Process of isostatic molding and bonding fluoropolymers

Claim 1

In the manufacture of a high purity bladder pump, the process of joining one end of a tubular bladder sleeve formed of PTFE with the outer surface of a cylindrical end plug formed of PTFE received in and closing an end of said sleeve, comprising the steps of: inserting said end plug within an end of said tubular sleeve for closing the end of said sleeve, inserting said plug and sleeve within a cup-shaped metallic mold which mold has an inside surface which conforms closely to the adjacent outer surface of the sleeve, heating by immersion of said mold in a molten bath to achieve fusion of said plug to said sleeve by reason of the differential cubic expansion of PTFE to said mold resulting in the formation of pressure on said plug and sleeve within said mold, removing said mold from said bath and quenching said mold with water to cause more rapid cooling of said mold than the plug and sleeve components therein, thereby maintaining said pressure thereon during at least a portion of the quench.

Claim 4

The method of forming threads on an inside surface of a tubular sleeve of PTFE material comprising the steps of: inserting a first metal mold member into the interior of said sleeve at one end thereof, said first mold member closely conforming to the inside surface of said sleeve and having threads formed on an outer surface thereof, inserting said sleeve and said first mold member into a cup-shaped second metal mold member closely conforming to the adjacent outside surface of said sleeve, with the difference in volume between said mold members and the portion of said sleeve inserted therebetween closely approximating the difference in cubic expansions of said inserted portion of said sleeve and said mold members at an elevated temperature approaching the fusion temperature of said PTFE material, heating said mold members with said sleeve therebetween in a molten salt bath to approximately said fusion temperature to cause the permanent displacement of said sleeve between said mold members into said threads of said first mold member, cooling said mold members while maintaining said pressure on said PTFE material therebetween during at least an initial portion of said cooling, and thereafter removing said second mold member and unthreading said first mold member from said sleeve to define permanent inside threads on said one end of said sleeve.

Claim 5

The method of forming threads on an inside surface of a tubular sleeve of PTFE material comprising the steps of: inserting a first metal mold member into the interior of said sleeve at one end thereof, said first mold member closely conforming to the inside surface of said sleeve and having threads formed on an outer surface thereof, inserting said sleeve and said first mold member into a cup-shaped second metal mold member closely conforming to the adjacent outside surface of said sleeve, with the difference in volume between said mold members and the portion of said sleeve inserted therebetween closely approximating the difference in cubic expansions of said inserted portion of said sleeve and said mold members at an elevated temperature approaching the fusion temperature of said PTFE material, heating said mold members with said sleeve therebetween in a molten salt bath to approximately said fusion temperature to cause the permanent displacement of said sleeve between said mold members into said threads of said first mold member, cooling said mold members while maintaining said pressure on said PTFE material therebetween during at least an initial portion of said cooling, and thereafter removing said second mold member and unthreading said first mold member from said sleeve to define permanent inside threads on said one end of said sleeve.

Claim 6

The method of reconfiguring a quantity of high density high molecular weight polymer material such as PTFE, comprising the steps of: supporting the quantity in a space between rigid metal mold members at least one of which has formed thereon a configuration different than that of said quantity, with the difference in volume between said mold members and said quantity closely approximating the difference in cubic expansion of said quantity and said members at an elevated temperature approaching or exceeding the melt temperature of said polymer, heating said quantity and said mold members together to cause said quantity to expand to said differential configuration, and cooling said quantity and said members together to maintain pressure between said quantity and members during at least an initial portion of said cooling.

Claim 7

The method of reconfiguring a quantity of high density high molecular weight polymer material such as PTFE, comprising the steps of: supporting the quantity in a space between rigid metal mold members at least one of which has formed thereon a configuration different than that of said quantity, with the difference in volume between said mold members and said quantity closely approximating the difference in cubic expansion of said quantity and said members at an elevated temperature approaching or exceeding the melt temperature of said polymer, heating said quantity and said mold members together to cause said quantity to expand to said differential configuration, and cooling said quantity and said members together to maintain pressure between said quantity and members during at least an initial portion of said cooling.