Assignee: UK Secretary of State for Defence
•
Filing: 1985-09-10
•
Granted: 1987-10-13
•
Expires: 2005-09-10
Abstract
Abstract A method of preparing a fibrous activated carbon including the steps of carbonizing and activating cellulose fibre at temperatures between 200° C. and 1000° C. in an inert atmosphere, characterized in that, prior to activation, the fibre is impregnated with an impregnating material comprising, in the form of one or more compounds, boron and at least one alkali metal.
Inventors
- 👤 Kenneth S. W. Sing
- 👤 Frederick G. R. Gimblett
- 👤 John J. Freeman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:05
CPC Classifications
B; B01; B01J; B01J21/00; B01J21/18; B01J23/00; B01J23/02; B01J23/04; C; C01; C01B; C01B32/00; C01B32/30; C01B32/312; C01B32/342; C01B32/348; C01B32/354; C01B32/382; D; D01; D01F; D01F11/00; D01F11/10; D01F11/12; D01F11/124; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/16
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
166 words
A method of preparing a fibrous activated carbon which comprises the steps of (a) carbonizing cellulose fibre in an inert atmosphere at a temperature between 200° and 600° C., and (b) activating the carbonized cellulose fibre in an inert atmosphere at a temperature between 450° and 1000° C. until the fibrous activated carbon product has a BET surface area in excess of 500 m 2 g -1 , wherein prior to step (b) the cellulose fibre is impregnated with an impregnating material consisting of the elements boron and at least one alkali metal, said elements being in the form of one or more compounds, such that after impregnation the amount of alkali metal on the fibre is from 0.01 to 10% by weight of the fibre and the amount of boron on the fiber is from 0.01 to 10% by weight of the fibre, whereby the fibrous activated carbon product of step (b) has a mesopore content of at least 15% of its total pore volume.
Claim 2
Independent Claim
166 words
A method of preparing a fibrous activated carbon which comprises the steps of (a) carbonizing cellulose fibre in an inert atmosphere at a temperature between 200° and 600° C., and (b) activating the carbonized cellulose fibre in an inert atmosphere at a temperature between 450° and 1000° C. until the fibrous activated carbon product has a BET surface area in excess of 500 m 2 g -1 , wherein prior to step (b) the cellulose fibre is impregnated with an impregnating material consisting of the elements boron and at least one alkali metal, said elements being in the form of one or more compounds, such that after impregnation the amount of alkali metal on the fibre is from 0.01 to 10% by weight of the fibre and the amount of boron on the fiber is from 0.01 to 10% by weight of the fibre, whereby the fibrous activated carbon product of step (b) has a mesopore content of at least 15% of its total pore volume.
Claim 3
Dependent Claim
24 words
A method according to claim 1 wherein the impregnating material comprises one or more compounds containing both boron and at least one alkali metal.
Claim 4
Dependent Claim
17 words
A method according to claim 2 wherein the impregnating material comprises one or more alkali metal borates.
Claim 5
Dependent Claim
37 words
A method according to claim 3 wherein the one or more alkali metal borates are selected from the group consisting of borax, sodium metaborate, sodium tetraborate, lithium metaborate, lithium pentaborate, lithium tetraborate, potassium tetraborate, and potassium metaborate.
Claim 6
Dependent Claim
23 words
A method according to claim 1 wherein the impregnating material comprises at least one boron compound and at least one alkali metal compound.
Claim 7
Dependent Claim
21 words
A method according to claim 5 wherein the at least one boron compound is selected from boric oxide and boric acid.
Claim 8
Dependent Claim
23 words
A method according to claim 5 wherein the at least one alkali metal compound comprises an alkali metal salt of a mineral acid.
Claim 9
Dependent Claim
19 words
A method according to claim 7 wherein the at least one alkali metal compound comprises an alkali metal halide.
Claim 10
Dependent Claim
42 words
A method according to claim 1 wherein the impregnating material comprises a mixture of at least one compound containing both boron and at least one alkali metal, with at least one compound selected from compounds of boron and compounds of alkali metals.
Claim 11
Dependent Claim
18 words
A method according to claim 9 wherein the impregnating material comprises a mixture of borax and boric acid.
Claim 12
Dependent Claim
14 words
A method according to claim 1 wherein the fibre is impregnated prior to carbonisation.
Claim 13
Dependent Claim
25 words
A method according to claim 1 wherein the atomic ratio of alkali metal to boron on the fibre after impregnation is from 0.1:1 to 1:0.1.
Claim 14
Dependent Claim
39 words
A method according to claim 1 wherein the impregnating material is impregnated onto the fibre by contacting the fibre with the material dissolved or suspended in a solvent, and thereafter drying the fibre to leave the material impregnated thereon.
Claim 15
Dependent Claim
33 words
A method according to claim 13 wherein the solvent is selected from the group consisting of water, methanol, ethanol, propanol, glycerol, acetone, isoamyl alcohol, ethylene glycol, mineral acids, formic acid, and diethyl ether.
Claim 16
Dependent Claim
25 words
A method according to claim 13 wherein the total concentration of boron compounds dissolved or suspended in the solvent is between 0.1% and 5% w/v.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-12 | 1991-04-13 | 1991-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-12 | 1995-04-13 | 1995-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-12 | 1999-04-13 | 1999-10-13 | $7700.00 | Window Closed / Lapsed |