and thorium oxide serving as both a catalyst component and a stabilizer.
Claim 3
Dependent Claim
34 words
The catalyst according to claim 1, utilizing one other component which is a ceramic oxide material selected from the group consisting of the oxides of thorium, zirconium, cerium, aluminum, magnesium-aluminum oxide spinel, and lanthanum.
Claim 4
Dependent Claim
24 words
The catalyst according to claim 1, wherein the catalyst components thorium oxide and lanthanum oxide are used in a ratio of 1:1 to 1:10.
Claim 5
Dependent Claim
26 words
The catalyst according to claim 1, wherein cerium oxide is added as an additional component with a ratio of 0.2 to 2 to said thorium oxide.
Claim 6
Dependent Claim
40 words
The catalyst according to claim 1, wherein said catalyst components comprise 8% to 30% of a member selected from the group consisting of thorium oxide or cerium oxide; 8% to 30% lanthanum oxide; and 30% to 84% LaCoO 3 .
Claim 7
Dependent Claim
41 words
A process for preparing a ceramic body catalyst for converting exhaust gas hydrocarbons, nitric oxides, and combustion gases comprising the steps of: coating a ceramic body with catalyst components including LaCoO 3 and thorium oxide; and baking the coated ceramic body.
Claim 8
Dependent Claim
41 words
A process for preparing a ceramic body catalyst for converting exhaust gas hydrocarbons, nitric oxides, and combustion gases comprising the steps of: coating a ceramic body with catalyst components including LaCoO 3 and thorium oxide; and baking the coated ceramic body.
Claim 9
Dependent Claim
26 words
The process according to claim 6, further comprising the steps of separately preparing LaCoO 3 in an acid-stabilized state and applying it to the ceramic body.
Claim 10
Dependent Claim
43 words
The process according to claim 6, wherein the ceramic body is coated first with a wash coat comprising of a ceramic-oxide substance containing from 1% to 10% by mass lanthanum and thorium with the two components having a ratio of 20% to 80%.
Claim 11
Dependent Claim
42 words
The process according to claim 6, further comprising the steps of: preparing a suspension of the catalyst components as oxides or salts in an organic acid solution of the acid associated with the salts; and applying the suspension to the ceramic body.
Claim 12
Dependent Claim
34 words
The process according to claim 6, further comprising the step of: decomposing the catalyst component applied to the ceramic body by subsequently rebaking the ceramic body at a temperature range not exceeding 1000° C.
Claim 13
Dependent Claim
27 words
The process according to claim 10, further comprising the steps of activating the catalyst components by exposing it to baking gas at from 50° to 400° C.
Claim 14
Dependent Claim
69 words
The process according to claim 6, wherein the catalyst component is applied by impregnation in a first stage, and the LaCoO 3 and a second portion of the thorium oxide or thorium salt is applied by impregnation in a second stage following the baking process, such that the ratio of the thorium oxide content between the first and second stages is in the range of from 1:1 to 5:1.
Claim 15
Dependent Claim
30 words
The process according to claim 8, wherein the wash coat includes oxide-ceramic substances selected from the group consisting of magnesium-aluminum oxide spinel, titanium oxide, zirconium oxide, and a combination thereof.
Claim 16
Dependent Claim
56 words
The process according to claim 8, wherein the wash coat includes a member selected from the group consisting of lanthanum oxide, thorium oxide, cerium oxide and a combination thereof, and is applied to the ceramic body without the LaCoO 3 , for the application of the catalyst as a combustion catalyst at temperatures above 700° C.
Claim 17
Dependent Claim
30 words
The process according to claim 6, wherein the catalyst component is formed and applied by prior baking of the individual substances, fine grinding of the oxide, and subsequent acid solubilizing.
Claim 18
Dependent Claim
22 words
A ceramic body catalyst comprising an inactive ceramic body supplied with a coating of catalyst components comprising LaCoO 3 and thorium oxide.
Claim 19
Dependent Claim
22 words
A ceramic body catalyst comprising an inactive ceramic body supplied with a coating of catalyst components comprising LaCoO 3 and thorium oxide.
Claim 20
Dependent Claim
51 words
The ceramic body catalyst according to claim 16, wherein the coating contains from 60% to 95% of an oxide-ceramic substance; 4% to 30% LaCoO 3 ; 1% 5% thorium oxide, 1% to 9% lanthanum oxide; with the coating making up from 6% to 12% of the total mass of the body.
Claim 21
Dependent Claim
45 words
The ceramic body catalyst according to claim 17, wherein the oxide-ceramic substance is a member selected from the group consisting of zirconium oxide, magnesium-aluminum oxide spinel, aluminum oxide, titanium oxide, and a combination thereof, and wherein the coating additionally includes 1% to 5% cerium oxide.
Claim 22
Dependent Claim
66 words
The ceramic body according to claim 16, wherein the ceramic body is supplied with a catalyst component by solution impregnation and non-ceramic substance amounts to 0.1% to 3% by weight with the proportion of the catalyst components of the impregnating solution being 20% to 90% LaCoO 3 ; 2% to 10% thorium oxide; and 2% to 20% lanthanum oxide, with the balance thereof being other components.
Claim 23
Dependent Claim
23 words
The ceramic body according to claim 16, wherein the inactive ceramic body has a porosity of 10% to 55% based on water absorption.
Claim 24
Dependent Claim
34 words
The ceramic body catalyst according to claim 16, wherein the inactive ceramic body is a member selected from the group consisting of cordierite, zirocnium oxide, magnesium-aluminum oxide spinel, aluminum oxide, and a combination thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-30 | 1991-06-01 | 1991-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-30 | 1995-06-01 | 1995-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-30 | 1999-06-01 | 1999-12-01 | $7700.00 | Window Closed / Lapsed |