Composition and method for metal surface refinement

Claim 2

An aqueous solution for use in the refinement of metal surfaces, comprising water, a water-soluble oxalate compound, a water-soluble nitrate compound, and a water-soluble peroxy compound, said solution containing a sufficient amount of said oxalate compound to provide about 0.125 to 0.65 gram mole per liter of the oxalate radical, a sufficient amount of said nitrate compound to provide at least about 0.004 gram mole per liter of the nitrate radical, and a sufficient amount of said peroxy compound to provide 0.001 to 0.05 gram mole per liter of the peroxy group.

Claim 3

The solution of claim 1 wherein said nitrate compound provides up to about 0.2 gram mole per liter of the nitrate radical.

Claim 4

The solution of claim 1 wherein said oxalate compound provides about 0.25 to 0.45 gram mole per liter of the oxalate radical, wherein said nitrate compound provides about 0.05 to 0.11 gram mole per liter of the nitrate radical, and wherein said peroxy compound provides about 0.01 to 0.03 gram mole per liter of the peroxy group.

Claim 5

The solution of claim 1 containing about 0.4 gram mole per liter of the oxalate radical, about 0.1 gram mole per liter of the nitrate radical, and 0.02 gram mole per liter of the peroxy group.

Claim 6

The solution of claim 1 additionally including an effective amount of a wetting agent.

Claim 7

The solution of claim 1 wherein said oxalate compound is oxalic acid, said nitrate compound is sodium nitrate, and said peroxy compound is hydrogen peroxide, said solution having a pH of about 1.5 to 3.0.

Claim 8

A composition for addition to water to provide an aqueous solution for use in the refinement of metal surfaces, comprising a water-soluble oxalate compound, a water-soluble nitrate compound, and a water-soluble peroxy compound, said composition including said compounds in quantities sufficient to provide, upon dilution with one liter of water, about 0.125 to 0.65 gram mole of the oxalate radical, at least about 0.004 gram mole of the nitrate radical, and 0.001 to 0.05 gram mole of the peroxy group.

Claim 9

A composition for addition to water to provide an aqueous solution for use in the refinement of metal surfaces, comprising a water-soluble oxalate compound, a water-soluble nitrate compound, and a water-soluble peroxy compound, said composition including said compounds in quantities sufficient to provide, upon dilution with one liter of water, about 0.125 to 0.65 gram mole of the oxalate radical, at least about 0.004 gram mole of the nitrate radical, and 0.001 to 0.05 gram mole of the peroxy group.

Claim 10

The composition of claim 7 wherein said compounds are solid under ambient conditions, said composition being in the form of a substantially dry powder.

Claim 11

The composition of claim 8 wherein said oxalate compound is oxalic acid, said nitrate compound is sodium nitrate, and said peroxy compound is selected from the group consisting of sodium perborate, sodium percarbonate, sodium persulfate, ammonium persulfate, potassium perborate, and potassium persulfate.

Claim 12

In a process for the refinement of metal surfaces of objects, the steps comprising: (a) providing an aqueous solution including water, a water-soluble oxalate compound, a water-soluble nitrate compound, and a water-soluble peroxy compound, said solution containing a sufficient amount of said oxalate compound to provide about 0.125 to 0.65 gram mole per liter of the oxalate radical, a sufficient amount of said nitrate compound to provide at least about 0.004 gram mole per liter of the nitrate radical, and a sufficient amount of said peroxy compound to provide 0.001 to 0.05 gram mole per liter of the peroxy group; (b) introducing into the container of a mass finishing unit a mass of elements comprising of a quantity of objects with metal surfaces; (c) wetting said mass of elements with said solution; (d) rapidly agitating said mass of elements while maintaining said surfaces in a wetted condition with said solution, said agitation producing relative movement and contact among said elements; and (e) continuing said agitation step for a period sufficient to effect a significant reduction in roughness of said surfaces.

Claim 13

In a process for the refinement of metal surfaces of objects, the steps comprising: (a) providing an aqueous solution including water, a water-soluble oxalate compound, a water-soluble nitrate compound, and a water-soluble peroxy compound, said solution containing a sufficient amount of said oxalate compound to provide about 0.125 to 0.65 gram mole per liter of the oxalate radical, a sufficient amount of said nitrate compound to provide at least about 0.004 gram mole per liter of the nitrate radical, and a sufficient amount of said peroxy compound to provide 0.001 to 0.05 gram mole per liter of the peroxy group; (b) introducing into the container of a mass finishing unit a mass of elements comprising of a quantity of objects with metal surfaces; (c) wetting said mass of elements with said solution; (d) rapidly agitating said mass of elements while maintaining said surfaces in a wetted condition with said solution, said agitation producing relative movement and contact among said elements; and (e) continuing said agitation step for a period sufficient to effect a significant reduction in roughness of said surfaces.

Claim 14

The process of claim 10 wherein said solution contains about 0.25 to 0.45 gram mole per liter of the oxalate radical, wherein said nitrate compound provides about 0.05 to 0.11 gram mole per liter of the nitrate radical, and wherein said peroxy compound provides about 0.01 to 0.03 gram mole per liter of the peroxy group.

Claim 15

The process of claim 10 wherein said mass of elements includes a quantity of mass finishing media.

Claim 16

The process of claim 10 wherein said metal surfaces have a finish of arithmetic average roughness in excess of about 30 at the time of introduction, and wherein said significant reduction in roughness produces an arithmetic roughness value of about 6.

Claim 17

The process of claim 13 wherein said period of said agitation step is about four hours or less.

Claim 18

The process of claim 14 wherein said agitation step produces continuous oxygenation of said solution.

Claim 19

The process of claim 15 wherein said solution is provided in an amount equal to about 15 to 25 percent of the volume of said mass finishing unit container.

Claim 20

The process of claim 10 wherein the metal of said object surfaces is selected from the group consisting of iron and alloys thereof.