US4682718A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Nozzle for continuous casting of molten steel
Assignee: Coorstek KK
•
Filing: 1985-11-12
•
Granted: 1987-07-28
•
Expires: 2005-11-12
Abstract
Abstract Silica powder is added to a primary mixture consisting of alumina powder and graphite powder, and is mixed therewith. A binder is added to the resultant secondary mixture and is well mixed therewith. The mixture thus obtained is granulated. The granulated product is placed in a rubber mold, and pressure is applied uniformly thereto to mold it. The molded product is fired but not sintered at a temperature between 850° and 950° C., preferably 900° C., which allows unreacted alumina and silica to remain in the final fired-product. Thus, a nozzle consisting of a fired body having a cavity volume index (the sum of the volume of open and closed pores/the volume of the fired body) of 0.15-0.25 including 6-60% of closed pores therein is manufactured.
Inventors
- 👤 Kuniaki Watanabe
- 👤 Hideo Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:07
CPC Classifications
C; C04; C04B; C04B38/00; C04B38/06; C04B38/0695; B; B22; B22D; B22D41/00; B22D41/50; B22D41/52; C04B35/00; C04B35/01; C04B35/10; C04B35/101; C04B2111/00; C04B2111/00474; C04B2111/0087
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
189 words
A nozzle for continuous casting comprising a fired unsintered body having a total volume and a minute cavities volume in the range of 0.1 to 0.25 of the total volume, said minute cavities comprising 6 to 60% closed pores, said closed pores comprising 1 to 10% of the total volume of the fired unsintered body, produced by the process of adding 2 to 30% by weight of silica powder to a primary mixture of 10 to 45% by weight of graphite powder uniformly dispersed in 40 to 88% by weight of alumina powder to obtain a secondary mixture, adding 2 to 30% by weight of a binder to the secondary mixture and kneading said secondary mixture and binder to obtain a final mixture, granulating said final mixture, molding said granulated final mixture in a rubber press to form a molded product, and firing the molded product at a temperature between 850° C. and 950° C. to decompose said binder into a gas to form said fired unsintered body with said closed pores while leaving unreacted alumina and silica in said fired unsintered body on surfaces of said closed pores.
Claim 2
Dependent Claim
189 words
A nozzle for continuous casting comprising a fired unsintered body having a total volume and a minute cavities volume in the range of 0.1 to 0.25 of the total volume, said minute cavities comprising 6 to 60% closed pores, said closed pores comprising 1 to 10% of the total volume of the fired unsintered body, produced by the process of adding 2 to 30% by weight of silica powder to a primary mixture of 10 to 45% by weight of graphite powder uniformly dispersed in 40 to 88% by weight of alumina powder to obtain a secondary mixture, adding 2 to 30% by weight of a binder to the secondary mixture and kneading said secondary mixture and binder to obtain a final mixture, granulating said final mixture, molding said granulated final mixture in a rubber press to form a molded product, and firing the molded product at a temperature between 850° C. and 950° C. to decompose said binder into a gas to form said fired unsintered body with said closed pores while leaving unreacted alumina and silica in said fired unsintered body on surfaces of said closed pores.
Claim 3
Dependent Claim
14 words
The nozzle according to claim 1, wherein said firing temperature is about 900° C.
Claim 4
Dependent Claim
36 words
A nozzle according to claim 1, wherein said granulated final mixture is molded in said rubber press under a pressure of 1000 kg/cm 2 to 1500 kg/cm 2 for a period of 5 to 20 minutes.
Claim 5
Dependent Claim
23 words
The nozzle according to claim 1, wherein said binder is selected from the group consisting of alcohol, a resin and a phenolic resin.
Claim 6
Dependent Claim
19 words
The nozzle according to claim 1, wherein the final mixture is granulated to granules of 0.5 to 1 mm.
Claim 7
Dependent Claim
21 words
The nozzle according to claim 1, wherein said minute cavities have a size in the range of 1 to 3000 microns.
Claim 8
Dependent Claim
35 words
The nozzle according to claim 1, wherein said minute cavities consist of open pores communicating with an outer surface of the refractory material constituting said nozzle and closed pores not communicating with said outer surface.
Claim 9
Dependent Claim
192 words
A nozzle for continuous casting molten steel comprising forming a primary mixture of 10 to 45% by weight of graphite powder uniformly dispered in 40 to 88% by weight of alumina powder, adding to said primary mixture 2 to 30% by weight of silica powder to form a secondary mixture, adding 2 to 30% by weight of a binder to the secondary mixture to thereby obtain a final mixture, granulating the final mixture to form a granulated product, molding the granulated product by the use of a rubber press to form a molded product, firing the molded product at a temperature between 850° C. and 950° C., and decomposing said binder into a gas to thereby form a fired unsintered body with closed pores while leaving unreacted alumina and silica in said fired unsintered body on surfaces of said closed pores, the fired unsintered body having a total volume and a minute cavities volume in the range of 0.1 to 0.25 of the total volume, said minute cavities comprising 6 to 60% of said closed pores, said closed pores comprising 1 to 10% of the total volume of the fired unsintered body.
Claim 10
Dependent Claim
192 words
A nozzle for continuous casting molten steel comprising forming a primary mixture of 10 to 45% by weight of graphite powder uniformly dispered in 40 to 88% by weight of alumina powder, adding to said primary mixture 2 to 30% by weight of silica powder to form a secondary mixture, adding 2 to 30% by weight of a binder to the secondary mixture to thereby obtain a final mixture, granulating the final mixture to form a granulated product, molding the granulated product by the use of a rubber press to form a molded product, firing the molded product at a temperature between 850° C. and 950° C., and decomposing said binder into a gas to thereby form a fired unsintered body with closed pores while leaving unreacted alumina and silica in said fired unsintered body on surfaces of said closed pores, the fired unsintered body having a total volume and a minute cavities volume in the range of 0.1 to 0.25 of the total volume, said minute cavities comprising 6 to 60% of said closed pores, said closed pores comprising 1 to 10% of the total volume of the fired unsintered body.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-27 | 1991-01-26 | 1991-07-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-27 | 1995-01-26 | 1995-07-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-27 | 1999-01-26 | 1999-07-28 | $7700.00 | Window Closed / Lapsed |