Polyurethane elastomers prepared in a two-step process using mixtures of chain extenders
Assignee: Dow Chemical Co
•
Filing: 1985-12-10
•
Granted: 1987-08-25
•
Expires: 2005-12-10
Abstract
Abstract This invention is a process for preparing polyurethane and/or polyurea elastomer comprising reacting a liquid, preformed isocyanate-terminated prepolymer, which prepolymer is the reaction product of a stoichiometric excess of a polyisocyanate and a relatively high equivalent weight isocyanate-reactive compound, with a chain extender mixture, which chain extender mixture comprises (a) a mixture comprising a hydroxyl-terminated chain extender and an aromatic amine terminated chain extender, and/or an aliphatic amine-terminated compound, or (b) a mixture comprising an aromatic amine-terminated chain extender and an aliphatic amine-terminated compound, wherein the isocyanate index is from about 70 to about 200. In this process, it is possible to prepare elastomers having excellent properties, particularly excellent flexural and thermal properties, which properties are difficult to obtain in a one-step process.
Inventors
- 👤 Richard D. Peffley
- 👤 John H. Spells
- 👤 James A. Vanderhider
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:19
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G2120/00
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
144 words
A two-step process for preparing a polyurethane and/or polyurea elastomer comprising reacting, in a reaction injection molding process, a preformed, liquid, isocyanate-terminated prepolymer, which prepolymer is the reaction product of a stoichiometric excess of a polyisocyanate and a relatively high equivalent weight isocyanate-reactive compound, with a chain extender mixture, which chain extender mixture comprises (a) a mixture comprising a hydroxyl-terminated chain extender having an equivalent weight of about 31 to about 150 and an aromatic amine terminated chain extender and/or an aliphatic amine-terminated compound, or (b) a mixture comprising an aromatic amine-terminated chain extender and an aliphatic amine-terminated compound, wherein the isocyanate index is from about 70 to about 200, wherein said chain extender mixture contains fewer than about 0.5 equivalent of a relatively high equivalent weight isocyanate-reactive compound per equivalent of relatively high equivalent weight isocyanate reactive compound used in preparing said prepolymer.
Claim 2
Dependent Claim
144 words
A two-step process for preparing a polyurethane and/or polyurea elastomer comprising reacting, in a reaction injection molding process, a preformed, liquid, isocyanate-terminated prepolymer, which prepolymer is the reaction product of a stoichiometric excess of a polyisocyanate and a relatively high equivalent weight isocyanate-reactive compound, with a chain extender mixture, which chain extender mixture comprises (a) a mixture comprising a hydroxyl-terminated chain extender having an equivalent weight of about 31 to about 150 and an aromatic amine terminated chain extender and/or an aliphatic amine-terminated compound, or (b) a mixture comprising an aromatic amine-terminated chain extender and an aliphatic amine-terminated compound, wherein the isocyanate index is from about 70 to about 200, wherein said chain extender mixture contains fewer than about 0.5 equivalent of a relatively high equivalent weight isocyanate-reactive compound per equivalent of relatively high equivalent weight isocyanate reactive compound used in preparing said prepolymer.
Claim 3
Dependent Claim
17 words
The process of claim 1 wherein said prepolymer has an equivalent weight from about 200 to 525.
Claim 4
Dependent Claim
24 words
The process of claim 2 wherein said chain extender mixture comprises a mixture of a hydroxyl-terminated chain extender and a stearically hindered aromatic diamine.
Claim 5
Dependent Claim
29 words
The process of claim 3 wherein said hydroxyl-terminated chain extender comprises about 25-75 percent of the combined weight of the hydroxyl terminated chain extender and the amine-terminated chain extender.
Claim 6
Dependent Claim
23 words
The process of claim 4 wherein said chain extender mixture comprises a mixture of ethylene glycol, propylene glycol or 1,4-butane diol and diethyltoluenediamine.
Claim 7
Dependent Claim
39 words
The process of claim 2 wherein said chain extender mixture comprises a mixture of an amine-terminated polyether having about 2-3 amine groups per molecule and an equivalent weight of about 100 to 2000, and a stearically hindered aromatic diamine.
Claim 8
Dependent Claim
26 words
The process of claim 5 wherein said chain extender mixture contains about 0.01 to about 0.5 equivalent of the amine-terminated polyether per equivalent of aromatic diamine.
Claim 9
Dependent Claim
24 words
The process of claim 7 wherein said stearically hindered aromatic diamine is diethyltoluenediamine and the amine-terminated polyether has an equivalent weight of about 150-300.
Claim 10
Dependent Claim
39 words
The process of claim 2 wherein said chain extender mixture comprises a mixture of an amine-terminated polyether having about 2-3 amine groups per molecule and an equivalent weight of about 100 to about 2000, and a hydroxyl-terminated chain extender.
Claim 11
Dependent Claim
25 words
The process of claim 9 wherein said chain extender mixture contains about 0.01 to about 0.5 equivalent of amine-terminated polyether per equivalent of aromatic diamine.
Claim 12
Dependent Claim
37 words
The process of claim 4, 7, or 10 wherein said prepolymer is the reaction product of a reaction mixture comprising an aromatic diisocyanate and a polyether polyol having an equivalent weight from about 700 to about 2500.
Claim 13
Dependent Claim
37 words
The process of claim 4, 7, or 10 wherein said prepolymer is the reaction product of a reaction mixture comprising an aromatic diisocyanate and an amine-terminated polyether having an equivalent weight from about 700 to about 2500.
Claim 14
Dependent Claim
17 words
The process of claim 4, 7, or 10 wherein said prepolymer is prepared from an aliphatic diisocyanate.
Claim 15
Dependent Claim
16 words
The process of claim 2 wherein the isocyanate index is from about 100 to about 115.
Claim 16
Dependent Claim
26 words
The process of claim 14 wherein the elastomer has an unfilled flexural modulus of at least about 150,000 psi at a density of about 1.15 g/cc.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-24 | 1991-02-23 | 1991-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-24 | 1995-02-23 | 1995-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-24 | 1999-02-23 | 1999-08-25 | $7700.00 | Window Closed / Lapsed |