Method of making a fiber reinforced product
Assignee: Boeing Co
•
Filing: 1986-03-24
•
Granted: 1987-11-17
•
Expires: 2006-03-24
Abstract
Abstract A method of manufacturing fiber reinforced silicone elastomer hoses and the hoses (25) resulting from the method are disclosed. The method comprises the step of extruding an unreinforced silicone elastomer inner tube (13) containing two vulcanizing agents having different activation temperatures. The extruded inner tube (13) is partially cured by heating the tube to the activation temperature of the lower temperture vulcanizing agent. The partially cured inner tube (13) is mounted on a mandrel (19) and wrapped with a fabric reinforced, calendered sheet (21) of uncured silicone elastomer containing a vulcanizing agent. External pressure is applied to the wrapped tube while the wrapped tube is heated to activate the second vulcanizing agent of the inner tube (13) and the vulcanizing agent of the wrapping sheet (21).
Inventors
- 👤 George E. Trepus, Jr.
- 👤 Barry D. Matin
- 👤 Preston L. Rider
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 05:41
CPC Classifications
B; B32; B32B; B32B25/00; B32B25/02; B29; B29C; B29C48/00; B29C48/022; B29C48/03; B29C48/07; B29C48/08; B29C53/00; B29C53/56; B29C53/566; B29C53/80; B29C53/84; B29C53/845; B29C61/00; B29C61/006; B29D; B29D23/00; B29D23/001; B32B1/00; B32B1/08; B32B25/20; F; F16; F16L; F16L11/00; F16L11/04; F16L11/10; B29K; B29K2021/00; B29K2083/00; B29K2105/00; B29K2105/24; B29K2105/243; B29L; B29L2009/00; B32B38/00; B32B2038/0052; B32B2038/0076; B32B2260/00; B32B2260/04; B32B2260/048; B32B2262/00; B32B2262/02; B32B2262/0261; B32B2262/0269; B32B2307/00; B32B2307/70; B32B2307/732; B32B2307/734; B32B2307/736; B32B2597/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
127 words
A method of manufacturing fiber reinforced silicone elastomer product comprising the steps of: (a) extruding an unreinforced silicone elastomer inner element containing two vulcanizing agents activated at different temperatures; (b) partially curing said silicone elastomer inner element by heating said element to a temperature at or above the activation temperature of the lower temperature vulcanizing agent but below the activation temperature of the higher temperature vulcanizing agent; (c) overwrapping said silicone elastomer inner element with a fabric reinforced, calendered sheet of uncured silicone elastomer containing a vulcanizing agent to create an overwrapped element; and, (d) applying external pressure to the overwrapped element while heating the overwrapped element to activate the second vulcanizing agent of the silicone elastomer inner element and the vulcanizing agent of the overwrapping sheet.
Claim 2
Independent Claim
127 words
A method of manufacturing fiber reinforced silicone elastomer product comprising the steps of: (a) extruding an unreinforced silicone elastomer inner element containing two vulcanizing agents activated at different temperatures; (b) partially curing said silicone elastomer inner element by heating said element to a temperature at or above the activation temperature of the lower temperature vulcanizing agent but below the activation temperature of the higher temperature vulcanizing agent; (c) overwrapping said silicone elastomer inner element with a fabric reinforced, calendered sheet of uncured silicone elastomer containing a vulcanizing agent to create an overwrapped element; and, (d) applying external pressure to the overwrapped element while heating the overwrapped element to activate the second vulcanizing agent of the silicone elastomer inner element and the vulcanizing agent of the overwrapping sheet.
Claim 3
Dependent Claim
25 words
The method claimed in claim 1, wherein the fabric of said fabric reinforced, calendered sheet of uncured silicone elastomer is made of aromatic polyamide fibers.
Claim 4
Dependent Claim
25 words
The method claimed in claim 2, wherein said external pressure is applied by wrapping said element with a layer of material that shrinks when heated.
Claim 5
Dependent Claim
22 words
The method claimed in claim 2, wherein said external pressure is applied by clamping said overwrapped element between a pair of jaws.
Claim 6
Dependent Claim
59 words
The method claimed in claim 1, including the additional step of applying an outer layer of high density fabric to said overwrapped element prior to said step of applying pressure to said overwrapped element while heating the overwrapped element to activate the second vulcanizing agent of the silicone elastomer inner element and the vulcanizing agent of the overwrapping sheet.
Claim 7
Dependent Claim
25 words
The method claimed in claim 5, wherein the fabric of said fabric reinforced, calendered sheet of uncured silicone elastomer is made of aromatic polyamide fibers.
Claim 8
Dependent Claim
25 words
The method claimed in claim 6, wherein said external pressure is applied by wrapping said element with a layer of material that shrinks when heated.
Claim 9
Dependent Claim
22 words
The method claimed in claim 6, wherein said external pressure is applied by clamping said overwrapping element between a pair of jaws.
Claim 10
Dependent Claim
13 words
The method claimed in claim 1, wherein said inner element is a tube.
Claim 11
Dependent Claim
33 words
The method claimed in claim 9, including the step of mounting said inner tube on a mandrel prior to overwrapping said inner tube with said fabric reinforced, calendered sheet of uncured silicone elastomer.
Claim 12
Dependent Claim
25 words
The method claimed in claim 10, wherein the fabric of said fabric reinforced, calendered sheet of uncured silicone elastomer is made of aromatic polyamide fibers.
Claim 13
Dependent Claim
25 words
The method claimed in claim 11, wherein said external pressure is applied by wrapping said element with a layer of material that shrinks when heated.
Claim 14
Dependent Claim
22 words
The method claimed in claim 11, wherein said external pressure is applied by clamping said overwrapped element between a pair of jaws.
Claim 15
Dependent Claim
59 words
The method claimed in claim 10, including the additional step of applying an outer layer of high density fabric to said overwrapped element prior to said step of applying pressure to said overwrapped element while heating the overwrapped element to activate the second vulcanizing agent of the silicone elastomer inner element and the vulcanizing agent of the overwrapping sheet.
Claim 16
Dependent Claim
25 words
The method claimed in claim 14, wherein the fabric of said fabric reinforced, calendered sheet of uncured silicone elastomer is made of aromatic polyamide fibers.
Claim 17
Dependent Claim
25 words
The method claimed in claim 15, wherein said external pressure is applied by wrapping said element with a layer of material that shrinks when heated.
Claim 18
Dependent Claim
22 words
The method claimed in claim 15, wherein said external pressure is applied by clamping said overwrapped element between a pair of jaws.
References Cited (Backward Citations)
US2974713A
Cited
US3414448A
Cited
GB1305893A
Cited
US3684602A
Cited
US4061704A
Cited
US4262704A
Cited
US4559782A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-16 | 1991-05-18 | 1991-11-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-16 | 1995-05-18 | 1995-11-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-16 | 1999-05-18 | 1999-11-17 | $7700.00 | Window Closed / Lapsed |