Zirconium pyrophosphate matrix layer for electrolyte in a fuel cell
Assignee: FUELCELL Corp OF AMERICA
•
Filing: 1985-07-26
•
Granted: 1987-08-18
•
Expires: 2005-07-26
Abstract
Abstract A fuel cell is made, where a porous electrolyte retaining matrix layer, containing acid electrolyte, is disposed between a pair of spaced apart gas diffusion electrodes; where the matrix contains ZrP 2 O 7 and binder, with no more than about a 10 wt. % total of the matrix containing non-binder material reactive with acid electrolyte.
Inventors
- 👤 Norman Michael
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 03:01
CPC Classifications
H; H01; H01M; H01M8/00; H01M8/02; H01M8/0289; H01M8/0293; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
51 words
A fuel cell comprising: (a) a pair of spaced apart electrodes; (b) a porous electrolyte retaining matrix layer disposed between the electrodes, said matrix layer comprising particles of a zirconium compound, wherein the zirconium compound consists essentially of ZrP 2 O 7 ; and (c) electrolyte contained within the matrix layer.
Claim 2
Dependent Claim
51 words
A fuel cell comprising: (a) a pair of spaced apart electrodes; (b) a porous electrolyte retaining matrix layer disposed between the electrodes, said matrix layer comprising particles of a zirconium compound, wherein the zirconium compound consists essentially of ZrP 2 O 7 ; and (c) electrolyte contained within the matrix layer.
Claim 3
Dependent Claim
20 words
The fuel cell of claim 1, wherein the matrix layer also contains binder, and the electrolyte is an acid electrolyte.
Claim 4
Dependent Claim
32 words
The fuel cell of claim 2, wherein the binder is a fluorocarbon, the electrolyte is phosphoric acid, and the matrix layer contains no more than about 5 wt.% of ZrO 2 .
Claim 5
Dependent Claim
65 words
A fuel cell comprising: (a) a pair of spaced apart gas diffusion electrodes; (b) a porous electrolyte retaining matrix layer disposed between the electrodes, said matrix layer comprising ZrP 2 O 7 particles and binder, with no more than about a 10 wt.% total of the matrix layer containing non-binder material substantially reactive with acid electrolyte; and (c) acid electrolyte contained within the matrix layer.
Claim 6
Dependent Claim
65 words
A fuel cell comprising: (a) a pair of spaced apart gas diffusion electrodes; (b) a porous electrolyte retaining matrix layer disposed between the electrodes, said matrix layer comprising ZrP 2 O 7 particles and binder, with no more than about a 10 wt.% total of the matrix layer containing non-binder material substantially reactive with acid electrolyte; and (c) acid electrolyte contained within the matrix layer.
Claim 7
Dependent Claim
30 words
The fuel cell of claim 4, where the matrix layer contains no more than about 10 wt.% total of ZrO 2 +zirconium orthophosphate+silicate materials and contacts at least one electrode.
Claim 8
Dependent Claim
40 words
The fuel cell of claim 4, where the matrix layer contains a fluorocarbon binder, and any non-binder material present reactive with acid electrolyte, is reactive at the fuel cell operating temperature of from about 175° C. to about 225° C.
Claim 9
Dependent Claim
41 words
The fuel cell of claim 4, where the matrix layer comprises the entire matrix and consists essentially of from about 93 wt.% to about 98 wt.% ZrP 2 O 7 and from about 2 wt.% to about 7 wt.% fluorocarbon binder.
Claim 10
Dependent Claim
26 words
The fuel cell of claim 7, where the matrix contains no more than a 1 wt.% total of ZrO 2 plus zirconium orthophosphate plus silicate materials.
Claim 11
Dependent Claim
12 words
The fuel cell of claim 4, where the acid is phosphoric acid.
Claim 12
Dependent Claim
36 words
The fuel cell of claim 4, where the ZrP 2 O 7 of the matrix is in the form of discrete particles having a particle size range of from about 2 micron to about 25 microns.
Claim 13
Dependent Claim
47 words
In a fuel cell comprising a plurality of electrodes having at least one electrolyte retaining matrix layer disposed between said electrodes, wherein the improvement comprises a matrix layer comprising particles of ZrP 2 O 7 , with no more than about 5 wt.% of ZrO 2 .
Claim 14
Dependent Claim
47 words
In a fuel cell comprising a plurality of electrodes having at least one electrolyte retaining matrix layer disposed between said electrodes, wherein the improvement comprises a matrix layer comprising particles of ZrP 2 O 7 , with no more than about 5 wt.% of ZrO 2 .
Claim 15
Dependent Claim
60 words
The fuel cell of claim 11, where fluorocarbon binder is included in the matrix layer, the electrolyte is phosphoric acid, the matrix layer contains no more than about a 10 wt.% total of ZrO 2 +zirconium orthophosphate+silicate materials, and the particles of ZrP 2 O 7 have a particle size range of from about 2 microns to about 25 microns.
Claim 16
Dependent Claim
74 words
A gas diffusion electrode having disposed thereon a porous, refractory type matrix layer capable of containing electrolyte, said matrix layer comprising discrete, sintered ZrP 2 O 7 particles having a particle size range of from about 2 microns to about 25 microns, and from about 2 wt.% to about 7 wt.% of acid resistant polymer binder, with no more than about a 10 wt.% total of ZrO 2 plus zirconium orthophosphate plus silicate materials.
Claim 17
Dependent Claim
74 words
A gas diffusion electrode having disposed thereon a porous, refractory type matrix layer capable of containing electrolyte, said matrix layer comprising discrete, sintered ZrP 2 O 7 particles having a particle size range of from about 2 microns to about 25 microns, and from about 2 wt.% to about 7 wt.% of acid resistant polymer binder, with no more than about a 10 wt.% total of ZrO 2 plus zirconium orthophosphate plus silicate materials.
Claim 18
Dependent Claim
47 words
The matrix layer of claim 13, where the matrix layer is 40% to 60% porous, comprises the entire matrix and consists essentially of from about 93 wt.% to about 98 wt.% ZrP 2 O 7 and from about 2 wt.% to about 7 wt.% fluorocarbon polymer binder.
Claim 19
Dependent Claim
22 words
The matrix layer of claim 14, containing less than a 1 wt.% total of ZrO 2 plus zirconium orthophosphate, plus silicate materials.
Claim 20
Dependent Claim
71 words
A matrix, capable of containing acid electrolyte and suitable for use in a fuel cell, comprising discrete, sintered particles of a zirconium compound, wherein the zirconium compound consists essentially of ZrP 2 O 7 particles having a particle size of from about 2 microns to about 25 microns, and from about 2 wt.% to about 7 wt.% of acid resistant polymer binder, where the matrix is from 40% to 60% porous.
Claim 21
Dependent Claim
71 words
A matrix, capable of containing acid electrolyte and suitable for use in a fuel cell, comprising discrete, sintered particles of a zirconium compound, wherein the zirconium compound consists essentially of ZrP 2 O 7 particles having a particle size of from about 2 microns to about 25 microns, and from about 2 wt.% to about 7 wt.% of acid resistant polymer binder, where the matrix is from 40% to 60% porous.
Claim 22
Dependent Claim
28 words
The matrix of claim 16 containing fluorocarbon binder, with no more than about a 10 wt.% total of the matrix containing non-binder material substantially reactive with acid electrolyte.
Claim 23
Dependent Claim
29 words
The matrix of claim 16, where the binder is a fluorocarbon and the matrix contains no more than about a 10 wt.% total of ZrO 2 +zirconium orthophosphate+silicate materials.
Claim 24
Dependent Claim
10 words
The matrix of claim 16, supported by a substrate material.
Claim 25
Dependent Claim
60 words
A matrix, capable of containing electrolyte and suitable for use in a fuel cell, comprising discrete, sintered particles of ZrP 2 O 7 having a particle size of from about 2 microns to about 25 microns, and from about 2 wt.% to about 7 wt.% of fluorocarbon polymer binder, with no more than about 5 wt.% of ZrO 2 .
Claim 26
Dependent Claim
60 words
A matrix, capable of containing electrolyte and suitable for use in a fuel cell, comprising discrete, sintered particles of ZrP 2 O 7 having a particle size of from about 2 microns to about 25 microns, and from about 2 wt.% to about 7 wt.% of fluorocarbon polymer binder, with no more than about 5 wt.% of ZrO 2 .
Claim 27
Dependent Claim
19 words
The matrix of claim 20, supported by a substrate material, where the matrix is from 40% to 60% porous.
References Cited (Backward Citations)
US2770749A
Cited
US3462314A
Cited
US3453149A
Cited
US4059679A
Cited
US3931056A
Cited
US3975308A
Cited
US3941715A
Cited
US4017664A
Cited
US4276355A
Cited
US4493879A
Cited
US4529671A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-17 | 1991-02-16 | 1991-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-17 | 1995-02-16 | 1995-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-17 | 1999-02-16 | 1999-08-18 | $7700.00 | Window Closed / Lapsed |