US4698258A Expired / Lapsed US ⏱️ 0.0 years remaining

Surface covering product and process therefor

Assignee: Individual

•

Filing: 1986-05-22

•

Granted: 1987-10-06

•

Expires: 2006-05-22

📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A base web is prepared which has two parallel layers of nonwoven fiber glass webs, each impregnated with a solidified resinous composition and separated from each other by a core layer of an expandable solidified resinous composition which is bonded to the resinous composition used to impregnate the fiber glass webs by a thin integral layer of nonexpandable resinous composition. Additional layers of resinous material, expandable and nonexpandable, and decorative effects may be supported by the base web. The composite web is subjected to heat processing to expand the core layer and other expandable layers that may be present and to fuse the resinous composition used in the construction of the product. The processes are particularly adaptable for the production of shapes such as floor tiles and decorations that employ chemical embossing.

Inventors

👤 Joseph C. Harkins, Jr.

Bibliographic Details

Application Number —

Jurisdiction US

Data Source google_patents

Last Synchronized 2026-11-03 13:55

CPC Classifications

B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B29; B29C; B29C44/00; B29C44/20; B29C44/32; B29C44/321; B29C44/326; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B29C70/086; B32B27/00; B32B27/06; B32B27/065; B32B27/12; B32B27/30; B32B27/304; B32B5/18; B32B5/20; B32B7/00; B32B7/04; D; D06; D06N; D06N3/00; D06N3/04; D06N3/06; D06N7/00; D06N7/0005; D06N7/0039; D06N7/0047; D06N7/0049; D06N7/006; B29C59/00; B29C59/02; B29C59/04; B29K; B29K2105/00; B29K2105/04; B29K2105/06; B29K2105/08; B29K2105/0854; B29L; B29L2031/00; B29L2031/10; B29L2031/104; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/04; B32B2260/046; B32B2262/00; B32B2262/10; B32B2262/101; B32B2266/00; B32B2266/02; B32B2266/0214; B32B2266/0221; B32B2266/0235; B32B2327/00; B32B2327/06; B32B2419/00; B32B2419/04; B32B2607/00; B32B2607/02; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1023; Y10T156/1039; Y10T156/1041; Y10T156/1043; Y10T156/1052; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24496; Y10T428/24504; Y10T428/249921; Y10T428/249953; Y10T428/249981; Y10T428/249982; Y10T428/249985; Y10T428/249987; Y10T428/24999; Y10T428/249991; Y10T428/249992; Y10T442/00; Y10T442/60; Y10T442/608; Y10T442/647; Y10T442/651; Y10T442/652; Y10T442/674

Claims Analysis

Total Claims: 38

Claim 1

Independent Claim 78 words

A base web for a surface covering product comprising two substantially parallel fiber glass webs each of which is impregnated with a resinous composition and spaced apart from the other by a core layer of expandable resinous composition and an integral layer of resinous composition positioned on each side of the core layer which separates the surfaces of the core layer from the impregnated fiber glass webs and adheres the impregnated fiber glass webs to the core layer.

Claim 2

Dependent Claim 78 words

Claim 3

Dependent Claim 77 words

A base web in accordance with claim 1 in which the fiber glass webs are comprised of randomly placed glass fibers having a length of between 0.75 and 1.5 inches, a diameter of between 10 and 13 microns and which are bound together by a binding material selected from the group of synthetic resins consisting of acrylic resins, polyvinyl resins, and ureaformaldehyde resins in an amount from to 12% to 25% by weight of the glass fibers.

Claim 4

Dependent Claim 21 words

A base web in accordance with claim 1 in which the resinous compositions are based on the resinous material polyvinyl chloride.

Claim 5

Dependent Claim 47 words

A base web in accordance with claim 2 in which the resinous compositions are based on the resinous material polyvinyl chloride and the core layer has a thickness from 0.010 inches to 0.030 inches and a blow ratio of from 1.2 to 1 to 4 to 1.

Claim 6

Dependent Claim 39 words

A base web in accordance with claim 4 in which the core layer contains a blowing system capable of expanding the core layer during exposure to heat which is sufficient to fuse the resinous compositions in the base web.

Claim 7

Dependent Claim 19 words

A base web in accordance with claim 5 in which the core layer contains azodicarbonamide and an accelerator therefor.

Claim 8

Dependent Claim 66 words

A surface covering product comprising: (a) a base web in accordance with claim 1 in which the resinous compositions in the base web are fused and the core layer is expanded and fused; (b) a layer of expanded and fused resinous composition adhered to the base web; (c) a layer of fused resinous composition adhered to the top surface of the composite of (a) and (b).

Claim 9

Dependent Claim 89 words

A surface covering product comprising: (a) a base web in accordance with claim 4 in which the resinous compositions in the base web are fused and the core layer is expanded and fused; (b) a multilevel layer of an expanded, fused resinous composition adhered to the base web having a first portion which is expanded to a greater thickness than a second portion; (c) decorative areas on the surface of the multilevel layer; (d) a layer of a translucent or clear fused resinous composition adhered to the multilevel layer.

Claim 10

Dependent Claim 22 words

A surface covering product in accordance with claim 8 in which the resinous compositions are based on the resinous material polyvinyl chloride.

Claim 11

Dependent Claim 24 words

A surface covering product in accordance with claim 9 in which the multilevel layer contains thermal decomposition products of azodicarbonamide and an accelerator therefor.

Claim 12

Dependent Claim 45 words

A surface covering product in accordance with claim 10 in which the second portion of the multilevel layer has been in contact with an expansion inhibitor which caused the second portion to expand to a lesser thickness than the first portion of the multilevel layer.

Claim 13

Dependent Claim 26 words

A surface covering product in accordance with claim 11 in which the inhibitor is selected from the group consisting of fumaric acid, trimellitic anhydride and tolyltriazole.

Claim 14

Dependent Claim 15 words

A surface covering product in accordance with claim 12 in which the inhibitor is tolyltriazole.

Claim 15

Dependent Claim 25 words

A surface covering product in accordance with claim 9 which contains a smoothing layer of resinous composition between the base web and the multilevel layer.

Claim 16

Dependent Claim 163 words

A process for producing a base web for a surface covering product which comprises: (a) impregnating a first fiber glass web with a resinous composition and gelling the resinous composition; (b) applying a first barrier coat of resinous composition to one surface of the impregnated first fiber glass web and gelling the first barrier coat; (c) applying a layer of expandable resinous compostion to the surface of the gelled first barrier coat and gelling the expandable resinous composition; (d) applying a second barrier coat of resinous composition in a liquid state to the top surface of the gelled expandable resinous composition; (e) impregnating a second fiber glass web with a resinous composition and gelling the resinous composition; (f) placing the impregnated second fiber glass web into intimate contact with the second barrier coat while in the liquid state, and gelling the second barrier coat to adhere the impregnated second fiber glass web to the composite web produced by the steps (a) through (d).

Claim 17

Dependent Claim 163 words

Claim 18

Dependent Claim 84 words

A process for producing a base web for a surface covering product in accordance with claim 15 in which steps (e) and (f) are performed by placing the second fiber glass web into intimate contact with the second barrier coat while in the liquid state so that the composition of the second barrier layer impregnates the second fiber glass web and forms an integral layer between the gelled expandable resinous layer and the impregnated second fiber glass layer and gelling the liquid resinous composition.

Claim 19

Dependent Claim 120 words

A process in accordance with claim 15 or 16 in which the first and the second fiber glass webs are comprised of randomly placed glass fibers having a length of between 0.75 and 1.5 inches, a diameter of between 10 and 13 microns and which are bound together by a binding material selected from the group of synthetic resins consisting of acrylic resins, polyvinyl resins, and ureaformaldehyde resins in an amount from to 12% to 25% by weight of the glass fibers, having a total weight ranging from 1 ounce per square yard to 1.77 ounces per square yard, and are positioned so that the machine direction of the first and second fiber glass webs are parallel to each other.

Claim 20

Dependent Claim 20 words

A process in accordance with claim 17 in which the resinous compositions are based on the resinous material polyvinyl chloride.

Claim 21

Dependent Claim 19 words

A process in accordance with claim 18 in which the expandable resinous composition contains azodicarbonamide and an accelerator therefor.

Claim 22

Dependent Claim 78 words

A process in accordance with claim 18 in which the steps (a) and (b) are performed by coating one surface of the first fiber glass web with a resinous composition in a liquid state, said composition having a viscosity that allows the composition to penetrate through at least a portion of the first fiber glass web while leaving sufficient composition on the surface of the web to form an integral layer when the liquid resinous composition is gelled.

Claim 23

Dependent Claim 68 words

A process in accordance with claim 20 in which the resinous composition applied to one surface of the first fiber glass web penetrates at least 80% of the thickness of the fiber glass web while maintaining the other surface of the first fiber glass web sufficiently dry to permit passage of the impregnated web over transport rollers with substantially no transfer of resinous material to the transport rollers.

Claim 24

Dependent Claim 58 words

A process in accordance with claim 20 in which gelling of a composite resinous composition impregnated fiber glass web and barrier coat is performed by placing the surface of the barrier coat of the composite web into a heated smooth surface and delivering sufficient heat from the smooth surface to the composite web to gel the resinous compositions.

Claim 25

Dependent Claim 144 words

A process in accordance with claim 18 in which the steps (a) and (b) are preformed by positioning the fiber glass web in a body of resinous composition in a liquid state so as to cause the liquid resinous composition to occupy the interstices of the fiber glass web and then removing the fiber glass web from the body of resinous composition along with the resinous compostion contained in the intersticies of the web and the resinous composion that accompanies the web on the surfaces thereof and then removing excess resinous composition from the surfaces of the web and placing one side of the impregnated web on a heated smooth surface to form the first barrier layer and delivering sufficient heat from the smooth surface to gel the resinous composition comprising the impregnant of the first fiber glass web and the first barrier coat.

Claim 26

Dependent Claim 83 words

A process in accordance with claim 15 or 16 which comprises the additional steps: (g) applying a second expandable layer of resinous composition on the surface of the second resinous impregnated fiber glass web; (h) gelling the second expandable resinous composition; (i) applying a top surface of resinous composition; (j) exposing the composite web produced by steps (a) through (i) to uniform heating conditions to fuse each layer thereof containing a resinous composition and to expand each layer thereof containing a blowing system.

Claim 27

Dependent Claim 19 words

A process in accordance with claim 24 in which the resinous compositions are based on the resin polyvinyl chloride.

Claim 28

Dependent Claim 22 words

A process in accordance with claim 25 in which the expandable layers contain a blowing system comprising azodicarbonamide and an accelerator therefor.

Claim 29

Dependent Claim 26 words

A process in accordance with claim 25 in which areas of decoration are placed on the composite web produced after step (f) and before step (j).

Claim 30

Dependent Claim 24 words

A process in accordance with claim 26 in which areas of decoration are placed on the gelled second expandable layer formed by step (h).

Claim 31

Dependent Claim 95 words

A process in accordance with claim 27 in which a portion of the areas of decoration contains an expansion inhibitor which penetrates into the composition of the second expandable layer during the uniform heating that causes expansion and fusion of the second expandable layer, said expansion inhibitor altering the amount of expansion of the second expandable layer that takes place in the portion of the areas of decoration containing the expansion inhibitor in contrast with the amount of expansion that takes place in the remaining portions of the areas of decoration containing no expansion inhibitor.

Claim 32

Dependent Claim 25 words

A process in accordance with claim 29 in which the expansion inhibitor is selected from the group consisting of fumaric acid, trimellitic anhydride and tolytriazole.

Claim 33

Dependent Claim 14 words

A process in accordance with claim 30 in which the expansion inhibitor is tolyltriazole.

Claim 34

Dependent Claim 50 words

A process in accordance with claim 29 which comprises the additional steps of: (k) applying a layer of adhesive to the bottom side of the composite web produced by steps (a) through (j); and, (l) applying a means to protect the adhesive during a period of storage prior to use.

Claim 35

Dependent Claim 29 words

A process in accordance with claim 29 which comprises the additional step: (m) cutting the composite web produced by steps (a) through (j) into a plurality of individual pieces.

Claim 36

Dependent Claim 18 words

A process in accordance with claim 32 in which the protective means of step (1) comprises release paper.

Claim 37

Dependent Claim 36 words

A process in accordance with claim 28 which comprises the additional step: (n) applying a smoothing layer of resinous material between the resinous impregnated second fiber glass web and the second expandable layer of resinous composition.

Claim 38

Dependent Claim 23 words

A process in accordance with claim 35 in which the resinous composition of step (n) is based on the resinous material polyvinyl chloride.

References Cited (Backward Citations)

US2920977A Cited

FR1307239A Cited

FR1315226A Cited

US3293108A Cited

US3293094A Cited

US4138521A Cited

US4100006A Cited

US4128688A Cited

US4388363A Cited

US4283456A Cited

US4349597A Cited

US4510201A Cited

US4454188A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1990-10-05	1991-04-06	1991-10-06	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1994-10-05	1995-04-06	1995-10-06	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1998-10-05	1999-04-06	1999-10-06	$7700.00	Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag

Select Category

Notes (Optional)