Abstract A method is disclosed for laser welding two sheets of metal, the metal being of the type having associated gases tending to be trapped and expand in the weld zone during welding due to heat from the laser. These expanded gases tend to separate the upper and lower portions of the weld zone and/or expand through the weld zone toward the laser beam to create porosity in the final weld. Such metal may be coated, such as galvanized steel, in which case the zinc vaporizes into a gas in the weld zone between the adjacent sheets, or it may be poorly fitting sheets, in which case air is trapped in surface irregularities between the sheets. In either case, the method adds to the standard laser beam a surrounding stream of pressurized shield gas effective to create a pressure at the surface of the weld zone sufficient to force the molten metal of the two sheets together and force the expanded associated gases out of the weld zone in a direction away from the laser beam, whereby a non-porous weld may be created. The pressure is higher than that of shield gas in the prior art used for protection from oxygen or dispersal of plasma. Specific pressure ranges are disclosed for argon and helium.
A method of laser welding two sheets of metal galvanized with a coating of zinc, the zinc coating being subject to vaporization in the weld zone at the adjacent surfaces of the sheets into a gas by the heat of the laser and tending to expand through the weld zone, the method comprising the following steps: placing the sheets of metal with coated surfaces adjacent in position for welding; directing a laser beam at one of the sheets of metal to create a weld zone of molten metal extending through the one sheet of metal and at least into the other sheet of metal, the heat of the laser beam tending to vaporize the zinc coating into an expanding gas in the weld zone at the adjacent surfaces of the sheets, the expanding gases tending to prevent joining of the molten metal at the adjacent surfaces of the sheets and migrate through the weld zone toward the laser beam to create porosity in the final weld; directing a stream of pressurized shield gas at the weld zone, the stream surrounding and being parallel to the laser beam and creating pressure on the surface of the weld zone, the pressure on the surface of the weld zone being sufficient to force the molten metal of the two sheets together and force the expanded gas out of the weld zone in a direction away from the laser beam, whereby a non-porous weld may be created.
Claim 2
Independent Claim
243 words
A method of laser welding two sheets of metal galvanized with a coating of zinc, the zinc coating being subject to vaporization in the weld zone at the adjacent surfaces of the sheets into a gas by the heat of the laser and tending to expand through the weld zone, the method comprising the following steps: placing the sheets of metal with coated surfaces adjacent in position for welding; directing a laser beam at one of the sheets of metal to create a weld zone of molten metal extending through the one sheet of metal and at least into the other sheet of metal, the heat of the laser beam tending to vaporize the zinc coating into an expanding gas in the weld zone at the adjacent surfaces of the sheets, the expanding gases tending to prevent joining of the molten metal at the adjacent surfaces of the sheets and migrate through the weld zone toward the laser beam to create porosity in the final weld; directing a stream of pressurized shield gas at the weld zone, the stream surrounding and being parallel to the laser beam and creating pressure on the surface of the weld zone, the pressure on the surface of the weld zone being sufficient to force the molten metal of the two sheets together and force the expanded gas out of the weld zone in a direction away from the laser beam, whereby a non-porous weld may be created.
Claim 3
Dependent Claim
28 words
The method of claim 1 in which the shield gas is helium and the pressure at the weld surface is in the range of 1.35 to 6.35 torr.
Claim 4
Dependent Claim
29 words
The method of claim 1 in which the shield gas is argon and the pressure at the weld surface is in the range of 12.3 to 18. 0 torr.