US4690990A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polymerization process using a catalyst comprising a phosphate and with a bis-(cyclopentadienyl)chromium(II) compound
Assignee: Phillips Petroleum Co
•
Filing: 1982-09-24
•
Granted: 1987-09-01
•
Expires: 2002-09-24
Abstract
Abstract In accordance with one embodiment of this invention, a bis-(cyclopentadienyl)chromium(II) compound is introduced onto an activated phosphate-containing support and utilized in conjunction with an organometal cocatalyst, such as an alkylaluminum. In accordance with another embodiment of this invention, a phosphate-containing xerogel is formed by removing water from an aluminum phosphate-containing hydrogel by means of azeotropic distillation or washing with a volatile, water miscible organic compound, activated and thereafter a bis-(cyclopentadienyl)chromium(II) compound is incorporated therewith. In other embodiments of this invention, a phosphate-containing support is formed by forming aluminum phosphate from an aluminum alkoxide or from a melt, or by phosphating silica or alumina, or by forming an aluminum phosphate/silica combination. A support thus formed is activated and a bis-(cyclopentadienyl)chromium(II) compound added. Alternatively in all embodiments, the chromium and phosphate components can be added separately. The resulting catalysts are capable of giving narrow molecular weight distribution polymer because of the inherent high molecular weight of the polymer produced, and the unusual sensitivity to hydrogen, a broad spectrum of polymers can be produced so far as molecular weight is concerned. The catalyst is ideally suited for forming olefin polymers such as ethylene and ethylene copolymers in a slurry system.
Inventors
- 👤 Max P. McDaniel
- 👤 James N. Short
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 00:12
CPC Classifications
C; C08; C08F; C08F10/00; C08F4/00; C08F4/42; C08F4/44; C08F4/60; C08F4/62; C08F4/639; C08F4/63904; C08F4/63912; C08F4/63916
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
48 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system comprising: (a) a catalyst comprising a bis-(cyclopentadienyl)chromium(II) compound and a phosphate-containing support; (b) an organometal cocatalyst; and recovering a polymer.
Claim 2
Dependent Claim
48 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system comprising: (a) a catalyst comprising a bis-(cyclopentadienyl)chromium(II) compound and a phosphate-containing support; (b) an organometal cocatalyst; and recovering a polymer.
Claim 3
Dependent Claim
29 words
A process according to claim 1 wherein said one mono-1-olefin is selected from ethylene, propylene, 1-butene, 1-pentene, 1-hexene and 1-octene, and said polymerization is carried out under slurry conditions.
Claim 4
Dependent Claim
23 words
A process according to claim 1 wherein said one mono-1-olefin comprises ethylene and said polymerization conditions include a temperature of below 205° F.
Claim 5
Dependent Claim
31 words
A method according to claim 1 wherein ethylene polymer having 0.2 to 3 mole percent comonomer incorporation is produced by incorporating 0.5 to 20 mole percent comonomer in an ethylene feed.
Claim 6
Dependent Claim
30 words
A process according to claim 1 wherein said at least one mono-1-olefin olefin includes ethylene and 0.5 to 20 mole percent of one of propylene, 1-butene, 1-pentene, 1-hexene, or 1-octene.
Claim 7
Dependent Claim
22 words
A method according to claim 1 wherein said support and said bis-(cyclopentadienyl)chromium compound are introduced into said reaction zone as separate streams.
Claim 8
Dependent Claim
100 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system comprising: combining an aqueous solution of an aluminum salt with a source of phosphate ions and neutralizing with a base to give a hydrogel; converting said hydrogel to a xerogel by one of azeotropic distillation or washing with a water miscible organic compound, activating by heating in an oxygen-containing ambient at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 9
Dependent Claim
100 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system comprising: combining an aqueous solution of an aluminum salt with a source of phosphate ions and neutralizing with a base to give a hydrogel; converting said hydrogel to a xerogel by one of azeotropic distillation or washing with a water miscible organic compound, activating by heating in an oxygen-containing ambient at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 10
Dependent Claim
26 words
A process according to claim 7 wherein said at least one mono-1-olefin is at least predominantly ethylene and said polymerization is carried out under slurry conditions.
Claim 11
Dependent Claim
78 words
A polymerization process comprising contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: combining an aluminum alkoxide with phosphoric acid to give a hydrogel; converting said hydrogel to a xerogel, activating the resulting xerogel by heating at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 12
Dependent Claim
78 words
A polymerization process comprising contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: combining an aluminum alkoxide with phosphoric acid to give a hydrogel; converting said hydrogel to a xerogel, activating the resulting xerogel by heating at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 13
Dependent Claim
26 words
A process according to claim 9 wherein said at least one mono-1-olefin is at least predominantly ethylene and said polymerization is carried out under slurry conditions.
Claim 14
Dependent Claim
85 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: combining a source of phosphate ions with a melt of an aluminum salt; neutralizing to give a hydrogel; converting said hydrogel to a xerogel, activating the resulting xerogel by heating to a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 15
Dependent Claim
85 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: combining a source of phosphate ions with a melt of an aluminum salt; neutralizing to give a hydrogel; converting said hydrogel to a xerogel, activating the resulting xerogel by heating to a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 16
Dependent Claim
26 words
A process according to claim 11 wherein said at least one mono-1-olefin is at least predominantly ethylene and said polymerization is carried out under slurry conditions.
Claim 17
Dependent Claim
24 words
A method according to claim 11 wherein said xerogel after activation and said bis-(cyclopentadienyl)chromium(II) compound are introduced into said reaction zone as separate streams.
Claim 18
Dependent Claim
22 words
A method according to claim 11 wherein said olefin comprises ethylene and said polymerization conditions include a temperature of below 205° F.
Claim 19
Dependent Claim
88 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: treating a silica-containing material with a phosphating agent selected from phosphate ions and vaporized phosphorus compounds so as to give 0.001 to 0.2 gram atoms of phosphorus per mole of silica; activating the resulting treated silica at a temperature of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 20
Dependent Claim
88 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: treating a silica-containing material with a phosphating agent selected from phosphate ions and vaporized phosphorus compounds so as to give 0.001 to 0.2 gram atoms of phosphorus per mole of silica; activating the resulting treated silica at a temperature of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 21
Dependent Claim
79 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: cogelling silica and aluminum phosphate to form a hydrogel; removing water from said hydrogel to form a xerogel, activating the resulting xerogel by heating at a temperature within the range of 150°-1000° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 22
Dependent Claim
79 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: cogelling silica and aluminum phosphate to form a hydrogel; removing water from said hydrogel to form a xerogel, activating the resulting xerogel by heating at a temperature within the range of 150°-1000° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 23
Dependent Claim
27 words
A polymerization process according to claim 16 wherein said at least one mono-1-olefin is at least predominantly ethylene and said polymerization is carried out under slurry conditions.
Claim 24
Dependent Claim
93 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: impregnating silica with aluminum phosphate by combining a source of aluminum ions and phosphate ions with a slurry of silica in a diluent; thereafter forming said aluminum phosphate by evaporating the diluent, activating the thus-impregnated silica by heating at a temperature within the range of 150°-1000° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer
Claim 25
Dependent Claim
93 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: impregnating silica with aluminum phosphate by combining a source of aluminum ions and phosphate ions with a slurry of silica in a diluent; thereafter forming said aluminum phosphate by evaporating the diluent, activating the thus-impregnated silica by heating at a temperature within the range of 150°-1000° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer
Claim 26
Dependent Claim
91 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: impregnating a silica xerogel with boron phosphate by adding a source of boron ions and a source of phosphate ions to a slurry of silica xerogel in a diluent; thereafter evaporating the diluent, activating the thus-impregnated silica by heating at a temperature of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 27
Dependent Claim
91 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: impregnating a silica xerogel with boron phosphate by adding a source of boron ions and a source of phosphate ions to a slurry of silica xerogel in a diluent; thereafter evaporating the diluent, activating the thus-impregnated silica by heating at a temperature of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 28
Dependent Claim
73 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a method comprising: precipitating aluminum phosphate in the presence of silica-alumina; activating the resulting xerogel by heating in an oxygencontaining ambient at a temperature within the range of 150°-1000° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 29
Dependent Claim
73 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a method comprising: precipitating aluminum phosphate in the presence of silica-alumina; activating the resulting xerogel by heating in an oxygencontaining ambient at a temperature within the range of 150°-1000° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 30
Dependent Claim
111 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: activating a silica-alumina xerogel by heating in an oxygen-containing ambient at a temperature within the range of 150°-1000° C., activating an aluminum phosphate xerogel by heating in an oxygen-containing ambient at a temperature within the range of 150°-800° C.; thereafter combining a bis-(cyclopentadienyl)chromium(II) compound with said thus activated silica and said thus activated aluminum phosphate, said silica and aluminum phosphate either being physically mixed prior to said activation or combined subsequent to said activation; and recovering a polymer.
Claim 31
Dependent Claim
111 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: activating a silica-alumina xerogel by heating in an oxygen-containing ambient at a temperature within the range of 150°-1000° C., activating an aluminum phosphate xerogel by heating in an oxygen-containing ambient at a temperature within the range of 150°-800° C.; thereafter combining a bis-(cyclopentadienyl)chromium(II) compound with said thus activated silica and said thus activated aluminum phosphate, said silica and aluminum phosphate either being physically mixed prior to said activation or combined subsequent to said activation; and recovering a polymer.
Claim 32
Dependent Claim
101 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: phosphating an alumina-containing composition by treating same with a phosphating agent selected from (1) phosphate ions and (2) vaporous phosphorus compounds to give a surface composition having a 0.2:1 to 1:1 P/Al atom ratio; activating said thus phosphated alumina composition by heating in an oxygen-containing ambient at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 33
Dependent Claim
101 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: phosphating an alumina-containing composition by treating same with a phosphating agent selected from (1) phosphate ions and (2) vaporous phosphorus compounds to give a surface composition having a 0.2:1 to 1:1 P/Al atom ratio; activating said thus phosphated alumina composition by heating in an oxygen-containing ambient at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 34
Dependent Claim
26 words
A process according to claim 22 wherein said at least one mono-1-olefin is at least predominantly ethylene and said polymerization is carried out under slurry conditions.
Claim 35
Dependent Claim
80 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: forming an aluminum phosphate hydrogel, contacting said hydrogel to a xerogel by azeotropic distillation or washing with a water miscible organic liquid; activating by heating at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
Claim 36
Dependent Claim
80 words
A polymerization process comprising: contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule in a reaction zone under polymerization conditions with a catalyst system produced by a process comprising: forming an aluminum phosphate hydrogel, contacting said hydrogel to a xerogel by azeotropic distillation or washing with a water miscible organic liquid; activating by heating at a temperature within the range of 150°-800° C.; thereafter combining with a bis-(cyclopentadienyl)-chromium(II) compound under anhydrous conditions; and recovering a polymer.
References Cited (Backward Citations)
US3013002A
Cited
US3342750A
Cited
US3453219A
Cited
US3794628A
Cited
US3709853A
Cited
US3757002A
Cited
US3806500A
Cited
US4101445A
Cited
US4219444A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-31 | 1991-03-02 | 1991-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-31 | 1995-03-02 | 1995-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-31 | 1999-03-02 | 1999-09-01 | $7700.00 | Window Closed / Lapsed |