Transparent laminated polarizing glasses

Claim 1

A method for fabricating a transparent laminated polarizing glass consisting of a support of an inorganic or organic glass, a coating exhibiting polarizing properties disposed on one of the surfaces of the support, and an optically transparent layer adhered to the coating exhibiting polarizing properties and which protects the coating from humidity, said method comprising the following steps: (a) forming parallel microgrooves in a surface of the inorganic or organic glass support prior to applying the polarizing coating thereon with the help of a slightly abrasive brushing of the support; (b) carefully washing and drying that surface of the support prior to applying the polarizing coating thereon; (c) depositing on that washed and dried surface of the support a mixture of three organic colorants corresponding to the three primary colors and exhibiting a nematic state; (d) treating the resultant polarizing coating to reduce the water solubility of the coating by immersing into an aqueous solution of inorganic salts having an acid pH; (e) treating the resultant product of Step (d) above with an aqueous solution free of organic co-solvent prepared from at least one compound chosen from among gamma-aminopropyltrimethoxysilane and gamma-aminopropyltriethoxysilane, the silane representing 0.1-10% by volume of the solution and the aqueous solution having a pH in the range of 10-11.2, this treatment being followed by a rinsing in water and a heat treatment between 80°-140° C.; (f) placing the resultant product of Step (e) above in contact with an aqueous solution of an epoxyalkyltrialkoxysilane and then rinsing in water followed by a condensation and/or partial polymerization of the epoxyalkyltrialkoxysilane; and (g) applying an optically transparent, inorganic or organic protective layer to form a barrier against humidity, that application requiring a heat treatment at elevated temperature or irradiation with ultraviolet rays.

Claim 2

A method for fabricating a transparent laminated polarizing glass consisting of a support of an inorganic or organic glass, a coating exhibiting polarizing properties disposed on one of the surfaces of the support, and an optically transparent layer adhered to the coating exhibiting polarizing properties and which protects the coating from humidity, said method comprising the following steps: (a) forming parallel microgrooves in a surface of the inorganic or organic glass support prior to applying the polarizing coating thereon with the help of a slightly abrasive brushing of the support; (b) carefully washing and drying that surface of the support prior to applying the polarizing coating thereon; (c) depositing on that washed and dried surface of the support a mixture of three organic colorants corresponding to the three primary colors and exhibiting a nematic state; (d) treating the resultant polarizing coating to reduce the water solubility of the coating by immersing into an aqueous solution of inorganic salts having an acid pH; (e) treating the resultant product of Step (d) above with an aqueous solution free of organic co-solvent prepared from at least one compound chosen from among gamma-aminopropyltrimethoxysilane and gamma-aminopropyltriethoxysilane, the silane representing 0.1-10% by volume of the solution and the aqueous solution having a pH in the range of 10-11.2, this treatment being followed by a rinsing in water and a heat treatment between 80°-140° C.; (f) placing the resultant product of Step (e) above in contact with an aqueous solution of an epoxyalkyltrialkoxysilane and then rinsing in water followed by a condensation and/or partial polymerization of the epoxyalkyltrialkoxysilane; and (g) applying an optically transparent, inorganic or organic protective layer to form a barrier against humidity, that application requiring a heat treatment at elevated temperature or irradiation with ultraviolet rays.