Method of manufacturing a photographic reflecting support
Assignee: Konica Minolta Inc
•
Filing: 1986-02-10
•
Granted: 1987-10-13
•
Expires: 2006-02-10
Abstract
Abstract A method of manufacturing a photographic reflecting support wherein chips and/or resin scraps of a thermoplastic resin are heat-treated in a vacuum and fed into an extruder to be melted and then extruded in the form of a sheet out of the die of the extruder. The resulting sheet is then cooled and solidified on a cooled casting drum and stretched 6 to 16 times in terms of area, lengthwise and then widthwise or vice versa, or biaxially at the same time, at a temperature within the range of from a temperature not lower than the glass transition point of the thermoplastic resin to a temperature not higher than 150° C. The stretched sheet is then thermoset at a temperature within the range of from a temperature not lower than 170° C. to a temperature of the melting point of the thermoplastic resin and the resulting photographic reflecting support is made from 40 μm to 300 μm in thickness and not higher than 20% in visible-wave-length range transmittance.
Inventors
- 👤 Takanori Nakadate
- 👤 Kazuto Kiyohara
- 👤 Ichiya Harada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:59
CPC Classifications
B; B29; B29C; B29C55/00; B29C55/005; B29B; B29B13/00; B29B13/02; B29B17/00; G; G03; G03C; G03C1/00; G03C1/76; G03C1/795; G03C1/7954; B29K; B29K2067/00; B29K2105/00; B29K2105/06; B29K2105/16; B29K2995/00; B29K2995/0018; B29K2995/003; B29K2995/0037; B29K2995/005; B29K2995/0053; B29L; B29L2031/00; B29L2031/764; B29L2031/7644; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
219 words
A method of manufacturing a photographic reflecting support comprising: heat-treating chips and/or resin scraps composed of a thermoplastic resin mainly comprising a polyester resin and containing a white inorganic pigment in an amount of not less than 10% by weight, at a temperature of from 180° C. to 245° C. for a period of not shorter than 3 hours in a vacuum of not more than 20 mmHg; feeding said heat-treated chips and/or resin scraps into an extruder to be melted and then extruded in the form of a sheet out of the die of the extruder; cooling and solidifying the resulting sheet on a cooled casting drum; stretching said cooled and solidified sheet 6 to 16 times in terms of area. lengthwise and then widthwise or vice versa, or biaxially at the same time, at a temperature within the range of from a temperature not lower than the glass transition point of said thermoplastic resin to a temperature not higher than 150° C.; thermosetting said stretched sheet at a temperature within the range of from a temperature not lower than 170° C. to a temperature of the melting point of said thermoplastic resin; and making the resulting photographic reflecting support be from 40 μm to 300 μm in thickness and not higher than 20% in visible-wave-length range transmittance.
Claim 2
Independent Claim
219 words
A method of manufacturing a photographic reflecting support comprising: heat-treating chips and/or resin scraps composed of a thermoplastic resin mainly comprising a polyester resin and containing a white inorganic pigment in an amount of not less than 10% by weight, at a temperature of from 180° C. to 245° C. for a period of not shorter than 3 hours in a vacuum of not more than 20 mmHg; feeding said heat-treated chips and/or resin scraps into an extruder to be melted and then extruded in the form of a sheet out of the die of the extruder; cooling and solidifying the resulting sheet on a cooled casting drum; stretching said cooled and solidified sheet 6 to 16 times in terms of area. lengthwise and then widthwise or vice versa, or biaxially at the same time, at a temperature within the range of from a temperature not lower than the glass transition point of said thermoplastic resin to a temperature not higher than 150° C.; thermosetting said stretched sheet at a temperature within the range of from a temperature not lower than 170° C. to a temperature of the melting point of said thermoplastic resin; and making the resulting photographic reflecting support be from 40 μm to 300 μm in thickness and not higher than 20% in visible-wave-length range transmittance.
Claim 3
Dependent Claim
43 words
The method of manufacturing a photographic reflecting support as claimed in claim 1, wherein said temperature of said stretching is within the range of from a temperature not lower than the glass transition point of said resin to not higher than 130° C.
Claim 4
Dependent Claim
67 words
The method of manufacturing a photographic reflecting support as claimed in claim 2, wherein said polyester resin is at least one selected from the group consisting of the polymers of the condensation products of such an aromatic dicarboxylic acid as terephthalic acid, isophthalic acid. phthalic acid and naphthalene dicarboxylic acid with such a glycolic compound as ethylene glycol, 1,3-propanediol and 1,4-butanediol; said polymers including the copolymers thereof.
Claim 5
Dependent Claim
40 words
The method of manufacturing a photographic reflecting support as claimed in claim 3, wherein said polyester resin is at least one selected from the group consisting of the polymers of polyethylene terephthalate, polyethylene-2,6-dinaphthalate, polypropylene terephthalate, polybutylene terephthalate and copolymers thereof.
Claim 6
Dependent Claim
42 words
The method of manufacturing a photographic reflecting support as claimed in claim 2, wherein said polyester resin is from 0.4 to 0.8 in inherent viscosity determined at ° C. in a mixed solvent of phenol and tetrachloroethane in the weight ratio 60:40.
Claim 7
Dependent Claim
40 words
The method of manufacturing a photographic reflecting support as claimed in claim 2, wherein said white inorganic pigment is at least one selected from the group consisting of titanium oxide, barium sulfate, calcium carbonate, silica, talc, zinc sulfide and clay.
Claim 8
Dependent Claim
55 words
The method of manufacturing a photographic reflecting support as claimed in claim 2, wherein said white inorganic pigment is contained in an amount of within from not less than 10 parts by weight to not more than 30 parts by weight per 100 parts by weight in total of said pigment and said thermoplastic resin.
Claim 9
Dependent Claim
30 words
The method of manufacturing a photographic reflecting support as claimed in claim 2, wherein said chips and/or resin scraps are heat-treated for a period of from 5 to 48 hours.
Claim 10
Dependent Claim
40 words
The method of manufacturing a photographic reflecting support as claimed in claim 2, wherein said temperature in the stretching process is higher than the temperature of the glass transition point of said thermoplastic resin by not lower than 5° C.
Claim 11
Dependent Claim
28 words
The method of manufacturing a photographic reflecting support as claimed in claim 2, wherein said white inorganic pigment is not greater than 20 μm in average particle size.
References Cited (Backward Citations)
US3154461A
Cited
US3201506A
Cited
US3720732A
Cited
US3804937A
Cited
US3627625A
Cited
US3980748A
Cited
US3753661A
Cited
US3944699A
Cited
US3903234A
Cited
JPS5036461A
Cited
JPS5371162A
Cited
JPS577048A
Cited
JPS57109948A
Cited
US4409167A
Cited
US4569885A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-12 | 1991-04-13 | 1991-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-12 | 1995-04-13 | 1995-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-12 | 1999-04-13 | 1999-10-13 | $7700.00 | Window Closed / Lapsed |