Rapid sintering feedstock for injection molding of stainless steel parts
Assignee: Flomet LLC
•
Filing: 1986-06-13
•
Granted: 1987-11-24
•
Expires: 2006-06-13
Abstract
Abstract A feedstock, for the production of stainless steel injection molded parts, capable of producing high theoretical density using lower than conventional sintering temperatures. In the production of powder metal parts, densities approaching theoretical density are normally achieved by the use of high compaction pressures, high temperature sintering, or a combination of both. By employing a higher chromium content and a lower nickel content than conventional 316L stainless steel, a duplex structure of ferrite and austenite will be produced with superior sintering capability--resulting in higher densification and better mechanical properties at lower sintering temperatures.
Inventors
- 👤 German Amaya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:33
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0285
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
118 words
A feedstock for the injection molding of type 300 stainless steel parts, consisting essentially of 75-95 weight percent finely divided metal powders; the balance, sacrificial binder materials, characterized by metal powders substantially all of which are finer than 40 microns and having a mean particle size finer than 15 microns, the cumulative concentrations of said powders consisting essentially of 18 to less than 20% Cr, 6 to less than 8% Ni, 1 to less than 2% Mo, with the balance essentially Fe and minor amounts of elements such as nitrogen, carbon, manganese, sulphur, phosphorus, and silicon, normally present in such type 300 steels, and wherein the ratio of chromium equivalents to nickel equivalents is within the range 1.4-1.65.
Claim 2
Dependent Claim
118 words
A feedstock for the injection molding of type 300 stainless steel parts, consisting essentially of 75-95 weight percent finely divided metal powders; the balance, sacrificial binder materials, characterized by metal powders substantially all of which are finer than 40 microns and having a mean particle size finer than 15 microns, the cumulative concentrations of said powders consisting essentially of 18 to less than 20% Cr, 6 to less than 8% Ni, 1 to less than 2% Mo, with the balance essentially Fe and minor amounts of elements such as nitrogen, carbon, manganese, sulphur, phosphorus, and silicon, normally present in such type 300 steels, and wherein the ratio of chromium equivalents to nickel equivalents is within the range 1.4-1.65.
Claim 3
Dependent Claim
38 words
The feedstock of claim 1, in which N does not exceed 0.05%, C does not exceed 0.03%, Mn does not exceed 0.5%, S does not exceed 0.03%, P does not exceed 0.05%, and Si does not exceed 0.5%.
Claim 4
Dependent Claim
25 words
The feedstock of claim 2, in which a major portion of the elements Cr, Ni, and Mo are provided by unalloyed powders of such elements.
Claim 5
Dependent Claim
21 words
The feedstock of claim 3, in which more than 90% of said powders are within the range 2 to 30 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-23 | 1991-05-25 | 1991-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-23 | 1995-05-25 | 1995-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-23 | 1999-05-25 | 1999-11-24 | $7700.00 | Window Closed / Lapsed |