Welding apparatus method for depositing wear surfacing material and a substrate having a weld bead thereon
Assignee: Technology Holding Co II
•
Filing: 1985-12-18
•
Granted: 1987-08-25
•
Expires: 2005-12-18
Abstract
Abstract The welding method may be used to lay down weld beads on metallic substrates with a narrow width of 0.125 inch and less. The process employs a plasma transferred arc and pulses the current delivered to the arc such that a wave form having at least a main amplitude and a lower auxiliary amplitude is provided. The powdered metal which is delivered is laid down in a series of overlapping weld deposits which solidify very rapidly and produce a fine grain structure.
Inventors
- 👤 Gary C. Shubert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:31
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/32; B23K35/327; B23K9/00; B23K9/04
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
125 words
A method of forming a wear surface on a metallic workpiece, said method comprising the steps of establishing a transferred direct current electric arc between a non-consumable electrode and a narrow surface of a workpiece; forming a plasma plume of inert gas in the arc; feeding a flow of powdered metal into the plasma plume while moving the electrode along the workpiece for depositing the powdered metal along the narrow surface of the workpiece to form a weld deposit; and pulsing a welding current to the electrode and workpiece between a main current level and a lower non-zero auxiliary current level during movement of the electrode along the workpiece to effect a series of sequentially overlapping weld deposits along the narrow surface of the workpiece.
Claim 2
Independent Claim
125 words
A method of forming a wear surface on a metallic workpiece, said method comprising the steps of establishing a transferred direct current electric arc between a non-consumable electrode and a narrow surface of a workpiece; forming a plasma plume of inert gas in the arc; feeding a flow of powdered metal into the plasma plume while moving the electrode along the workpiece for depositing the powdered metal along the narrow surface of the workpiece to form a weld deposit; and pulsing a welding current to the electrode and workpiece between a main current level and a lower non-zero auxiliary current level during movement of the electrode along the workpiece to effect a series of sequentially overlapping weld deposits along the narrow surface of the workpiece.
Claim 3
Dependent Claim
19 words
A method as set forth in claim 1 wherein the series of overlapping weld deposits form a bead deposit.
Claim 4
Dependent Claim
26 words
A method as set forth in claim 2 wherein the bead deposit has a thickness of from 0.010 inch to 0.125 inch for a single pass.
Claim 5
Dependent Claim
22 words
A method as set forth in claim 2 wherein the bead deposit has a width of from 0.020 inch to 0.125 inch.
Claim 6
Dependent Claim
31 words
A method as set forth in claim 2 wherein the bead deposit has a width relative to the width of the narrow surface of the workpiece of from 1:1 to 1:2.
Claim 7
Dependent Claim
30 words
A method as set forth in claim 2 wherein the bead deposit has a ratio of bead height to bead width of from 0.5:1 to 2:1 for a single pass.
Claim 8
Dependent Claim
38 words
A method as set forth in claim 1 wherein said main current level is in the range of from 20 to 70 amps and said auxiliary current level is in the range of from 4 to 15 amps.
Claim 9
Dependent Claim
40 words
A method as set forth in claim 7 wherein said main current level is pulsed for a time of from 0.3 to 0.6 seconds and said auxiliary current level is pulsed for a time of from 1 to 1.4 seconds.
Claim 10
Dependent Claim
18 words
A method as set forth in claim 1 wherein said auxiliary current level is 1 to 2 amps.
Claim 11
Dependent Claim
40 words
A method as set forth in claim 1 wherein said main current level is pulsed for a time of from 0.1 seconds or less and said auxiliary current level is pulsed for a time of from 3 or more seconds.
Claim 12
Independent Claim
137 words
A method of forming an overlay on a narrow surface of a width not greater than 0.125 inch of a metallic workpiece, said method comprising the steps of establishing a transferred direct current electric arc between a non-consumable electrode and the narrow surface of the metal piecework; forming a plasma plume of inert gas in the arc; feeding a flow of powdered metal into the plasma plume while moving the electrode along the piecework for depositing the powdered metal along the narrow surface of the workpiece to form a weld deposit; and pulsing a welding current to the electrode and workpiece between a main current level and a lower non-zero auxiliary current level during movement of the electrode along the workpiece to effect a series of sequentially overlapping weld deposits along the narrow surface of the workpiece.
Claim 13
Independent Claim
137 words
A method of forming an overlay on a narrow surface of a width not greater than 0.125 inch of a metallic workpiece, said method comprising the steps of establishing a transferred direct current electric arc between a non-consumable electrode and the narrow surface of the metal piecework; forming a plasma plume of inert gas in the arc; feeding a flow of powdered metal into the plasma plume while moving the electrode along the piecework for depositing the powdered metal along the narrow surface of the workpiece to form a weld deposit; and pulsing a welding current to the electrode and workpiece between a main current level and a lower non-zero auxiliary current level during movement of the electrode along the workpiece to effect a series of sequentially overlapping weld deposits along the narrow surface of the workpiece.
Claim 14
Dependent Claim
38 words
A method as set forth in claim 11 wherein said main current level is in the range of from 20 to 70 amps and said auxiliary current level is in the range of from 4 to 15 amps.
Claim 15
Dependent Claim
40 words
A method as set forth in claim 12 wherein said main current level is pulsed for a time of from 0.3 to 0.6 seconds and said auxiliary current level is pulsed for a time of from 1 to 1.4 seconds.
Claim 16
Dependent Claim
34 words
A method as set forth in claim 13 wherein the weld deposits form a bead deposit with a ratio of bead height to bead width of from 0.5:1 to 2:1 for a single pass.
Claim 17
Dependent Claim
19 words
A method as set forth in claim 11 wherein said auxiliary current level is about 1 to 2 amps.
Claim 18
Dependent Claim
36 words
A method as set forth in claim 11 wherein said auxiliary current level is pulsed for a time of from 3 or more seconds and said main current level is pulsed from 0.1 seconds or less.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-24 | 1991-02-23 | 1991-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-24 | 1995-02-23 | 1995-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-24 | 1999-02-23 | 1999-08-25 | $7700.00 | Window Closed / Lapsed |