Optical waveguide glass fiber flame processing
Assignee: Nokia Bell Labs
•
Filing: 1986-02-14
•
Granted: 1987-08-25
•
Expires: 2006-02-14
Abstract
Abstract In the interest of reducing the effect on tensile strength of flame processing of a silica-based optical fiber waveguide, such processing is by a method in which a significant flow of oxygen surrounds a flame produced by combustion of hydrogen, deuterium, ammonia, or deuterated ammonia. Flame processing may be for purposes such as, e.g., fiber drawing, fiber fusing for the sake of lateral coupling, refractive index modification by the diffusion of dopants, and fiber splicing in the manufacture of long lengths of fiber. Even though there is no use of chlorine, at least 80 percent of spliced fibers have a tensile strength greater than or equal to 500 kpsi (3.45 GPa) as is desirable in optical fiber cable manufacture.
Inventors
- 👤 John T. Krause
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 01:14
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/24; G02B6/255; G02B6/2551; C; C03; C03B; C03B23/00; C03B23/04; C03B23/043; C03B23/20; C03B23/207; C03B37/00; C03B37/01; C03B37/02; C03B37/025; C03B37/027; C03B37/02736; C03B37/10; C03B37/14; C03B37/15; C03B2205/00; C03B2205/30; C03B2205/60; C03B2205/62; C03B2205/68
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
145 words
Method for making at least one silica-based optical waveguide glass fiber having a dopant-induced core-cladding waveguiding structure, said method comprising a step of heat processing at least a portion of at least one silica-based optical waveguide glass fiber segment, heat processing being by means of a flame which results upon combustion in a flow of gases, said flow comprising a first flow portion and a second flow portion surrounding said first flow portion, said first flow portion comprising a significant amount of one or several combustible gases selected from the group consisting of hydrogen, deuterium, ammonia, and deuterated ammonia, said second flow portion comprising a significant amount of oxygen, said method being characterized in that no appreciable amounts of chlorine are present in said flow and said second flow portion having volume and velocity significantly in excess of volume and velocity as required for combustion.
Claim 2
Dependent Claim
145 words
Method for making at least one silica-based optical waveguide glass fiber having a dopant-induced core-cladding waveguiding structure, said method comprising a step of heat processing at least a portion of at least one silica-based optical waveguide glass fiber segment, heat processing being by means of a flame which results upon combustion in a flow of gases, said flow comprising a first flow portion and a second flow portion surrounding said first flow portion, said first flow portion comprising a significant amount of one or several combustible gases selected from the group consisting of hydrogen, deuterium, ammonia, and deuterated ammonia, said second flow portion comprising a significant amount of oxygen, said method being characterized in that no appreciable amounts of chlorine are present in said flow and said second flow portion having volume and velocity significantly in excess of volume and velocity as required for combustion.
Claim 3
Dependent Claim
62 words
Method of claim 1 in which a second silica-based optical waveguide glass fiber segment is aligned with and abutted to said first silica-based optical waveguide glass fiber segment, heating being of abutting end portions of said segments and for a duration which is sufficient to heat-fuse said segments, thereby producing said silica-based optical waveguide fiber as a spliced fiber from said segments.
Claim 4
Dependent Claim
49 words
Method of claim 2 in which said at least one silica-based optical waveguide fiber is a significant plurality of silica-based optical waveguide glass fibers, at least 80 percent of the fibers of said plurality having a tensile strength which is greater than or equal to 500 kpsi (3.45 GPa).
Claim 5
Dependent Claim
15 words
Method of claim 3 in which said plurality is assembled into an optical waveguide cable.
Claim 6
Dependent Claim
54 words
Method of claim 1 in which a second silica-based optical waveguide glass fiber segment is in at least partial lateral contact with said first silica-based optical waveguide glass fiber segment, heating being of a portion along which said segments are in lateral contact and for a duration which is sufficient to heat-fuse said segments.
Claim 7
Dependent Claim
13 words
Method of claim 1 in which said segment is being drawn during heating.
Claim 8
Dependent Claim
29 words
Method of claim 1 in which said segment is being heated for a duration which is sufficient to result in a significant change of dopant distribution in said portion.
Claim 9
Dependent Claim
23 words
Method of claim 1 in in which the material of said segment comprises silica in an amount of at least 90 mole percent.
Claim 10
Dependent Claim
22 words
Method of claim 1 in which the surface material of said segment comprises silica in an amount of at least 95 percent.
Claim 11
Dependent Claim
44 words
Method of claim 1 in which said second flow portion has a velocity in the range of from 0.3 to 10 m/sec in a region which adjoins said flame and which has a radial thickness which is greater than or equal to 0.1 mm.
Claim 12
Dependent Claim
20 words
Method of claim 1 in which said flame has a size in the range of from 0.5 to 10 mm.
Claim 13
Dependent Claim
23 words
Method of claim 1 in which said first flow portion comprises at least 50 volume percent of said one or several combustible gases.
Claim 14
Dependent Claim
17 words
Method of claim 1 in which said second flow portion comprises at least 50 volume percent oxygen.
Claim 15
Dependent Claim
29 words
Method of claim 1 in which flame heating produces a temperature at the surface of said portion in the range of from 1200 degrees C. to 2200 degrees C.
References Cited (Backward Citations)
US3825319A
Cited
US4217027A
Cited
US4217027B1
Cited
EP0025585A1
Cited
US4326870A
Cited
US4439221A
Cited
JPS5792533A
Cited
US4557557A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-24 | 1991-02-23 | 1991-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-24 | 1995-02-23 | 1995-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-24 | 1999-02-23 | 1999-08-25 | $7700.00 | Window Closed / Lapsed |