Matting lacquer, paint and light-transmitting matte film
Assignee: Individual
•
Filing: 1986-07-30
•
Granted: 1987-08-04
•
Expires: 2006-07-30
Abstract
Abstract The sprayable matting lacquer is preferably applied to a transparent or translucent polymeric base film to provide the composite film with desired non-streaking matte properties so that such film becomes suitable for use by artists and the like. The matting lacquer includes a plastic resin film-forming agent, a soft matting agent formed of discrete uniformly spherical, smooth-surfaced polyolefin, preferably polyethylene particles having an average diameter not in excess of about 40 microns and preferably 10-40 microns and in a ratio of 1-3:3-1 to the resin, a relatively hard matting agent composed of particles of silica, calcium carbonate or the like, in a concentration of about 10% that of the soft matting agent, an organic solvent for the film-former and a plasticizer. The aqueous paint which is utilizable on the matted film includes the described soft matting agent, a resinous film-forming binder and dispersing agent, as well as a transparent coloring agent. This composition without the coloring agent can be used as a diluent for the paint.
Inventors
- 👤 Charles P. Collier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 11:31
CPC Classifications
C; C09; C09D; C09D123/00; C09D123/02; C09D7/00; C09D7/40; C09D7/42
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
98 words
An improved sprayable matting lacquer providing, when set on a substrate, a paint-receptive surface, said lacquer comprising: (a) a film-forming plastic resin agent; (b) a relatively soft matting agent comprising a plurality of discrete substantially uniformly spherical, smooth-surfaced fingernail-depressible non-elastomeric polyethylene particles; (c) a relatively hard matting agent comprising a plurality of discrete particles of an average diameter approximately comparable to that of said polyethylene particles and particles sufficiently hard to prevent fingernail indentation of a dried film when formed from said lacquer; (d) an organic solvent for said film-forming agent; and, (e) plasticizer for said film-forming agent.
Claim 2
Dependent Claim
98 words
An improved sprayable matting lacquer providing, when set on a substrate, a paint-receptive surface, said lacquer comprising: (a) a film-forming plastic resin agent; (b) a relatively soft matting agent comprising a plurality of discrete substantially uniformly spherical, smooth-surfaced fingernail-depressible non-elastomeric polyethylene particles; (c) a relatively hard matting agent comprising a plurality of discrete particles of an average diameter approximately comparable to that of said polyethylene particles and particles sufficiently hard to prevent fingernail indentation of a dried film when formed from said lacquer; (d) an organic solvent for said film-forming agent; and, (e) plasticizer for said film-forming agent.
Claim 3
Dependent Claim
35 words
The improved lacquer of claim 1 wherein said soft matting agent particles have an average diameter not in excess of about 40 microns and wherein said hard particles are of about the same average diameter.
Claim 4
Dependent Claim
37 words
The improved lacquer of claim 2 wherein the ratio, by weight, of said film forming agent to said soft matting agent is about 1-3:3-1 and wherein said average soft matting agent particle diameter is about 10-40 microns.
Claim 5
Dependent Claim
37 words
The improved lacquer of claim 2 wherein said film-forming agent is present in a concentration sufficient to hold said matting agent particles securely in the resulting dried film but insufficient to cover said soft matting agent particles.
Claim 6
Dependent Claim
25 words
The improved lacquer of claim 1 wherein said hard matting agent is in a ratio, by weight, to said soft matting agent of about 1:10.
Claim 7
Dependent Claim
20 words
The improved lacquer of claim 5 wherein said hard matting agent comprises at least one of silica and calcium carbonate.
Claim 8
Dependent Claim
38 words
The improved lacquer of claim 5 wherein said solvent comprises at least one of isopropanol, propylene glycol monomethyl ether, methyl ethyl ketone, toluene and ethylalcohol and is present in an amount sufficient to dissolve or fluidize said film-former.
Claim 9
Dependent Claim
34 words
The improved lacquer of claim 5 wherein said plasticizer comprises at least one of sucrose acetate isobutyrate, dibutyl phthalate and tricresyl phosphate and is present in an amount sufficient to plasticize said film former.
Claim 10
Dependent Claim
24 words
The improved lacquer of claim 1 wherein said film former comprises at least one of styrene maleate resin, acrylic ester resin and ethyl cellulose.
References Cited (Backward Citations)
US2191939A
Cited
US3152899A
Cited
US3527729A
Cited
US3592725A
Cited
GB1440269A
Cited
US4424091A
Cited
US4301046A
Cited
JPS56118444A
Cited
US4429065A
Cited
US4474909A
Cited
JPS59155434A
Cited
US4526910A
Cited
US4598112A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-03 | 1991-02-02 | 1991-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-03 | 1995-02-02 | 1995-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-03 | 1999-02-02 | 1999-08-04 | $7700.00 | Window Closed / Lapsed |