Abstract

Abstract Starting mixture for an insulating composition, silk-screening ink comprising such a mixture, and the use of said ink for the manufacture of hybrid microcircuits on colaminated sustrates. The invention relates to the formulation of a starting mixture for an insulating composition, comprising a vitreous phase and several ceramic phases in the respective ratios by volume for the vitreous phase between 85 and 60% and for the ceramic phases between 15 and 40%, the vitreous phase being a silicate of zinc and alkaline earth. According to an embodiment of the invention the starting mixture is remarkable in that the vitreous phase is constituted by the molar ratios of the following oxides: 30 to 55% of silicon (SiO2), 15 to 30% of zinc oxide (ZnO), 0 to 20% of boric anhydride (B2O3), 0 to 10% of alumina (Al2O3), 15 to 40% of barium oxide (BaO), and in that the ceramic phases are constituted by the ratios by volume of the following oxides: 0 to 10% of cobalt oxide (Co3O4), 5 to 20% of zinc oxide (ZnO), and 10 to 25% of lead oxide (PbO2). Application: Manufacture of microcircuits on colaminated metallic substrates.

Inventors

  • 👤 Hugues Baudry

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-08 17:05
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/02; H01B3/12; H01B3/08; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/46; H05K3/4644; H05K3/4664; H05K3/4667; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/68; H10W70/682; H10W70/685; H10W72/00; H10W72/071; H10W72/073; H10W72/07331; H10W72/07336; H10W72/07337; H10W72/30; H10W72/351; H10W72/352; H10W72/851; H10W72/874; H10W72/884; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/931; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12597; Y10T428/12611; Y10T428/12618; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/12917; Y10T428/12951

Claims Analysis

Total Claims: 5
Claim 1
Independent Claim 149 words
An electric device comprising at least one copper-iron alloy containing 36% of nickel-copper laminate in which at least one of the exposed copper surfaces is provided with a coating of a silk-screening ink that has been deposited on the copper surface through a silk-screening screen and is then fired in a nitrogen atmosphere at a peak temperature of between 850° C. and 950° C. for at least 5 minutes, said ink being a dispersion, in an organic carrier, of a dielectric composition consisting essentially of 85%-60% by volume of a vitreous phase and 15%-40% by volume of ceramic phases, said vitreous phase having the following composition by mol.%: 30-55% SiO 2 , 15-30% ZnO, 15-40% BaO, 0-20% B 2 O 3 , and 0-10% Al 2 O 3 , and said ceramic phases consisting essentially in volume percent of: ZnO-5-20%, Co 3 O 4 -0-10% and PbO 2 -10-25%.
Claim 2
Dependent Claim 149 words
An electric device comprising at least one copper-iron alloy containing 36% of nickel-copper laminate in which at least one of the exposed copper surfaces is provided with a coating of a silk-screening ink that has been deposited on the copper surface through a silk-screening screen and is then fired in a nitrogen atmosphere at a peak temperature of between 850° C. and 950° C. for at least 5 minutes, said ink being a dispersion, in an organic carrier, of a dielectric composition consisting essentially of 85%-60% by volume of a vitreous phase and 15%-40% by volume of ceramic phases, said vitreous phase having the following composition by mol.%: 30-55% SiO 2 , 15-30% ZnO, 15-40% BaO, 0-20% B 2 O 3 , and 0-10% Al 2 O 3 , and said ceramic phases consisting essentially in volume percent of: ZnO-5-20%, Co 3 O 4 -0-10% and PbO 2 -10-25%.
Claim 3
Dependent Claim 38 words
The electric device of claim 1 wherein the vitreous phase has the following composition by mol. %: 45% SiO 2 , 20% ZnO, 5% B 2 O 3 , 5% Al 2 O 3 and 25% of BaO.
Claim 4
Dependent Claim 52 words
The electric device of claim 1 wherein the dielectric composition consists essentially of 68% by volume of the vitreous phase, a ceramic phase of ZnO in 11% by volume, a ceramic phase of Co 3 O 4 in 2% by volume and a ceramic phase of PbO 2 in 19% by volume.
Claim 5
Dependent Claim 44 words
The electric device of claim 3 wherein the molar ratios of the vitreous phase are chosen to be equal to 45% of SiO 2 , 20% of ZnO, 5% of B 2 O 3 5% of Al 2 O 3 and 25% of BaO.

References Cited (Backward Citations)

GB1489031A Cited
US4323652A Cited
US4619590A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1990-10-12 1991-04-13 1991-10-13 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1994-10-12 1995-04-13 1995-10-13 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1998-10-12 1999-04-13 1999-10-13 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag