Process for the production of a metallic denture
Assignee: Evonik Operations GmbH
•
Filing: 1986-04-04
•
Granted: 1987-08-25
•
Expires: 2006-04-04
Abstract
Abstract A denture with a metallic microstructure and with low shrinkage and porosity is produced by metallurgical sintering by providing a multimodal size distribution of coarse and fine fractions of metal powder, optionally also with glass or ceramic powder, converting this powder mixture with water into a slip, modelling the denture with this, and sintering the slip at a temperature which exceeds the solidus temperature of at least one component of the powder mixture.
Inventors
- 👤 Werner Groll
- 👤 Josef Rothaut
- 👤 Angela Klaus
- 👤 Rudi Steinke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:47
CPC Classifications
A; A61; A61C; A61C13/00; A61C13/0003; A61K; A61K6/00; A61K6/80; A61K6/84; A61K6/844; B; B22; B22F; B22F1/00; B22F1/05; B22F1/052; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49567; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12056
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
158 words
In a process for the production of a denture, optionally veneered with ceramic or plastic, having a metallic microstructure, using sintering technology, from a mixture of metal powders, optionally together with glass or ceramic powders which mixture is treated with a mixing fluid to form a spreadable mass with which the denture is modelled on a ceramic model of the prepared tooth which is used as bat and then sintered comprising employing a metal powder mixture having a multimodal size distribution of coarse and fine fractions in which the particle size of the coarsest fraction does not exceed 100 microns; converting this powder mixture with water to a slip sintering the slip and selecting the sintering temperature of the slip mass such that it exceeds the solidus temperature of at least one component of the powder mixture and in the case of planned veneering with ceramic exceeds the baking-on temperature of the ceramic by at least 50° C.
Claim 2
Dependent Claim
158 words
In a process for the production of a denture, optionally veneered with ceramic or plastic, having a metallic microstructure, using sintering technology, from a mixture of metal powders, optionally together with glass or ceramic powders which mixture is treated with a mixing fluid to form a spreadable mass with which the denture is modelled on a ceramic model of the prepared tooth which is used as bat and then sintered comprising employing a metal powder mixture having a multimodal size distribution of coarse and fine fractions in which the particle size of the coarsest fraction does not exceed 100 microns; converting this powder mixture with water to a slip sintering the slip and selecting the sintering temperature of the slip mass such that it exceeds the solidus temperature of at least one component of the powder mixture and in the case of planned veneering with ceramic exceeds the baking-on temperature of the ceramic by at least 50° C.
Claim 3
Dependent Claim
16 words
A process according to claim 1 wherein the denture is veneered with a ceramic or plastic.
Claim 4
Dependent Claim
14 words
A process according to claim 1 wherein the powder mixture consists of metal powder.
Claim 5
Dependent Claim
26 words
A process according to claim 1 wherein the powder mixture in addition to metal powder contains a minor amount by weight of glass or ceramic powder.
Claim 6
Dependent Claim
52 words
A process according to claim 1 wherein th coarse fraction has a particle size between 30 and 100 microns and is of spherical shape and the fine fraction has a particle size below 50 microns and is of any shape, the percent by volume of the coarse fraction being 30 to 90%.
Claim 7
Dependent Claim
27 words
A process according to claim 5 comprising adding the powder component having a solidus temperature below the sintering temperature of the slip composition as a fine fraction.
Claim 8
Dependent Claim
27 words
A process according to claim 1 comprising adding the powder component having a solidus temperature below the sintering temperature of the slip composition as a fine fraction.
Claim 9
Dependent Claim
53 words
A process according to claim 7 wherein the slip composition contains powders of a plurality of metals and the sintering temperature lies in the range between T solidus minus 200° C. and T solidus of the sintered metal but is also above the solidus temperature of a least one of the powder components.
Claim 10
Dependent Claim
53 words
A process according to claim 6 wherein the slip composition contains powders of a plurality of metals and the sintering temperature lies in the range between T solidus minus 200° C. and T solidus of the sintered metal but is also above the solidus temperature of at least one of the powder components.
Claim 11
Dependent Claim
53 words
A process according to claim 5 wherein the slip composition contains powders of a plurality of metals and the sintering temperature lies in the range between T solidus minus 200° C. and T solidus of the sintered metal but is also above the solidus temperature of at least one of the powder components.
Claim 12
Dependent Claim
53 words
A process according to claim 1 wherein the slip composition contains powders of a plurality of metals and the sintering temperature lies in the range between T solidus minus 200° C. and T solidus of the sintered metal but is also above the solidus temperature of at least one of the powder components.
Claim 13
Dependent Claim
30 words
A process according to claim 7 wherein the slip composition contains powders of only one alloy and sintering temperature lies between the solidus and liquidus temperature of the sintered metal.
Claim 14
Dependent Claim
30 words
A process according to claim 6 wherein the slip composition contains powders of only one alloy and sintering temperature lies between the solidus and liquidus temperature of the sintered metal.
Claim 15
Dependent Claim
30 words
A process according to claim 5 wherein the slip composition contains powder of only one alloy and sintering temperature lies between the solidus and liquidus temperature of the sintered metal.
Claim 16
Dependent Claim
29 words
A process according to claim 1 wherein the slip composition contains powders of only one alloy and sintering temperature lies between the solidus and liquidus temperature of sintered metal.
Claim 17
Dependent Claim
32 words
A process according to claim 13 comprising sintering a low melting metal or a low melting alloy for finishing a surface and closing pores onto the surface of the sintered slip composition.
Claim 18
Dependent Claim
31 words
A process according to claim 9 comprising sintering a low melting metal or low melting alloy for finishing a surface and closing pores onto the surface of the sintered slip composition.
Claim 19
Dependent Claim
32 words
A process according to claim 1 comprising sintering a low melting metal or a low melting alloy for finishing a surface and closing pores onto the surface of the sintered slip composition.
Claim 20
Dependent Claim
31 words
A process according to claim 17 comprising applying a layer consisting essentially of a material which burns without residue to the model used as a bat according to shrinkage during sintering.
Claim 21
Dependent Claim
31 words
A process according to claim 13 comprising applying a layer consisting essentially of a material which burns without residue to the model used as a bat according to shrinkage during sintering.
Claim 22
Dependent Claim
31 words
A process according to claim 1 comprising applying a layer consisting essentially of a material which burns without residue to the model used as a bat according to shrinkage during sintering.
Claim 23
Dependent Claim
12 words
A process according to claim 1 wherein the metal is an alloy.
References Cited (Backward Citations)
US29093A
Cited
DE1915977A1
Cited
US3933961A
Cited
USRE29093E
Cited
US4431449A
Cited
US4277283A
Cited
US4434211A
Cited
EP0104320A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-24 | 1991-02-23 | 1991-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-24 | 1995-02-23 | 1995-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-24 | 1999-02-23 | 1999-08-25 | $7700.00 | Window Closed / Lapsed |