Cross-linked polymer coated metal particle filler compositions
Assignee: Siemens AG
•
Filing: 1985-11-06
•
Granted: 1987-08-25
•
Expires: 2005-11-06
Abstract
Abstract A filler composition composed of metal particles present in the tightest possible packing which are individually coated with a cross-linked polymer layer is provided which has high thermal conductivity and high electrical insulation capacity. Such filler composition is usefull as an addition to resins employed in injection molding and extrusion. A high resistance to abrasion is achieved by the cross-linked coating layers (22,24). A filing degree of about 90 Vol. % is achievable with such a filler composition, and such displays a breakdown voltage greater than about 100 V.
Inventors
- 👤 Ferdinand Quella
- 👤 Ulrich Leute
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:56
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/02; C08K3/08; C08K9/00; C08K9/08; C08K9/10; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2998
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
110 words
A method of making a filler composition having high thermal conductivity and high electrical insulatiabiltiy for use in injection moldable or extrudable plastic formulations comprising the steps of: (a) dispersing metal particles either in a non-aqueous medium or in water containing an emulsifier, (b) adding to the resulting dispersion a composition to be cross-linked in a concentration of 0.1 through 5% by weight based upon total dispersion weight, and further adding any agents necessary to produce a cross-linked polymer, (c) executing a cross-linking polymerization about said so dispersed metal particles, and (d) separating the resulting cross-linked polymer coated metal particles in a medium which does not dissolve such coated polymer.
Claim 2
Independent Claim
110 words
A method of making a filler composition having high thermal conductivity and high electrical insulatiabiltiy for use in injection moldable or extrudable plastic formulations comprising the steps of: (a) dispersing metal particles either in a non-aqueous medium or in water containing an emulsifier, (b) adding to the resulting dispersion a composition to be cross-linked in a concentration of 0.1 through 5% by weight based upon total dispersion weight, and further adding any agents necessary to produce a cross-linked polymer, (c) executing a cross-linking polymerization about said so dispersed metal particles, and (d) separating the resulting cross-linked polymer coated metal particles in a medium which does not dissolve such coated polymer.
Claim 3
Dependent Claim
159 words
The method of claim 1, wherein said metal particles comprise aluminum particles having a surface oxide layer and wherein said composition to be cross-linked comprises radically-polymerizable monomers with cross-linking adjuvants, and: (a) a mono-molecular, hydrophobic layer is applied to said aluminum particles in their surface oxidized condition by treatment thereof with, a chlorosilane in organic solvent; (b) the resulting particles (1,2,4) are dispersed in water containing an emulsifier; (c) a radically-polymerizable monomer selected from the group consisting of styrene, vinyl acetate, acrylonitrile and mixtures thereof, together with a cross-linking monomer selected from the group consisting of divinyl benzene triallyl cyanurate, and mixtures thereof are added to the said water, thereby to produce an emulsion; (d) said emulsion is heated to about 60° C. and an initiator is added thereto which is selected from the group consisting of benzoyl peroxide, azobisisobutyronitrile and mixtures thereof, and (e) the resulting cross-link polymer coated aluminum grains are precipitated in water and separated off.
Claim 4
Dependent Claim
21 words
The method of claim 2, wherein a cationic surfactant, a nonionic surfactant, or an anionic surfactant is employed as said emulsifier.
Claim 5
Dependent Claim
20 words
The method of claim 2 wherein a redox system containing sodium dithionite/potassium peroxo-di-sulfate is employed in place of said initiator.
Claim 6
Dependent Claim
72 words
The method of claim 1, wherein said metal particles comprise surface oxidized iron particles and said composition to be cross-linked comprises a polyphenylenesulfide, and: (a) the oxidized iron particles are suspended in a high-boiling organic liquid medium which is a solvent for low-molecular weight polyphenylenesulfide, and said iron particles are suspended therein with rapid agitation; (b) said polyphenylenesulfide is then added to the resulting suspension; (c) a cross-linking polymerization is executed at
Claim 7
Dependent Claim
9 words
about 280° C. over a timespan extending up to
Claim 8
Dependent Claim
9 words
about 280° C. over a timespan extending up to
Claim 9
Dependent Claim
20 words
about 8 hours, and (d) the resulting cross-linked polymer coated iron particles are separated from said liquid medium after settling.
Claim 10
Dependent Claim
20 words
about 8 hours, and (d) the resulting cross-linked polymer coated iron particles are separated from said liquid medium after settling.
Claim 11
Dependent Claim
23 words
The method of claim 5, wherein residual solvent is eliminated by brief suspension of said resulting cross-linked polymer coated iron particles in methanol.
Claim 12
Dependent Claim
22 words
The method of claim 5, wherein said liquid medium is selected from the group consisting of benzyl benzoate, diphenyl ether, and chloronaphthalene.
Claim 13
Dependent Claim
82 words
The method of claim 1, wherein said metal particles have their surfaces oxidized and wherein said composition to be cross-linked comprises unsaturated polyester resin, and: (a) said oxidized metal particles are suspended with rapid agitation in dimethyl-formamide which contains dissolved therein said unsaturated polyester resin, (b) an accelerator is added in dissolved form into such suspension dropwise, and (c) a cross-linking polymerization is executed with constant agitation over a timespan of about 2 hours with slow heating up to about 80° C.
Claim 14
Dependent Claim
39 words
The method of claim 8, wherein said oxidized metal particles are comprised of a metal selected from the group consisting of cobalt, and copper, and said acceleration comprises a 5% by weight solution of benzoyl peroxide in phthalic acid
Claim 15
Dependent Claim
82 words
The method of claim 1, wherein said metal particles have their surfaces oxidized and wherein said composition to be cross-linked comprises an epoxy resin, and: (a) said oxidized metal particles are suspended in a high-boiling, non-aqueous carrier liquid; (b) said epoxy resin and an accelerator which is preferably an amine complex with a metal ion, are added to such suspension; and (c) a cross-linking polymerization is executed within about 8 hours at a temperature ranging from about 80° C. to 120° C.
Claim 16
Dependent Claim
27 words
The method of claim 10, wherein said oxidized metal particles are composed of copper, and wherein said amine complex comprises a solution of ethylene diamine in xylol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-24 | 1991-02-23 | 1991-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-24 | 1995-02-23 | 1995-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-24 | 1999-02-23 | 1999-08-25 | $7700.00 | Window Closed / Lapsed |