Fiber-reinforced rubber composition and production process thereof and fiber-reinforced elastic product
Assignee: Ube Corp
•
Filing: 1985-10-21
•
Granted: 1987-10-27
•
Expires: 2005-10-21
Abstract
Abstract A fiber-reinforced rubber composition capable of providing a vulcanizate having an excellent strength and modulus and a production process thereof. This fiber-reinforced rubber composition includes fine short fibers of thermoplastic polymer having <IMAGE> groups buried in vulcanizable rubber. The vulcanizable rubber and the thermoplastic polymer are grafted to each other through a resol type alkylphenol formaldehyde resin precondensate or a novolak type phenol formaldehyde resin precondensate at an interface of the fiber. The ratio of the fiber to the vulcanizable rubber (A) 1 to 70 parts by weight based on 100 parts by weight of the rubber in the case of the resol type alkylphenol formaldehyde resin precondensate or (B) 1 to 100 parts by weight based on 100 parts by weight of the rubber in the case of the novolak type phenol formaldehyde resin precondensate.
Inventors
- 👤 Shinji Yamamoto
- 👤 Kouhei Kaijiri
- 👤 Kouichi Nagakura
- 👤 Denichi Oda
- 👤 Yasuo Matsumori
- 👤 Kimio Nakayama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 02:41
CPC Classifications
C; C08; C08G; C08G81/00; C08G81/02; C08G81/024; C08G81/028; C08K; C08K7/00; C08K7/02; C08L; C08L21/00; C08L51/00; C08L51/04; C08L51/08; C08L7/00; C08L77/00; Y; Y10; Y10S; Y10S525/00; Y10S525/935
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
185 words
A process for producing a fiber-reinforced rubber composition comprising the steps of: mixing vulcanizable rubber, fiber-forming polyamide having ##STR22## groups and having a number-average molecular weight of less than 200,000 and 0.2 to 2.5 parts by weight, based on 100 parts by weight of the total amount of the rubber and the polyamide, of a resol type alkylphenol formaldehyde resin precondensate together at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; adding additional vulcanizable rubber in a quantity such that the amount of polyamide in the resultant mixture is within a range of 1 to 70 parts by weight based on 100 parts by weight of the vulcanizable rubber and further mixing the resultant mixture at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; extruding the mixture from an extruder at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; and drawing an extrudate at a temperature of less than the melting point of the polyamide.
Claim 2
Dependent Claim
185 words
A process for producing a fiber-reinforced rubber composition comprising the steps of: mixing vulcanizable rubber, fiber-forming polyamide having ##STR22## groups and having a number-average molecular weight of less than 200,000 and 0.2 to 2.5 parts by weight, based on 100 parts by weight of the total amount of the rubber and the polyamide, of a resol type alkylphenol formaldehyde resin precondensate together at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; adding additional vulcanizable rubber in a quantity such that the amount of polyamide in the resultant mixture is within a range of 1 to 70 parts by weight based on 100 parts by weight of the vulcanizable rubber and further mixing the resultant mixture at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; extruding the mixture from an extruder at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; and drawing an extrudate at a temperature of less than the melting point of the polyamide.
Claim 3
Dependent Claim
20 words
A process as claimed in claim 8, wherein the melting point of the polyamide is 190° C. to 235° C.
Claim 4
Dependent Claim
66 words
A process as claimed in claim 1, wherein the resol type alkylphenol formaldehyde resin precondensate has the general formula: ##STR23## Wherein R is an alkyl group having 1 to 15 carbon atoms, or a combination of said alkyl group and a hydrogen atom; X is a hydroxyl group or a halogen atom; m is 1 or 2; and n is a number of 2 to 15.
Claim 5
Dependent Claim
13 words
A process as claimed in claim 3 wherein X is chlorine or bromine.
Claim 6
Dependent Claim
193 words
A process for producing a fiber-reinforced rubber composition comprising the steps of: mixing vulcanizable rubber, fiber-forming polyamide having ##STR24## groups and having a number-average molecular weight of less than 200,000, 0.2 to 5 parts by weight, based on 100 arts by weight of the total amount of the rubber and the polyamide, of a novolak type phenol formaldehyde resin precondensate, and a compound capable of producing formaldehyde upon heating together at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; adding additional vulcanizable rubber in a quantity such that the amount of polyamide in the resultant mixture is within a range of 1 to 100 parts by weight based on 100 parts by weight of the vulcanizable rubber and further mixing the resultant mixture at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; extruding the mixture from an extruder at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; and drawing an extrudate at a temperature of less than the melting point of the polyamide.
Claim 7
Dependent Claim
193 words
A process for producing a fiber-reinforced rubber composition comprising the steps of: mixing vulcanizable rubber, fiber-forming polyamide having ##STR24## groups and having a number-average molecular weight of less than 200,000, 0.2 to 5 parts by weight, based on 100 arts by weight of the total amount of the rubber and the polyamide, of a novolak type phenol formaldehyde resin precondensate, and a compound capable of producing formaldehyde upon heating together at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; adding additional vulcanizable rubber in a quantity such that the amount of polyamide in the resultant mixture is within a range of 1 to 100 parts by weight based on 100 parts by weight of the vulcanizable rubber and further mixing the resultant mixture at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; extruding the mixture from an extruder at a temperature of not less than the melting point of the polyamide, but not more than 270° C.; and drawing an extrudate at a temperature of less than the melting point of the polyamide.
Claim 8
Dependent Claim
20 words
A process as claimed in claim 5, wherein the melting point of the polyamide is 190° C. to 235° C.
Claim 9
Dependent Claim
107 words
A process as claimed in claim 5, wherein the novolak type phenol formaldehyde resin precondensate is a precondensate having the general formula ##STR25## wherein R 1 , R 2 and R 3 are independently a hydrogen atom, or an alkyl group having 1 to 15 carbon atoms, p is 1 or 2, and q is a number of 0 to 13; or a styrenated phenol-phenol-formaldehyde resin precondensate; a p-cumylphenol-formaldehyde resin precondensate; a phenyl phenol-formaldehyde resin precondensate; a lactum-bisphenol F-formaldehyde resin precondensate; a bisphenol A-formaldehyde resin precondensate; a xylenol-formaldehyde resin precondensate; or the denatured phenol-formaldehyde resin precondensate with cashew nut shell liquid, rosin, drying oil or synthetic rubber.
Claim 10
Dependent Claim
38 words
A process as claimed in claim 5, wherein the compound capable of producing formaldehyde upon heating is used in an amount of 0.02 to 1 part by weight based on 100 parts by weight of the vulcanizable rubber.
Claim 11
Dependent Claim
15 words
A fiber-reinforced rubber composition prepared in accordance with the process of claim 1 or 5.
References Cited (Backward Citations)
US2683697A
Cited
US3226276A
Cited
US3507689A
Cited
US3715332A
Cited
US3738948A
Cited
US3853796A
Cited
US3965055A
Cited
US3888805A
Cited
US4257926A
Cited
US4219452A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-26 | 1991-04-27 | 1991-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-26 | 1995-04-27 | 1995-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-26 | 1999-04-27 | 1999-10-27 | $7700.00 | Window Closed / Lapsed |