Method of processing high purity low-OH vitreous silica fibers
Assignee: Individual
•
Filing: 1986-04-21
•
Granted: 1987-08-11
•
Expires: 2006-04-21
Abstract
Abstract A method of achieving long-term stability in the transmission properties of high purity low-hydroxyl vitreous silica optical waveguide fibers having preexisting peroxy linkages disposed therein in which the peroxy linkages are exposed to deuterium molecules and the reaction between the deuterium molecules and the peroxy linkages to form deuteroxyl group is substantially enhanced by simultaneously or sequentially exposing the permeated fibers to a light source having an intensity of at least 10 Lambert Units and a wave length of from the short wave length absorption edge of vitreous silica up to about 650 nanometers until the absorption at 1.7 micrometers reaches saturation.
Inventors
- 👤 Friedemann Freund
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:45
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/62; C03C25/6206; C03C25/622; C03B; C03B37/00; C03B37/10; C03B37/14; C03C25/60; C03C25/607; G; G02; G02B; G02B6/00; G02B6/02; Y; Y10; Y10S; Y10S65/00; Y10S65/90
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
136 words
A method of substantially eliminating peroxy linkages from high purity vitreous silica optical waveguide fibers having such linkages disposed therein to produce a waveguide fiber having enhanced stability in its transmission properties in the wavelength region of 1.0 to 1.7 micrometers, said method comprising exposing said vitreous silica optical waveguide fibers to deuterium molecules for a time sufficient to permeate said fibers with deuterium molecules and thereafter exposing said fibers to a high intensity light source having a wavelength of from the short wavelength absorption edge of vitreous silica up to about 650 nanometers and an intensity of at least 10 Lamberts to activate the peroxy linkages therein and react substantially all of said peroxy linkages with deuterium molecules to create deuteroxyl groups within said fibers and to provide a maximum absorption loss at 1.7 micrometers.
Claim 2
Independent Claim
136 words
A method of substantially eliminating peroxy linkages from high purity vitreous silica optical waveguide fibers having such linkages disposed therein to produce a waveguide fiber having enhanced stability in its transmission properties in the wavelength region of 1.0 to 1.7 micrometers, said method comprising exposing said vitreous silica optical waveguide fibers to deuterium molecules for a time sufficient to permeate said fibers with deuterium molecules and thereafter exposing said fibers to a high intensity light source having a wavelength of from the short wavelength absorption edge of vitreous silica up to about 650 nanometers and an intensity of at least 10 Lamberts to activate the peroxy linkages therein and react substantially all of said peroxy linkages with deuterium molecules to create deuteroxyl groups within said fibers and to provide a maximum absorption loss at 1.7 micrometers.
Claim 3
Independent Claim
136 words
A method of substantially eliminating peroxy linkages from high purity vitreous silica optical waveguide fibers having such linkages disposed therein to produce a waveguide fiber having enhanced stability in its transmission properties in the wavelength region of 1.0 to 1.7 micrometers, said method comprising exposing said vitreous silica optical waveguide fibers to deuterium molecules for a time sufficient to permeate said fibers with deuterium molecules and simultaneously exposing said fibers to a high intensity light source having a wavelength of from the short wavelength absorption edge of vitreous silica up to about 650 nanometers and an intensity of at least 10 Lamberts to activate the peroxy linkages therein and react substantially all of said peroxy linkages with deuterium molecules to create deuteroxyl groups within said fibers and to provide a maximum absorption loss at 1.7 micrometers.
Claim 4
Independent Claim
136 words
A method of substantially eliminating peroxy linkages from high purity vitreous silica optical waveguide fibers having such linkages disposed therein to produce a waveguide fiber having enhanced stability in its transmission properties in the wavelength region of 1.0 to 1.7 micrometers, said method comprising exposing said vitreous silica optical waveguide fibers to deuterium molecules for a time sufficient to permeate said fibers with deuterium molecules and simultaneously exposing said fibers to a high intensity light source having a wavelength of from the short wavelength absorption edge of vitreous silica up to about 650 nanometers and an intensity of at least 10 Lamberts to activate the peroxy linkages therein and react substantially all of said peroxy linkages with deuterium molecules to create deuteroxyl groups within said fibers and to provide a maximum absorption loss at 1.7 micrometers.
Claim 5
Dependent Claim
28 words
A method according to claim 1 in which said optical waveguide fibers are bundled and placed into a sealed vessel before exposing said fibers to said deuterium molecules.
Claim 6
Dependent Claim
34 words
A method according to claim 3 in which the pressure of the deuterium gas in said vessel is about 1 barometer and the temperature therein is beneath the degradation temperature of specific fiber configuration.
Claim 7
Dependent Claim
28 words
A method according to claim 2 in which said optical waveguide fibers are bundled and placed into a sealed vessel before exposing said fibers to said deuterium molecules.
Claim 8
Dependent Claim
42 words
A method according to claim 5 in which the pressure of the deuterium gas in said vessel is about 1 barometer and the temperature therein is no higher than that which can be tolerated by the fiber bundle without degradation or deformation.
Claim 9
Dependent Claim
23 words
A method according to claim 1 in which said fibers are exposed to said light source along the longitudinal axis of said fibers.
Claim 10
Dependent Claim
23 words
A method according to claim 2 in which said fibers are exposed to said light source along the longitudinal axis of said fibers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |